牌号简介 About |
---|
Capran 1000是一种0.40密耳(10微米)的双轴取向尼龙6薄膜,具有优异的抗弯曲裂纹性和优异的透明性,非常适合需要优异机械强度的包装应用。 CAPRAN® 1000 is a 0.40 mil (10 micron) biaxially oriented nylon 6 film with excellent flex crack resistance and superior clarity properties well suited for packaging applications requiring excellent mechanical strength. |
技术参数 Technical Data | |||
---|---|---|---|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
摩擦系数 friction coefficient |
ASTM D1894 | ||
与金属 - 动态 &Metal - Dynamic |
0.23 | ASTM D1894 | |
与自身 - 动态 With oneself - dynamic |
0.75 | ASTM D1894 | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
10 | µm | |
割线模量 Secant modulus |
ASTM D882 | ||
MD:10 µm MD:10 µm |
2760 | MPa | ASTM D882 |
TD:10 µm TD:10 µm |
2760 | MPa | ASTM D882 |
拉伸强度 tensile strength |
ASTM D882 | ||
MD,断裂,100 µm MD, fracture, 100 µ m |
MPa | ASTM D882 | |
TD,断裂,100 µm TD, fracture, 100 µ m |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,断裂,100 µm MD, fracture, 100 µ m |
% | ASTM D882 | |
TD,断裂,100 µm TD, fracture, 100 µ m |
% | ASTM D882 | |
透氧率 Oxygen permeability |
|||
25℃,100 µm 25℃,100 µm |
cm³·mm/m²/atm/24 hr | ASTM D3985 | |
水气透过率 Water vapor transmittance |
|||
10 µm,38℃,100% RH 10 µm,38℃,100% RH |
g·mm/m²/atm/24 hr | ASTM F1249 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
20°,102 µm 20°,102 µm |
ASTM D2457 | ||
雾度 Haze |
|||
102 µm 102 µm |
% | ASTM D1003 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
陶氏这款加强型珍珠棉,竟有如此神奇缓冲成效?
2017-03-01 物流增速之快,增量之大,难免出现商品因运输过程的颠簸而破损,导致消费者拒收和退货,为商家带来巨大风险和经济损失! 怎么办?靠包装材料啦! 据悉,目前除了产品的一次包装以及快递用的外在包装用纸箱,电商采用最多的包装材料就是防止产品破损的各类缓冲包装,包括EPE(珍珠棉),气泡膜,气柱袋,以及气垫袋等,用以减少破损。 从应用而言,EPE是使用最广泛的一种新型环保包装材料,各种形式的卷材和板材能够满足不同类型的需求,可为小如水果、电子元器件,大如电 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |