牌号简介 About |
---|
FRAGOM是我们的阻燃无卤聚烯烃化合物的商标。FRAGOM G/991 XA阻燃交联化合物,具有良好的绝缘和护套耐油性。它是一种易于嫁接的化合物,能够在水分和催化剂的存在下反应。我们通常建议使用Mac/100 SCU型催化剂。为了用于太阳能电缆护套(TUV),我们建议在接枝和催化剂之间添加10-11%的催化剂MAC/500反应。这两种化合物分开储存,在开始挤压之前必须按以下比例混合:接枝/催化剂95/5认证VDE 0207-24 hm3,BS 7655 EI5,CEI 2011 M2-EM2,IEC 60092-359 SHF2 FRAGOM is the trade-mark of our flame retardant halogen free polyolefine compounds. FRAGOM G/991 XA flame retardant crosslinkable compound having GOOD RESISTANCE TO OIL for insulation and sheathing. It is a conveniently grafted compound able to react in presence of moisture and of a catalyst. We normally suggest our catalyst type MAC/100 SCU. To use in solar cables sheathing (TUV) we suggest to add 10-11 % of catalyst MAC/500 REACTION BETWEEN GRAFTING AND CATALYST These two compounds, separately stored, must be mixed before starting extrusion in the ratio: GRAFTING/CATALYST 95/5 CERTIFY VDE 0207-24 HM3, BS 7655 EI5, CEI 2011 M2-EM2, IEC 60092-359 SHF2 |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.40 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,21.6kg 190℃,21.6kg |
7.0 到 12 | g/10min | ASTM D1238 |
老化性能 Aging performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
空气中拉伸强度的变化率 The rate of change in tensile strength in air |
IEC 60811 | ||
127℃,40 hr 127℃,40 hr 2 |
15 | % | IEC 60811 |
135℃,168 hr 135℃,168 hr 3 |
20 | % | IEC 60811 |
在空气中断裂时拉伸应力变化 Changes in tensile stress during fracture in air |
IEC 60811 | ||
127℃,40 hr 127℃,40 hr 2 |
-7.0 | % | IEC 60811 |
135℃,168 hr 135℃,168 hr 3 |
% | IEC 60811 | |
拉伸强度的变化率 The rate of change in tensile strength |
IEC 60811 | ||
70℃,168 hr 70℃,168 hr 4 |
% | IEC 60811 | |
100℃,168 hr 100℃,168 hr 5 |
% | IEC 60811 | |
极限伸长率的变化率 Change rate of ultimate elongation |
IEC 60811 | ||
70℃,168 hr 70℃,168 hr 4 |
% | IEC 60811 | |
100℃,168 hr 100℃,168 hr 5 |
% | IEC 60811 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热固性 thermosetting 6 |
IEC 60811 | ||
250℃ 250℃ |
% | IEC 60811 | |
Residual:250℃ Residual:250℃ |
% | IEC 60811 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
传导率 Conductivity |
µS/mm | IEC 60754-2 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
极限氧指数 Extreme oxygen index |
% | ASTM D2863 | |
Halogen Content Halogen Content |
% | IEC 60754-1 | |
毒性 toxicity |
|||
pH pH |
IEC 60754-2 | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
ASTM D2240 | ||
拉伸强度 tensile strength |
MPa | IEC 60811 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | IEC 60811 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 20 N/cm² |
3 Air Bomb |
4 Heat Aging |
5 Aging in IRM 903 oil |
6 Aging in IRM 902 oil |
【新闻资讯】查看全部
新一代摩拜单车采用陶氏全新低阻力实心胎
2017-09-30 近日摩拜单车正式发布全新一代车型。新款单车在保留橙色主色调的同时,将原本的银色替换成了黑白两色,配色上作出了明显改变。除了在外观上的改变,新款单车更是进行了技术升级。 全新一代摩拜单车是摩 拜单车的第四次全面升级,前三款分别是初代经典款摩拜单车、第二代轻巧的Lite版单车和今年4月发布的第三代“风轻扬”单车。新车型重新设计了每一个车身零件,车型更加简约流畅,车身重量更是降至全行业最低,整车仅重15.5kg,是市场上最轻的主流共享单车。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |