牌号简介 About |
---|
说明:EPOCAST1633-A/B环氧树脂复合材料是一种中等糊状无卤自熄化合物,设计用于蜂窝结构中的密封紧固件。环氧树脂句法很容易挤出1/8英寸。(3毫米)喷嘴孔,但使用后不流动。它很容易处理在孤立的维修区域,因为句法膏是在双筒墨盒。环氧树脂1633-A/B在室温下快速凝固。 DESCRIPTION: Epocast® 1633-A/B epoxy syntactic is a medium paste, halogen-free self-extinguishing compound designed for potting fasteners in honeycomb structures. The epoxy syntactic is easily extruded through 1/8 in. (3mm) nozzle orifice, but is non-flowing after application. It is easy to handle in isolated repair areas because the syntactic paste is available in dual-barrel cartridges. Epocast® 1633-A/B epoxy syntactic sets quickly at room temperature. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
ASTM D792 | ||
-- -- 2 |
0.660 | g/cm³ | ASTM D792 |
-- -- 3 |
0.680 | g/cm³ | ASTM D792 |
-- -- 4 |
0.730 | g/cm³ | ASTM D792 |
粘度 viscosity |
ASTM D2196 | ||
-- -- 3 |
Soft-paste | ASTM D2196 | |
-- -- 4 |
Paste | ASTM D2196 | |
-- -- 2 |
ASTM D2196 | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
压缩模量 Compression modulus |
MPa | ASTM D695 | |
压缩强度 compressive strength |
|||
25℃ 25℃ |
MPa | ASTM D695 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热固组件 Thermosetting components |
|||
树脂 resin |
|||
硬化法 Hardening method |
|||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
固化时间 Curing time |
|||
120℃ 120℃ |
hr | ||
Tensile Lap Shear(chromic acid etched al/al,25℃) Tensile Lap Shear(chromic acid etched al/al,25℃) |
MPa | ASTM D1002 | |
体重增量 Weight gain 5 |
ASTM D570 | ||
Distilled water:25℃ Distilled water:25℃ |
% | ASTM D570 | |
Mil-M-5606,hydraulic fluid:25℃ Mil-M-5606,hydraulic fluid:25℃ |
% | ASTM D570 | |
Skydrol 500-A:25℃ Skydrol 500-A:25℃ |
% | ASTM D570 | |
TTS-735,Type III test fluid:25℃ TTS-735,Type III test fluid:25℃ |
% | ASTM D570 | |
工作期限 Working period |
|||
10 grams,25℃ 10 grams,25℃ |
min | ASTM D1338 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Hardener |
3 Resin |
4 System |
5 on immersion - 24 hrs |
【新闻资讯】查看全部
梧州投资15亿元规划再生塑料加工
2018-06-05 近日,梧州年处理15万吨PET再生塑料加工项目投产。该项目引进国际最先进的PET瓶破碎清洗加工设备,是目前亚洲单线产能最大的再生瓶级聚酯切片生产线,其投产可以有效带动再生塑料产业链上下游产业的集聚和发展,推动循环经济园区产业转型升级取得新进展。 据了解,该项目计划总投资15亿元,主要投资PET塑料回收再生、HDPE塑料回收再生以及ABS塑料回收再生三大项目。项目建成达产后,预计年销售收入5亿元,利税收入约3000万元。为保证原材料供应,目前国龙再生资源公司已投入1000万元 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |