| 牌号简介 About |
|---|
| Cycoloy树脂CX7720是一种无溴、无氯阻燃PC/ABS树脂，具有高耐热性和薄壁阻燃性能。它是UL-94标准中的1.2 mm v0和1.5 mm 5vb。它的高热变形温度允许该产品被考虑用于需要比传统的fr-pc/abs更高的耐热性的应用。 Cycoloy resin CX7720 is a non brominated and non chlorinated flame retardant PC/ABS resin grade featuring high heat resistance and thin wall FR. It is UL-94 listed at 1.2 mm V0 and 1.5mm 5VB. Its high heat deflection temperature allows this product to be considered for applications requiring higher heat resistance than conventional FR PC/ABS. |
产品描述 Product Description
加工条件：注射成型 Injection Molding
性能特点： 无卤; 防火阻燃等级V-1; 防火阻燃等级V-0; 耐高温; 防火阻燃等级5VB; 阻燃; 防火阻燃等级5VA; Halogen free,Flame Characteristics,High Heat Resistance,V-1,V-0,5VA,5VB
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.22 | g/cm³ | ASTM D792 , ISO 1183 |
|
熔体质量流动速率 Melt Flow Rate |
ASTM D1238 | ||
|
260℃，2.16kg 260℃，2.16kg |
9.0 | g/10min | ASTM D1238 |
|
260℃，5.0kg 260℃，5.0kg |
25 | g/10min | ASTM D1238 |
|
熔体体积流动速率 Melt Volume Rate |
|||
|
260℃，5 kg 260℃，5 kg |
22.0 | cm³/10min | ISO 1133 |
|
收缩率 Shrinkage rate |
|||
|
MD：3.2 mm MD：3.2 mm |
0.50 到 0.70 | % | 内部方法 |
|
吸水率 Water absorption rate |
ISO 62 | ||
|
饱和，23℃ Saturation, 23 ℃ |
% | ISO 62 | |
|
平衡，23℃，50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus |
|||
|
-- -- 3 |
MPa | ASTM D638 | |
|
-- -- |
MPa | ISO 527-1-2 | |
|
拉伸强度 tensile strength |
|||
|
屈服 yield 4 |
MPa | ASTM D638 | |
|
屈服 yield |
MPa | ISO 527-2/50 | |
|
断裂 fracture 4 |
MPa | ASTM D638 | |
|
断裂 fracture |
MPa | ISO 527-2/50 | |
|
拉伸应变 Tensile strain |
|||
|
屈服 yield 4 |
% | ASTM D638 | |
|
屈服 yield |
% | ISO 527-2/50 | |
|
断裂 fracture 4 |
% | ASTM D638 | |
|
断裂 fracture |
% | ISO 527-2/50 | |
|
弯曲模量 Bending modulus |
|||
|
50 mm跨距 50 mm span 5 |
MPa | ASTM D790 | |
|
-- -- 6 |
MPa | ISO 178 | |
|
弯曲强度 bending strength |
|||
|
-- -- 6 , 7 |
MPa | ISO 178 | |
|
屈服，50 mm跨度 Yield, 50 mm span 5 |
MPa | ASTM D790 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength 8 |
|||
|
23℃ 23℃ 8 |
kJ/m² | ISO 179/1eA | |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
|
-30℃ -30℃ |
J/m | ASTM D256 | |
|
23℃ 23℃ |
J/m | ASTM D256 | |
|
-30℃ -30℃ 9 |
kJ/m² | ISO 180-1A | |
|
23℃ 23℃ 9 |
kJ/m² | ISO 180-1A | |
|
23℃ 23℃ 10 |
kJ/m² | ISO 180-1A | |
|
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
|||
|
23℃，Total Energy 23℃，Total Energy |
J | ASTM D3763 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
0.45 MPa，未退火，3.2 mm 0.45 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
|
0.45 MPa，未退火，6.4 mm 0.45 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
|
1.8 MPa，未退火，3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
|
1.8 MPa，未退火，6.4 mm 1.8 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
|
1.8 MPa，未退火，64 mm跨距 1.8 MPa, unannealed, 64 mm span 11 |
℃ | ISO 75-2/Af | |
|
维卡软化温度 Vicat Softening Temp |
|||
|
B50 B50 |
℃ | ASTM D1525 12 , ISO 306/B50 12 | |
|
B120 B120 |
℃ | ISO 306/B120 | |
|
线性热膨胀系数 Linear coefficient of thermal expansion |
ASTM E831 , ISO 11359-2 | ||
|
MD：-40~40℃ MD：-40~40℃ |
1/℃ | ASTM E831，ISO 11359-2 | |
|
TD：-40~40℃ TD：-40~40℃ |
1/℃ | ASTM E831，ISO 11359-2 | |
|
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
相比漏电起痕指数 Compared to the leakage tracing index |
UL 746 | ||
|
高电弧燃烧指数（HAI） High Arc Burning Index (HAI) |
UL 746 | ||
|
热丝引燃 Hot wire ignition |
|||
|
HWI HWI |
UL 746 | ||
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
阻燃等级 Flame retardant level |
UL 94 | ||
|
1.00 mm 1.00 mm |
UL 94 | ||
|
1.20 mm 1.20 mm |
UL 94 | ||
|
1.50 mm 1.50 mm |
UL 94 | ||
|
2.50 mm 2.50 mm |
UL 94 | ||
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 2.0 in/min |
| 3 类型 1, 2.0 in/min |
| 4 0.051 in/min |
| 5 0.079 in/min |
| 6 Yield |
| 7 80*10*3 sp=62mm |
| 8 80*10*3 |
| 9 80*10*4 |
| 10 80*10*4 mm |
| 11 标准 B (120°C/h), 载荷2 (50N) |
|