| 牌号简介 About |
|---|
| Alkamax ML1810PN是一种茂金属线性低密度聚乙烯共聚物。这种茂金属品位具有良好的加工性能，可提高生产率。它是为高性能薄膜应用而设计的，要求最大的韧性和良好的密封性能。Alkamax ML1810PN采用工艺助剂和工艺稳定包配制而成。不含防滑或防堵塞添加剂。Alkamax ML1810PN适用于需要高性能聚乙烯树脂的应用。用Alkamax ML1810PN生产的薄膜具有优异的韧性，使其非常适合用于重型应用或对现有薄膜结构进行下测。此外，该等级的高性能密封和热粘性能结合其优良的光学性能，使其成为层压和成型、填充和密封薄膜的理想选择。它被设计用于各种吹塑薄膜挤出设备的加工。如果预期的应用涉及间歇性到长时间暴露在阳光下，则应考虑添加紫外线稳定剂。 Alkamax ML1810PN is a metallocene linear low density polyethylene copolymer. This metallocene grade has excellent processability permitting higher production rates. It is designed for high performance film applications requiring maximum toughness and excellent sealing performance. Alkamax ML1810PN is formulated with a process aid and process stabilisation package. It does not contain slip or antiblocking additives. Film Extrusion: Alkamax ML1810PN is intended for applications requiring high performance polyethylene resins. Films produced with Alkamax ML1810PN have outstanding toughness, making this grade ideal for use in heavy duty applications or for downgauging existing film structures. In addition, the high performance sealing and hot tack properties of this grade combined with its excellent optical properties make it ideal for lamination and form, fill and seal films. It has been designed for processing on a wide range of blown film extrusion equipment. Addition of a UV stabiliser should be considered where the intended application involves intermittent to extended exposure to sunlight. |
产品描述 Product Description
用途：薄膜;层压板;
加工条件：薄膜挤出 Film extrusion
性能特点： 共聚物; 食品接触; 耐候抗UV; 韧性好; 低密度; 密封范围宽; 易加工; Weather resistance is good,Excellent Processability,Good flexibility,Food contact compliance,Broad Seal Range,Low density,Copolymer
紫外线：UV Stabilized
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.918 | g/cm³ | ASTM D1505 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
190℃，2.16kg 190℃，2.16kg |
1.0 | g/10min | ASTM D1238 |
|
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
薄膜厚度 film thickness |
|||
|
测试 test |
50 | µm | |
|
割线模量 Secant modulus 2 |
ASTM D882 | ||
|
2% 正割，MD：50 µm 2% secant, MD: 50 µ m |
183 | MPa | ASTM D882 |
|
2% 正割，TD：50 µm 2% secant, TD: 50 µ m |
190 | MPa | ASTM D882 |
|
拉伸强度 tensile strength 3 |
ASTM D882 | ||
|
MD，屈服，50 µm MD, yield, 50 µ m |
MPa | ASTM D882 | |
|
TD，屈服，50 µm TD, yield, 50 µ m |
MPa | ASTM D882 | |
|
MD，断裂，50 µm MD, fracture, 50 µ m |
MPa | ASTM D882 | |
|
TD，断裂，50 µm TD, fracture, 50 µ m |
MPa | ASTM D882 | |
|
拉伸应变 Tensile strain 3 |
ASTM D882 | ||
|
MD，断裂，50 µm MD, fracture, 50 µ m |
% | ASTM D882 | |
|
TD，断裂，50 µm TD, fracture, 50 µ m |
% | ASTM D882 | |
|
落锤冲击 Drop hammer impact 4 |
g | ASTM D1709 | |
|
埃尔曼多夫抗撕强度 Elmandorf tear strength |
ASTM D1922 | ||
|
MD：50 µm MD：50 µm |
g | ASTM D1922 | |
|
TD：50 µm TD：50 µm |
g | ASTM D1922 | |
|
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
光泽度 gloss 5 |
|||
|
45° 45° 5 |
ASTM D2457 | ||
|
雾度 Haze 5 |
|||
|
50 µm 50 µm 5 |
% | ASTM D1003 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 0.79 in/min |
| 3 20 in/min |
| 4 F50 |
| 5 (10% LDPE blended) |
|
【新闻资讯】查看全部
环保税按季度申报，4月环保税迎来首个征期
2018-05-21 四月以来，环保税开征和增值税将降低1%的消息传开，政策的变化在业内激起波澜，那么“两税”的实施，到底会对塑料行业产生怎样的影响呢? 首先来说环保税，《环境保护税法》在2018年年初实施，税法中规定，环保税按季度申报，4月环保税迎来首个征期。“费”改“税”最重要的目的不是为了获取财政收入，而是建立一个“企业多排多缴税，少排少缴税”的机制，通过刚性的税收倒逼高污染、高能耗企业转型升级。近年随着国家对环保的重视，企业在生产中对环保的各项要求积极响应，目前环保税的实施对规范性较好的 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付