牌号简介 About |
---|
SABIC® HDPE M40060S是一种紫外稳定的高密度聚乙烯共聚物注塑级,分子量分布窄。它改善了塑性。这种级别的产品通常具有良好的冲击强度、低翘曲、抗应力开裂(ESCR)和良好的光泽。典型应用。SABIC® HDPE M40060S通常用于制造注塑制品,如提桶、运输容器和工业零件。本产品不适用于任何医药/医疗应用,也不适用于任何医药/医疗应用。 SABIC® HDPE M40060S is an UV stabilized, high density polyethylene copolymer injection moulding grade with a narrow molecular weight distribution. It has improved mouldability. Articles produced from this grade typically show good impact strength, low warpage, stress crack resistance (ESCR) and good gloss. Typical applications. SABIC® HDPE M40060S is typically used for the manufacture of injection moulded articles such as pails, shipping containers and industrial parts. This product is not intended for and must not be used in any pharmaceutical/medical applications. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.960 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
ISO 1133 | ||
190℃,2.16kg 190℃,2.16kg |
4.0 | g/10min | |
190℃,5.0kg 190℃,5.0kg |
11 | g/10min | |
抗环境应力开裂 ESCR(Environmental Stress Cracking Resistance) 1 |
|||
60 ℃,3.00 mm,洗涤剂,模压成型 60 ℃, 3.00 mm, detergent, molded 1 |
70.0 | hr | 内部方法 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃,模压成型 23 ℃, molded |
5.0 | kJ/m² | ISO 180-A |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A | |
熔融温度 Melting temperature |
|||
DSC DSC |
℃ | ISO 11357-3 | |
Enthalpy Change Enthalpy Change |
J/g | ISO 11357-3 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D,模压成型 Shaw's D, molded |
ISO 868 | ||
拉伸模量 Tensile modulus |
|||
2 mm,模压成型 2 mm, molded into shape |
MPa | ISO 527-2/1BA/50 | |
拉伸强度 tensile strength |
ISO 527-2/1BA/50 | ||
屈服,2 mm,模压成型 Yield, 2 mm, molded |
MPa | ||
断裂,2 mm,模压成型 Fracture, 2 mm, molded |
MPa | ||
拉伸应变 Tensile strain |
|||
断裂,2 mm,模压成型 Fracture, 2 mm, molded |
% | ISO 527-2/1BA/50 | |
弯曲模量 Bending modulus |
|||
2 mm,模压成型 2 mm, molded into shape |
MPa | ISO 178 | |
弯曲强度 bending strength |
|||
2 mm,模压成型 2 mm, molded into shape |
MPa | ISO 178 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 2 MPa |
【新闻资讯】查看全部
废塑料循环再生行业崛起 从这里末尾
2017-10-26 塑料是20世纪的一项伟大发明,其应用领域不断扩宽,品种也不断增加,极大方便了人们的生活,成为了与人类生活息息相关的材料。如果没有了塑料,我们的生活会变成啥样,已不可想象。 1、塑料的两面性 2016年,我国的塑料制品产量已超过7700多万吨,产值近2万亿,且每年还在递增。如此大的市场也承载了无数人的英雄梦,为之不懈努力奋斗着,传奇人物李嘉诚的长江实业曾经就是从塑胶制品开始的。 但是,完美的事物是不可能存在的, |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |