牌号简介 About |
---|
Trirex是三养公司生产的聚碳酸酯树脂的注册商标。Trirex聚碳酸酯树脂具有优异的机械性能、良好的尺寸稳定性和高的电气性能,可广泛应用于电气、电子、电器、汽车和光学工业。TRIREX® 3020PJ是一种聚碳酸酯树脂级,专为配制而设计,特点颗粒型优越的冲击性能,良好的流动性,高电气性能,良好的尺寸稳定性,低吸水性,良好的耐候性。低粘度。仅限透明色。 TRIREX is the registered trademark of polycarbonate resin manufactured by Samyang Corporation. TRIREX polycarbonate resins offer superior mechanical properties, good dimensional stability and high electrical performance, which allows it to be widely used for electrical, electronic, appliance, automotive and optical industries. TRIREX 3020PJ is a polycarbonate resin grade which has high low temperature impact strength in combination with superior mechanical and physical property. CHARACTERISTICS Granule type Superior low temperature impact resistance Good flow-ability Workable under a wide range of temperatures (-100°C ~ 135°C) High electrical performance Good dimensional stability Low moisture absorbency Good weather resistance APPLICATIONS TRIREX 3020PJ resin grade is designed for Compounding. Low viscosity. Transparent colors only. |
产品描述 Product Description
厂家:韩国三养 Samyang
类别:PC Polycarbonate
用途:电气/电子应用领域;汽车领域的应用;光学应用;复合;电器用具;
颜色:清晰/透明
加工条件:复合,注射成型 Injection Molding
性能特点: 低吸湿性; 尺寸稳定性好; 防火阻燃等级V-2; 电气性好; 低粘度; 易流动; 耐候抗UV; V-2,Good Dimensional Stability,Good Electrical Properties,Good liquidity,Low Viscosity,Low moisture absorption,Weather resistance is good
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.20 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
300℃,1.20kg 300℃,1.20kg |
22 | g/10min | ASTM D1238 |
收缩率 Shrinkage rate |
|||
MD:3.0 mm MD:3.0 mm |
0.50 to 0.70 | % | ASTM D955 |
吸水率 Water absorption rate |
|||
23℃,24hr 23℃,24hr |
0.15 | % | ASTM D570 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
屈服 yield |
69.0 | MPa | ASTM D638 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲强度 bending strength |
|||
屈服 yield |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃,3.2mm 23℃,3.2mm |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1/℃ | ASTM D696 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength |
kV/mm | ASTM D149 | |
耐电弧性 Arc resistance |
sec | ASTM D495 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
1.60 mm 1.60 mm |
UL 94 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
科思创上调2020财年息税折旧摊销前利润和自由经营性现金流预测
2020-12-13 搜料网资讯: 由于2020年第四季度业务发展优于预期,科思创上调了对2020财年息税折旧摊销前利润和自由经营性现金流(FOCF)的预测。 科思创对2020财年的预测调整如下: 公司息税折旧 |
科思创上调2020财年息税折旧摊销前利润和自由经营性现金流预测
搜料网资讯:
科思创对2020财年的预测调整如下: 公司息税折旧及摊销前利润预计在14.4亿至15亿欧元之间。而之前的指导意见预计息税折旧及摊销前利润约为12亿欧元。指导意见调整的主要原因是聚氨酯和聚碳酸酯这两个领域的利润增长非常好。市场一致预期这一数字会达到11.99亿欧元。 公司预计自由经营现性金流(FOCF)在4亿至5.5亿欧元之间。此前的指导意见预计FOCF在0至3亿欧元之间。指导意见调整的主要原因是预测息税折旧及摊销前利润将会增加。一致预期这一数字为3.09亿欧元。 公司的核心业务量增长率曾预期--不变, 目前预期核心业务量增长率将会低于上一年(2019年:+2.0%)。下降幅度会在-5%至-6%之间。 公司2020年报将于2021年2月23日公布。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】
全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情
【精准,及时,权威!】
专业团队挖掘行情信息,第一时间发布行情
抱歉!该牌号暂无认证数据。
免责声明:参考价格是搜料网根据网络大数据拟合分析的结果,仅供参考。实际成交价取决但不限于以下因素:下单时间,付款方式,交货方式,数量,税费,色号,产地,项目信息。
抱歉!暂无数据。
抱歉!暂无数据。