牌号简介 About |
---|
Adflex KS311P是一种反应器TPO(热塑性聚烯烃),采用Lyondellbasell专有的Catalloy工艺技术制造。它适用于挤压、注塑和吹塑应用,包括需要弹性类型特性的机械和装饰性汽车零件,如彩色汽车外部组件的注塑。该产品实际上被我们的客户用于具有可喷漆和耐候性要求的应用,如注塑蒙皮、覆层、保险杠盖、车身板、踏板和空气导流板。它也被用作复合材料的一种组分,用于广泛的工业应用。该等级为天然颗粒形式。有关法规遵从性信息,请参阅Adflex KS311P产品管理公告(PSB)。 Adflex KS311P is a reactor TPO (thermoplastic polyolefin) manufactured using LyondellBasell's proprietary Catalloy process technology. It is suitable for extrusion as well as injection molding and blow molding applications, including mechanical and decorative automotive parts requiring elastomeric type properties, like molded-in color automotive exterior components. The product is in fact used by our customers for applications with paintable and weatherable requirements, such as injection molded fascias, claddings, bumper covers, body panels, step pads, and air deflectors. It is also used as a component in compounded materials for a wide range of industrial applications. The grade is available in natural pellet form. For regulatory compliance information see Adflex KS311P Product Stewardship Bulletin (PSB). |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.890 | g/cm³ | ISO 1183/A |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
9.5 | g/10min | ISO 1133 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D,15 秒 Shore D, 15 seconds |
46 | ISO 868 | |
拉伸强度 tensile strength |
|||
断裂,23℃ Fracture, 23 ℃ |
19.0 | MPa | ISO 527-2/50 |
屈服,23℃ Yield, 23 ℃ |
14.0 | MPa | ISO 527-2/50 |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ISO 527-2/50 | |
屈服,23℃ Yield, 23 ℃ |
% | ISO 527-2/50 | |
弯曲模量 Bending modulus 2 |
|||
弦,23℃ String, 23 ℃ 2 |
MPa | ISO 178 | |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
撕裂强度 tear strength 3 |
kN/m | ASTM D624 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180/1A | ||
-40℃,局部断裂 -40 ℃, localized fracture |
kJ/m² | ISO 180-1A | |
23℃,局部断裂 23 ℃, localized fracture |
kJ/m² | ISO 180-1A | |
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
ASTM D3763 | ||
-40℃,3.20 mm,Energy at Peak Load,Ductile Failure -40℃,3.20 mm,Energy at Peak Load,Ductile Failure 4 |
J | ASTM D3763 | |
23℃,3.20 mm,Energy at Peak Load,Ductile Failure 23℃,3.20 mm,Energy at Peak Load,Ductile Failure 5 |
J | ASTM D3763 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
维卡软化温度 Vicat Softening Temp |
|||
A50 A50 |
℃ | ISO 306/A50 | |
熔融温度 Melting temperature |
℃ | ISO 11357-3 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0.079 in/min |
3 C 模具, 2.0 in/min |
4 21.7 ft/sec |
5 7.22 ft/sec |
【新闻资讯】查看全部
巴斯夫马来西亚Ucrete®新设备举行开幕式
2016-04-05 巴斯夫位于马来西亚生产Ucrete® 的新设施已举行了开幕式,它将更好的满足于亚太地区对高质耐用工业地板日益增长的需求。 巴斯夫新加坡,马来西亚,缅甸,柬埔寨,老挝等国家的建筑化学负责人Arnold De Silva表示:“新设施使我们能更好的服务客户,从而提高35%的交货效率。” 该设施是第一个可以生产四种Ucrete聚氨酯混凝土地板系统的设施,巴斯夫在英国也有同样的设施。 巴斯夫马来西亚常务董事Daniel Loh表示:“巴斯夫在马来西亚 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |