牌号简介 About |
---|
Bayflex 180是一种高性能聚合物系统,具有优异的热稳定性、低吸湿性、低热膨胀特性和优异的抗冲击性。用这种材料制成的零件具有良好的表面和油漆粘合质量,并且具有与涂漆钢零件相当的DOI(图像区别)。Bayflex 180系统可以对各种零件进行成型,从薄壁门槛板和装饰件到大型耐用车身板和专用设备的发动机外壳。与任何产品一样,在给定应用中使用Bayflex 180系统必须由用户提前进行测试(包括现场测试等),以确定其适用性。Bayflex 180系统作为两种反应性液体成分提供。A组分为二苯基甲烷二异氰酸酯(MDI)预聚物,B组分为聚醚多元醇。 Bayflex 180 is a high-performance polymer system with excellent heat stability, low moisture absorption, low thermal expansion characteristics and excellent impact resistance. Parts made from this material have excellent surface and paint adhesion qualities and have a DOI (Distinction of Image) comparable to painted steel parts. A wide range of parts can be molded with the Bayflex 180 system, from thin wallstock rocker panels and trim to large, durable body panels and engine enclosures for specialty equipment. As with any product, use of the Bayflex 180 system in a given application must be tested (including field testing, etc.) in advance by the user to determine suitability. The Bayflex 180 system is supplied as two reactive liquid components. Component A is a diphenylmethane diisocyanate (MDI) prepolymer and Component B is a polyether polyol. |
产品描述 Product Description
厂家:德国科思创 Covestro
类别:PUR-脂肪族+MDI PUR-脂肪族+MDI
用途:汽车领域的应用;汽车外部零件;汽车外部装饰;汽车的发动机罩下的零件;
加工条件:反应注射成型 (RIM)
性能特点: 低吸湿性; 热稳定性好; 可表面喷涂; 冲击性能好; 表面光泽度好; Good surface appearance,High impact resistance,Sprayable,Low moisture absorption,Heat Stabilized
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.04 | g/cm³ | ASTM D792 , ASTM D1622 |
收缩率 Shrinkage rate |
|||
MD MD |
1.7 | % | 内部方法 |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
断裂,3.18 mm Fracture, 3.18 mm |
28.3 | MPa | ASTM D638 |
断裂,3.18 mm Fracture, 3.18 mm |
28.3 | MPa | ASTM D412 |
拉伸应变 Tensile strain |
|||
断裂,3.18 mm Fracture, 3.18 mm |
130 | % | ASTM D638 |
断裂,3.18 mm Fracture, 3.18 mm |
% | ASTM D412 | |
撕裂强度 tear strength 2 |
|||
3.18 mm 3.18 mm 2 |
kN/m | ASTM D624 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
3.2mm 3.2mm |
J/m | ASTM D256 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Heat Sag Heat Sag 4 |
ASTM D3769 | ||
4 in Overhang:121℃,3.18 mm 4 in Overhang:121℃,3.18 mm |
µm | ASTM D3769 | |
6 in Overhang:121℃,3.18 mm 6 in Overhang:121℃,3.18 mm |
µm | ASTM D3769 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D,3.18 mm Shaw D, 3.18 mm |
ASTM D2240 | ||
弯曲模量 Bending modulus |
ASTM D790 | ||
-30℃,3.18 mm -30℃,3.18 mm |
MPa | ASTM D790 | |
23℃,3.18 mm 23℃,3.18 mm |
MPa | ASTM D790 | |
65℃,3.18 mm 65℃,3.18 mm |
MPa | ASTM D790 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:3.2 mm MD:3.2 mm |
1/℃ | ASTM D696 | |
热固组件 Thermosetting components 3 |
|||
部件 A Component A |
|||
部件 B Component B |
|||
贮藏期限 Storage period |
|||
32℃ 32℃ |
wk |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 C 模具 |
3 105 Index |
4 1 hr |
【新闻资讯】查看全部
尼龙两头体-己二腈产能散布
2018-08-09 什么是己二腈 (1)性能:无色油状液体,略有气味,是制造尼龙的中间体。遇明火、高热可燃,与强氧化剂可发生反应,受热分解放出有毒的氧化氮烟气。 (2)用途:主要用于生产尼 |
尼龙两头体-己二腈产能散布 什么是己二腈(1)性能:无色油状液体,略有气味,是制造尼龙的中间体。遇明火、高热可燃,与强氧化剂可发生反应,受热分解放出有毒的氧化氮烟气。
(2)用途:主要用于生产尼龙纤维的中间体已二胺,橡胶促进剂和防锈剂,也用作洗涤剂的添加剂,丙烯腈、甲基丙烯腈和甲基丙烯酸甲酯三元共聚体的纺丝溶剂,聚氯乙烯纤维湿纺和干纺溶剂,尼龙的着色剂,织物漂白剂的助剂,醋酸酯、丙酸酯、丁酸酯和混合酯增塑剂;以及作为芳烃抽提的萃取剂等。
丙烯腈电解二聚法:
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】
全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情
【精准,及时,权威!】
专业团队挖掘行情信息,第一时间发布行情
抱歉!该牌号暂无认证数据。
免责声明:参考价格是搜料网根据网络大数据拟合分析的结果,仅供参考。实际成交价取决但不限于以下因素:下单时间,付款方式,交货方式,数量,税费,色号,产地,项目信息。
抱歉!暂无数据。
抱歉!暂无数据。