牌号简介 About |
---|
F0554是一种高分子量高密度聚乙烯树脂,专为吹塑薄膜应用而设计。该树脂分子量分布广泛,易于加工。由该树脂制成的薄膜具有高硬度、优异的冲击韧性。应用购物袋垃圾袋工业内衬 F0554 is a high molecular weight high density polyethylene resin designed for blown film applications. This resin has broad molecular weight distribution that makes it easier to process. Films made from this resin exhibit high stiffness, excellent impact and toughness characteristics. Applications Shopping bag Trash bag Industrial liner |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.951 | g/cm³ | ASTM D792-A |
熔体质量流动速率 Melt Flow Rate |
ASTM D1238 | ||
190℃,2.16kg 190℃,2.16kg |
0.050 | g/10min | ASTM D1238 |
190℃,21.6kg 190℃,21.6kg |
9.3 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
20 | µm | |
割线模量 Secant modulus |
ASTM D882 | ||
1% 正割,MD:20 µm 1% secant, MD: 20 µ m 2 |
930 | MPa | ASTM D882 |
1% 正割,MD:20 µm 1% secant, MD: 20 µ m 3 |
MPa | ASTM D882 | |
1% 正割,TD:20 µm 1% secant, TD: 20 µ m 2 |
MPa | ASTM D882 | |
1% 正割,TD:20 µm 1% secant, TD: 20 µ m 3 |
MPa | ASTM D882 | |
拉伸强度 tensile strength |
|||
MD,屈服,20 µm MD, yield, 20 µ m 2 |
MPa | ASTM D882 | |
TD,屈服,20 µm TD, yield, 20 µ m 2 |
MPa | ASTM D882 | |
MD,断裂,20 µm MD, fracture, 20 µ m 2 |
MPa | ASTM D882 | |
MD,断裂,20 µm MD, fracture, 20 µ m 3 |
MPa | ASTM D882 | |
TD,断裂,20 µm TD, fracture, 20 µ m 2 |
MPa | ASTM D882 | |
TD,断裂,20 µm TD, fracture, 20 µ m 3 |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,断裂,20 µm MD, fracture, 20 µ m 2 |
% | ASTM D882 | |
MD,断裂,20 µm MD, fracture, 20 µ m 3 |
% | ASTM D882 | |
TD,断裂,20 µm TD, fracture, 20 µ m 2 |
% | ASTM D882 | |
TD,断裂,20 µm TD, fracture, 20 µ m 3 |
% | ASTM D882 | |
落锤冲击 Drop hammer impact |
ASTM D1709 | ||
20 µm 20 µm 2 |
g | ASTM D1709 | |
20 µm 20 µm 3 |
g | ASTM D1709 | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
ASTM D1922 | ||
MD:20 µm MD:20 µm 2 |
g | ASTM D1922 | |
MD:20 µm MD:20 µm 3 |
g | ASTM D1922 | |
TD:20 µm TD:20 µm 2 |
g | ASTM D1922 | |
TD:20 µm TD:20 µm 3 |
g | ASTM D1922 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp 2 |
℃ | ASTM D1525 4 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 With Stabilizer |
3 Without Stabilizer |
4 压 力1 (10N) |
【新闻资讯】查看全部
为什么保险杠是塑料的?
2018-01-19 最近有网友问:为什么保险杠是塑料的?铁的不是更耐用吗?原因很简单,但道理很深奥!早期的汽车前后保险杠都是金属材料为主,第一个使用塑料保险杠的是菲亚特,从此其他车企 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |