牌号简介 About |
---|
VYPET 630 FR是一种30%玻璃纤维增强阻燃聚酯注塑化合物,专为电气和结构应用而设计。特点阻燃UL黄牌文件E216152优异的强度和刚度优异的尺寸稳定性典型应用电器电器电子应用 Vypet 630 FR is a 30 % glass reinforced Flame retardant, PET injection molding compound designed for electrical and structural applications. Features Flame retardant UL yellow card file E216152 Excellent strength and stiffness Excellent dimensional stability Typical Applications Electrical parts Appliances Electronic Applications |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.65 | g/cm³ | ASTM D792 , ISO 1183 |
收缩率 Shrinkage rate |
|||
MD:2.0 mm MD:2.0 mm |
0.20 | % | ASTM D955 |
TD:2.0 mm TD:2.0 mm |
0.90 | % | ASTM D955 |
TD:2.0 mm TD:2.0 mm |
0.90 | % | ISO 294-4 |
MD:2.0 mm MD:2.0 mm |
0.20 | % | ISO 294-4 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
断裂 fracture 3 |
MPa | ASTM D638 | |
断裂 fracture |
MPa | ISO 527-2/5 | |
弯曲模量 Bending modulus 4 |
|||
-- -- |
MPa | ASTM D790 | |
-- -- |
MPa | ISO 178 | |
弯曲强度 bending strength 4 |
MPa | ASTM D790,ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
J/m | ASTM D256 | |
23℃ 23℃ |
kJ/m² | ISO 180-A | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
|||
1 kHz 1 kHz |
ASTM D150 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
UL 746 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
0.90 mm 0.90 mm |
UL 94 | ||
1.50 mm 1.50 mm |
UL 94 | ||
3.00 mm 3.00 mm |
UL 94 | ||
灼热丝可燃性指数 Glowing wire flammability index |
|||
1.0 mm 1.0 mm |
℃ | IEC 60695-2-12 | |
灼热丝起燃温度 Igniting temperature of the hot wire |
|||
1 mm 1 mm |
℃ | IEC 60695-2-13 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0.20 in/min |
3 0.079 in/min |
【新闻资讯】查看全部
俄罗斯1-9月高密度聚乙烯产量下降5%
2021-04-21 搜料网资讯: 10月23日莫斯科报道 根据MRC ScanPlast报告,俄罗斯1-9月高密度聚乙烯(HDPE)产量同比下降5%,四分之三的生产商减产。 2019年前9个月,高密度聚乙烯总产量为69.52万吨,而去年同 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |