牌号简介 About |
---|
SABIC PP化合物5521是一种填充矿物的冲击改性聚丙烯TPO。这种材料结合了良好的流动性和外部汽车风化稳定性。一般用途的黑色产品没有耐候性,具有良好的可涂性。该耐候产品最初设计用于未上漆的汽车外部保险杠盖和踏板应用,需要高灵活性。IMDS是163257209。 SABIC® PPCOMPOUND 5521 is a mineral filled, impact modified polypropylene TPO. This material combines good flow with exterior automotive weathering stability. The general purpose black color product is offered without weathering stability for good paintability. The weatherable product was originally designed for unpainted automotive exterior bumper cap and step pad applications where high flexibility is required. The IMDS is 163257209. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.900 | g/cm³ | ASTM D792 |
密度 Density |
0.900 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
19 | g/10min | ISO 1133 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
57 | ISO 868 | |
拉伸模量 Tensile modulus |
853 | MPa | ISO 527-1-2 |
拉伸强度 tensile strength |
|||
断裂 fracture |
MPa | ISO 527-2/1A/50 | |
屈服 yield |
MPa | ISO 527-2/50 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ISO 527-2/50 | |
屈服 yield |
% | ISO 527-2/50 | |
弯曲模量 Bending modulus 2 |
|||
64 mm跨距 64 mm span 2 |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
-30℃ -30℃ 3 |
kJ/m² | ISO 179/1eA | |
0℃ 0℃ 4 |
kJ/m² | ISO 179/1eA | |
23℃ 23℃ 4 |
kJ/m² | ISO 179/1eA | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch 3 |
ISO 180/1A | ||
-30℃ -30℃ |
kJ/m² | ISO 180-1A | |
0℃ 0℃ |
kJ/m² | ISO 180-1A | |
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments 5 |
ASTM D3763 | ||
-30℃,Energy at Peak Load -30℃,Energy at Peak Load |
J | ASTM D3763 | |
23℃,Energy at Peak Load 23℃,Energy at Peak Load |
J | ASTM D3763 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature 3 |
|||
1.8 MPa,未退火 1.8 MPa, unannealed 3 |
℃ | ISO 75-2/A | |
0.45 MPa,未退火 0.45 MPa, unannealed 3 |
℃ | ISO 75-2/B | |
维卡软化温度 Vicat Softening Temp |
|||
A50 A50 |
℃ | ISO 306/A50 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD:-30~100℃ TD:-30~100℃ |
1/℃ | ISO 11359-2 | |
MD:-30~100℃ MD:-30~100℃ |
1/℃ | ISO 11359-2 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0.079 in/min |
3 80*10*4mm, Cut |
4 80*10*4 mm, Cut |
5 7.22 ft/sec |
【新闻资讯】查看全部
万华化学:烟台工业园MDI装置复产,子公司匈牙利宝思德化学公司装置
2021-08-10 搜料网资讯: 万华化学8月9日晚间公告,公司烟台工业园MDI装置检修结束,恢复正常生产。按照年度检修计划,公司子公司匈牙利宝思德化学公司MDI装置(30万吨/年)将于8月17日开始陆续停 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |