牌号简介 About |
---|
MARCOBLEND 2100是一种阻燃的玻璃纤维增强聚碳酸酯树脂。该树脂无卤,符合TCO和RoHS认证。其独特的特点是加工性好、刚度好、尺寸稳定性好,适用于TFT液晶显示器框架和内部结构件。 MARCOBLEND 2100 is an ignition resistant and glass fiber reinforced polycarbonate resin. The resin is Halogen free and compliance with TCO and RoHS certification. The unique characters include superior processability, good stiffness, and excellent dimension stability and suitable for use in TFT LCD frame and internal structure parts. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.28 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
300℃,1.20kg 300℃,1.20kg |
18 | g/10min | ASTM D1238 |
收缩率 Shrinkage rate |
|||
MD MD |
0.22 到 0.28 | % | ASTM D955 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
屈服 yield |
70.0 | MPa | ASTM D638 |
弯曲模量 Bending modulus |
3630 | MPa | ASTM D790 |
弯曲强度 bending strength |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
科莱恩将携创新PET膜材和功用性板材处理方案
2017-05-23 第十三届上海国际功能性膜材展览会(APFE)期间,科莱恩将着重推出专为PET膜材和板材行业设计的解决方案和产品 针对产能和实验室进行投资以更好地服务于地区市场 为CESA®系列色母粒产品将为消费品行业的包装产品带来新的功能特性 用于PET膜材的Renol®色母粒能够为设计师提供鲜艳、持久且均匀一致的色彩 上海,2017年5月22日――全球领先的特种化学品制造商科莱恩将参加第十三届上海国际功能性膜材展览会(APFE),全面推出针 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |