牌号简介 About |
---|
Lupoy PC 1201-15树脂专为挤出和注塑产品设计。它在耐热性、透明度和冲击强度方面表现出良好的物理性能平衡。 LUPOY PC 1201-15 resin is designed for extrusion and injection molding products. It exhibits an excellent physical property balance of heat resistance, transparency and impact strength. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.20 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
300℃,1.20kg 300℃,1.20kg |
15 | g/10min | ASTM D1238 |
收缩率 Shrinkage rate |
|||
MD MD |
0.50 to 0.70 | % | ASTM D955 |
吸水率 Water absorption rate |
|||
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
0.32 | % | ASTM D570 |
23℃,24hr 23℃,24hr |
0.15 | % | ASTM D570 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃,3.2mm 23℃,3.2mm 4 |
J/m | ASTM D256 | |
23℃ 23℃ |
ASTM D256 | ||
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments 5 |
|||
23℃,3.20 mm,Total Energy 23℃,3.20 mm,Total Energy 5 |
J | ASTM D3763 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,退火,4.0 mm 1.8 MPa, annealed, 4.0 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火,4.0 mm 1.8 MPa, unannealed, 4.0 mm |
℃ | ASTM D648 | |
0.45 MPa,退火,4.0 mm 0.45 MPa, annealed, 4.0 mm |
℃ | ASTM D648 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 6 | |
球压温度 Ball pressure temperature |
℃ | IEC 60598-1 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:-40~82℃ MD:-40~82℃ |
1/℃ | ASTM D696 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
|||
23℃ 23℃ |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
|||
60 Hz 60 Hz |
ASTM D150 | ||
耗散因数 Dissipation factor |
|||
60 Hz 60 Hz |
ASTM D150 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
|||
2.00 mm 2.00 mm |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
3.00 mm 3.00 mm |
UL 94 | ||
0.50 mm 0.50 mm |
UL 94 | ||
1.60 mm 1.60 mm |
UL 94 | ||
2.50 mm 2.50 mm |
UL 94 | ||
2.70 mm 2.70 mm |
UL 94 | ||
灼热丝起燃温度 Igniting temperature of the hot wire 7 |
|||
2 mm 2 mm 7 |
℃ | IEC 60695-2-13 | |
极限氧指数 Extreme oxygen index |
% | ASTM D2863 | |
平均燃烧程度 Average combustion degree |
cm | ASTM D635 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
折射率 Refractive index |
ASTM D542 | ||
透光率 Transmittance |
% | ASTM D1003 | |
雾度 Haze |
% | ASTM D1003 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
MPa | ASTM D638 | |
拉伸强度 tensile strength 2 |
|||
断裂 fracture |
MPa | ASTM D638 | |
屈服,23℃ Yield, 23 ℃ 2 |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
屈服 yield |
% | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲强度 bending strength |
MPa | ASTM D790 | |
耐磨耗性 Wear resistance 3 |
|||
Change in Haze Change in Haze 3 |
% | ASTM D1004 | |
洛氏硬度 Rockwell hardness |
ASTM D785 | ||
M 级 M-level |
ASTM D785 | ||
R 级 R-level |
ASTM D785 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 2.0 in/min |
3 1000g, 500 cycles, CS-10F Wheel |
4 9.8 mil 缺口深度 |
5 11.1 ft/sec |
6 速率 A (50°C/h), 载荷2 (50N) |
7 5 sec |
【新闻资讯】查看全部
道康宁展现新型橡胶胶粘剂
2016-04-15 道康宁公司将在4月12-14日于密歇根底特律举办的SAE2016世界会展上(展位是1135)展示它在硅酮胶和氟硅橡胶技术方面的重要突破,借以彰显智能科技如何推动移动创新发展。此次展出的新型胶黏剂和工程弹性体技术,由道康宁经由行业合作研发而成,以满足汽车行业的重点设计需求。 道康宁去年首次推出其轰动一时的创新型产品,而这次展会上推出的是它备受称赞的先进热自由基固化(简称TRC)硅酮胶和高性能氟硅橡胶(FSR),以及其他在高性能移动解决方案方面的创新性材料科技技术。这些技术包含 |
道康宁展现新型橡胶胶粘剂 道康宁企业将在4月12-14日于密歇根底特律举行的SAE2016全球展会上(展台是1135)展现它在硅酮胶和氟硅橡胶技术层面的关键提升,进而突显信息科技怎样促进挪动改革创新。本次展览的新式胶黏剂和工程项目聚氨酯弹性体技术,由道康宁经过领域协作产品研发而成,以考虑汽车领域的关键设计方案要求。 道康宁上年初次发布其轰动一时的技术创新商品,而此次展览会上发布的是它深受夸赞的优秀热氧自由基固化(通称TRC)硅酮胶和性能卓越氟硅橡胶(FSR),及其别的在性能卓越挪动解决方法层面的创新能力原材料高新科技技术。这种技术包括有在汽车运用中具有优点特性及特性的自主创新化学变化。来道康宁展台的观看者将还有机会触碰到本企业在商品样版、互动演示、技术主要参数层面的权威专家,并还有机会两者之间讨论各商品潜在性的运用要求。 道康宁EA-7100胶黏剂,是领域领跑的TRC胶黏剂知名品牌,巨大地拓展了汽车用电子产品的设计方案多元性,能够将高韧性的机器设备拼装件粘接到各种各样的基钢板上。除此之外,这类胶黏剂选用一步加温固化成形技术,固化时间较短,且在超低温标准下,还可以从內部大大的加快全部生产过程,减少耗能和原材料成本费。 道康宁交通出行电子产品部全世界销售总监Brice Le Gouic说:“新硅橡胶化工品已设知识产权保护,拥有它,大家的自主创新系列胶黏剂大家族将为新一代控制、感应器、照明灯具和显示信息控制模块确立了极为广泛的设计空间及高宽比。此项技术得到了产品研发杂志期刊2015千名设计方案巨奖,证实协作的使用价值是完成顾客与本身的互利共赢。” 为考虑顾客的必须和要求,将要公布的容许高溫实际操作标准的Silastic牌氟硅橡胶,大大的提高了道康宁本就处在领域领跑的氟硅橡胶大家族的整体实力,顺从了较小模块隔断的设计方案发展趋势,提高了有机废气的循环工作能力,而且降低了推动发动机盖溫度快速上升的气旋的产生。 来源于:PUWORLD |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
抱歉!该牌号暂无认证数据。
价格走势图
抱歉!该牌号暂无认证数据。
抱歉!暂无数据。
抱歉!暂无数据。