牌号简介 About |
---|
Lupoy PC 1302LT-12树脂专为挤出和注塑产品设计。它在耐热性、透明度和冲击强度方面表现出良好的物理性能平衡。主要特点中粘度紫外线吸收剂无脱模剂应用灯具户外电器镜片 LUPOY PC 1302LT-12 resin is designed for extrusion and injection molding products. It exhibits an excellent physical property balance of heat resistance, transparency and impact strength. Main Characteristics Medium viscosity UV absorbers No mold release agent Applications Luminaires Outdoor appliances Lens |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.20 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
300℃,1.20kg 300℃,1.20kg |
12 | g/10min | ASTM D1238 |
收缩率 Shrinkage rate |
|||
MD MD |
0.50 到 0.70 | % | ASTM D955 |
吸水率 Water absorption rate |
|||
23℃,24hr 23℃,24hr |
0.15 | % | |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
0.32 | % | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch 4 |
|||
23℃,3.2mm 23℃,3.2mm 4 |
J/m | ASTM D256 | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
23℃ 23℃ |
ASTM D256 | ||
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments 5 |
|||
23℃,3.18 mm,Total Energy 23℃,3.18 mm,Total Energy 5 |
J | ASTM D3763 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,退火,4.0 mm 0.45 MPa, annealed, 4.0 mm |
℃ | ||
1.8 MPa,未退火,4.0 mm 1.8 MPa, unannealed, 4.0 mm |
℃ | ||
1.8 MPa,退火,4.0 mm 1.8 MPa, annealed, 4.0 mm |
℃ | ||
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 6 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:-40~82℃ MD:-40~82℃ |
1/℃ | ASTM D696 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
折射率 Refractive index |
ASTM D542 | ||
透光率 Transmittance |
% | ASTM D1003 | |
雾度 Haze |
% | ASTM D1003 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
|||
M 级 M-level |
|||
R 级 R-level |
|||
拉伸模量 Tensile modulus |
MPa | ASTM D638 | |
拉伸强度 tensile strength |
|||
屈服,23℃ Yield, 23 ℃ 2 |
MPa | ||
断裂 fracture |
MPa | ||
拉伸应变 Tensile strain |
|||
屈服 yield |
% | ||
断裂 fracture |
% | ||
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲强度 bending strength |
MPa | ASTM D790 | |
耐磨耗性 Wear resistance 3 |
|||
Delta Haze Delta Haze 3 |
% | ASTM D1004 |
备注 |
---|
2、50 mm/min |
3、CS-10F Wheel, 500 cycles, 1000 g |
4、0.25 mm 缺口深度 |
5、3.39 m/sec |
6、速率 A (50°C/h), 载荷2 (50N) |
【新闻资讯】查看全部
RECTICEL宣布MDI货源充足
2017-05-15 在2017年4月26日的最新交易中,Recticel强调了由于异氰酸酯(TDI和MDI)供应紧张,现聚氨酯行业面临着极具挑战性的原材料价格普遍空前高涨的情况。 Recticel今天宣布,由于Covestro面临着新的不可抗力且Huntsman起步方面也存在问题,MDI(亚甲基二苯基二异氰酸酯)的生产情况随之进一步恶化。 因此,MDI出现了货源短缺的情况。这种短缺正在影响Recticel的绝缘业务,现已削减了其15%的生产量,预计此情况2017年7月之前不会有 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |