牌号简介 About |
---|
Kalix® 2940是一种生物来源的聚酰胺基化合物,按重量计有40%的玻璃纤维增强。这种材料是专门为高强度和刚度应用而设计的,在这些应用中,要求具有良好的抗冲击性和成型后的良好尺寸稳定性。该公式还解决了与玻璃纤维增强材料的各向异性收缩有关的翘曲问题,以便更容易实现精密公差成型。它的低粘度和优良的流动性能使这种材料非常适合于填充具有薄壁截面的部件,如移动电子工业中遇到的部件。 Kalix® 2940 is a bio-sourced, polyamide-based compound with 40% by weight glass fiber reinforcement. This material is specifically formulated for high strength and stiffness applications where good impact resistance and excellent dimensional stability after molding are required. The formulation also addresses warpage issues associated with the anisotropic shrinkage of glass fiber reinforced materials so that close tolerance molding is more easily achieved. Its low viscosity and excellent flow properties make the material ideal for filling parts with thin-walled sections such as those encountered in the mobile electronics industry. |
产品描述 Product Description
厂家:比利时索尔维 Solvay
类别:HPPA HPPA
用途:电气元件;手机;电气/电子应用领域;薄壁部件;
加工条件:注射成型 Injection Molding
性能特点: 机械强度好; 尺寸稳定性好; 成型周期快; 可表面喷涂; 低翘曲性; 电镀; 流动性高; 冲击性能好; 表面光泽度好; Good Rigidity,Low warping,Good surface appearance,High impact resistance,Good Dimensional Stability,High liquidity,Sprayable,Quick molding cycle,Electroplating
填料:玻璃纤维 40
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.40 | ||
收缩率 Shrinkage rate 2 |
|||
TD TD |
0.55 | % | |
MD MD |
0.15 | % | |
吸水率 Water absorption rate |
|||
23℃,24hr 23℃,24hr |
0.13 | % | ISO 62 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
13000 | MPa | ISO 527-2 |
拉伸强度 tensile strength |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ISO 527-2 | |
弯曲模量 Bending modulus |
MPa | ISO 178 | |
弯曲强度 bending strength |
MPa | ISO 178 | |
断裂弯曲应变 Fracture bending strain |
% | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
kJ/m² | ISO 180-1A | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
kJ/m² | ISO 180 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
玻璃化转变温度 Glass transition temperature |
℃ | ASTM D3418 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
介电常数 Dielectric constant |
|||
1 kHz 1 kHz |
|||
1 MHz 1 MHz |
|||
耗散因数 Dissipation factor |
|||
1 kHz 1 kHz |
|||
1 MHz 1 MHz |
|||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
备注 |
---|
2、Solvay Test Method. Shrink rates can vary with part design and processing conditions. Please consult a Solvay Technical Representative for more information. |
【新闻资讯】查看全部
可以不用弯腰推肉车啦!
2015-12-21 近日,RPC的Sæplast系列引入一种新把手,为它那广受欢迎的无声肉车Buggy改善人体工程学设计,提高肉车运行时的健康和安全水平。 新的智能把手 新的智能 |
可以不用弯腰推肉车啦! 近日,RPC的Sæplast系列产品引入一种新把手,为它那广火爆的无音肉车Buggy改进人体工学设计方案,提升肉车运作时的身心健康和安全性水准。 新的智能把手 新的智能把手在目前的把手上立即打槽竖直插进,提升手柄高宽比,让实际操作工作人员能更非常容易促进小轿车,且在手推车全过程可以维持站立。 Buggy肉车现阶段在食品类加工制造业中恒火爆。它专业为新鲜猪肉、干肉及其别的食品类而设计方案,符合实际法国DIN9797规范,而且净重仅有22Kg,便于实际操作。 强劲的三面聚乙烯设计方案和一体式构造,使Buggy肉车能长期性承担极端标准和不光滑应用。除此之外,与传统式不锈钢板车对比,此车大幅度降低了噪声。Buggy车具备四种不一样色调,让顾客可对于不一样生产制造地区应用不一样专用汽车。 智能把手选用聚乙烯生产制造,与Buggy肉车一样,是彻底可回收利用再运用的。 来源于:雅式橡塑制品网 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】
全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情
【精准,及时,权威!】
专业团队挖掘行情信息,第一时间发布行情
抱歉!该牌号暂无认证数据。
免责声明:参考价格是搜料网根据网络大数据拟合分析的结果,仅供参考。实际成交价取决但不限于以下因素:下单时间,付款方式,交货方式,数量,税费,色号,产地,项目信息。
抱歉!暂无数据。
抱歉!暂无数据。