牌号简介 About |
---|
Durethan® BKV 215 H2.0 901510 含有15%的玻璃纤维PA 6共聚物材料,用注射成型方式进行加工,具有良好的抗冲击性能和热老化稳定性。 Durethan® BKV215H2.0 901510 (Dry) PA 6-Copolymer, 15 % glass fibers, injection molding, improved impact strength, heat-aging stabilized Durethan® BKV215H2.0 901510 PA 6-Copolymer, 15 % glass fibers, injection molding, improved impact strength, heat-aging stabilized Durethan® BKV215H2.0 901510 PA 6-Copolymer, 15 % glass fibers, injection molding, improved impact strength, heat-aging stabilized |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.17 | g/cm³ | ISO 1183 |
表观密度 Apparent density |
0.60 | g/cm³ | ISO 60 |
收缩率 Shrinkage rate |
ISO 2577 | ||
TD:280℃,2.0 mm TD:280℃,2.0 mm 2 |
0.60 | % | ISO 2577 |
TD:120℃,2.0 mm,4 hrs TD:120℃,2.0 mm,4 hrs 3 |
0.10 | % | ISO 2577 |
MD:280℃,2.0 mm MD:280℃,2.0 mm 2 |
0.60 | % | ISO 2577 |
MD:120℃,2.0 mm,4 hrs MD:120℃,2.0 mm,4 hrs 3 |
% | ISO 2577 | |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
% | ISO 62 | |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
-30℃ -30℃ |
kJ/m² | ISO 179/1eA | |
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179/1eU | ||
-30℃ -30℃ |
kJ/m² | ISO 179/1eU | |
23℃ 23℃ |
kJ/m² | ISO 179/1eU | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180/1A | ||
-30℃ -30℃ |
kJ/m² | ISO 180-1A | |
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
ISO 180/1U | ||
-30℃ -30℃ |
kJ/m² | ISO 180/1U | |
23℃ 23℃ |
kJ/m² | ISO 180/1U | |
多轴向仪器化冲击能量 Multi axial instrumented impact energy |
ISO 6603-2 | ||
-30℃ -30℃ |
J | ISO 6603-2 | |
23℃ 23℃ |
J | ISO 6603-2 | |
多轴向仪器化冲击力峰值 Multi axial instrumented peak impact force |
ISO 6603-2 | ||
-30℃ -30℃ |
N | ISO 6603-2 | |
23℃ 23℃ |
N | ISO 6603-2 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
8.0 MPa,未退火 8.0 MPa, unannealed |
℃ | ISO 75-2/C | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
维卡软化温度 Vicat Softening Temp |
|||
B120 B120 |
℃ | ISO 306/B120 | |
熔融温度 Melting temperature 5 |
℃ | ISO 11357-3 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD:23~55℃ TD:23~55℃ |
1/℃ | ISO 11359-2 | |
MD:23~55℃ MD:23~55℃ |
1/℃ | ISO 11359-2 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
1.60 mm 1.60 mm |
UL 94 | ||
3.20 mm 3.20 mm |
UL 94 | ||
灼热丝可燃性指数 Glowing wire flammability index |
|||
2.0 mm 2.0 mm |
℃ | IEC 60695-2-12 | |
极限氧指数 Extreme oxygen index 7 |
% | ISO 4589-2 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
ISO Shortname ISO Shortname |
ISO 1874 | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
|||
断裂,23℃ Fracture, 23 ℃ |
MPa | ISO 527-2/5 | |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ISO 527-2/5 | |
弯曲模量 Bending modulus 4 |
|||
23℃ 23℃ 4 |
MPa | ISO 178-A | |
弯曲强度 bending strength |
ISO 178/A | ||
3.50% 应变,23℃ 3.50% strain, 23 ℃ |
MPa | ISO 178-A | |
23℃ 23℃ 4 |
MPa | ISO 178-A | |
弯曲应变 Bending strain 5 |
% | ISO 178/A | |
球压硬度 Ball hardness |
MPa | ISO 2039-1 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 60x60x2mm, 80°C MT, 600 bar |
3 60x60x2mm |
4 0.079 in/min |
5 2 mm/min |
6 10°C/min |
7 程序 A |
【新闻资讯】查看全部
塑料企业加大改造力度 杭州环保工程有序推进
2016-05-31 时间飞逝,转眼间,G20峰会已经进入倒计时,它对中国乃至整个世界都有着特殊的意义,对世界各国经济的发展,既是机遇也是挑战。中国作为今年的主席国,杭州作为被选中的峰会举办城市,更是不敢有任何懈怠。 据了解,外交部长王毅表示,中方将力争打造杭州峰会十大成果,其中有一项就是推动气候变化《巴黎协定》尽早生效。在长三角区域大气污染防治协作机制办公室会议中,环保部部长陈吉宁也表示,杭州G20峰会是一次重要国际会议,保障G20峰会期间良好的空气质量,是向世界展示我国生态文明建设成果的重要 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |