牌号简介 About |
---|
Exceed™ 3518PA树脂是一种茂金属乙烯-己烯共聚物。由Exceed™ 3518PA树脂制成的薄膜具有优异的拉伸性能和冲击和穿孔韧性。这些优良的性能,加上优良的可拉伸性,使这些树脂可用于单层和多层铸造包装膜。Exceed™ 3518PA不含TNPP。 Exceed 3518PA resin is an ethylene 1-hexene copolymer. Films made from Exceed 3518PA resin have outstanding tensile properties and impact and puncture toughness. These superior properties, along with excellent drawability, make these resins versatile for both monolayer and multilayer cast packaging film. Exceed 3518PA is TNPP-free. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.918 | g/cm³ | ExxonMobil Method |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
3.5 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
割线模量 Secant modulus |
|||
1% 正割,MD 1% secant, MD |
110 | MPa | |
1% 正割,TD 1% secant, TD |
131 | MPa | |
拉伸强度 tensile strength |
|||
MD,断裂 MD, fracture |
86.2 | MPa | |
TD,断裂 TD, fracture |
MPa | ||
拉伸应变 Tensile strain |
|||
MD,断裂 MD, fracture |
% | ||
TD,断裂 TD, fracture |
% | ||
落锤冲击 Drop hammer impact |
g | ASTM D1709-A | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
|||
MD MD |
g | ||
TD TD |
g | ||
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
60° 60° |
ASTM D2457 | ||
雾度 Haze |
% | ASTM D1003 | |
法律声明 Legal Statement |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
GET!!注塑或塑料加工检验术语及定义!请收藏~
2016-07-19 塑料件注塑加工检验技术术语 熔接痕(俗称:夹水纹;其它名称:夹线、夹纹) 定义:在注塑加工过程中,两股料流相遇时,其世界面处未完全熔合而造成的痕迹。 缩痕(俗称:缩水;其它名称:无) 定义:塑料件在模腔内冷却凝固时,由于塑料件壁厚不均匀、射胶压力不足、冷却时间不够等原因而在塑料件表面产生的凹陷。 技术术语:无(俗称:气纹;其它名称:无) |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |