牌号简介 About |
---|
InnoPlus LL7410D1树脂是一种线性低密度聚乙烯与丁烯共聚单体,低含量的滑动和抗阻塞。这一等级提供了优良的机械加工性能的转换线。从InnoPlus LL7410D1挤出的薄膜具有较高的拉伸强度、延伸率、良好的韧性和突出的击穿强度。适用于管状吹膜加工。典型应用:InnoPlus LL7410D1推荐用于生产通用薄膜、衬垫、食品包装、重型和农用薄膜。 InnoPlus LL7410D1 resin is a linear low density polyethylene with butene comonomers, with low content of slip and antiblock. This grade offers the excellent machinability on conversion lines. Films extruded from InnoPlus LL7410D1 have high tensile strength, elongation, good toughness and outstanding puncture strength. It is available for tubular blown film processing. Typical Applications : InnoPlus LL7410D1 is recommended for producing the general purpose films, liners, food packaging, heavy duty and agricultural films. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.920 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
1.0 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
25 | µm | |
割线模量 Secant modulus |
|||
1% 正割,MD:25 µm,吹塑薄膜 1% secant, MD: 25 µ m, blow molded film |
190 | MPa | |
1% 正割,TD:25 µm,吹塑薄膜 1% secant, TD: 25 µ m, blow molded film |
230 | MPa | |
拉伸强度 tensile strength |
|||
MD,断裂,25 µm,吹塑薄膜 MD, fracture, 25 µ m, blow molded film |
MPa | ||
TD,断裂,25 µm,吹塑薄膜 TD, fracture, 25 µ m, blow molded film |
MPa | ||
拉伸应变 Tensile strain |
|||
MD,断裂,25 µm,吹塑薄膜 MD, fracture, 25 µ m, blow molded film |
% | ||
TD,断裂,25 µm,吹塑薄膜 TD, fracture, 25 µ m, blow molded film |
% | ||
落锤冲击 Drop hammer impact |
|||
25 µm,吹塑薄膜 25 µ m, blow molded film |
g | ASTM D1709 | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
|||
MD:25 µm,吹塑薄膜 MD: 25 µ m, blow molded film |
g | ||
TD:25 µm,吹塑薄膜 TD: 25 µ m, blow molded film |
g | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
熔融峰值温度 Melting peak temperature |
℃ | ASTM D3418 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,25 µm,吹塑薄膜 45 °, 25 µ m, blow molded film |
ASTM D2457 | ||
雾度 Haze |
|||
25 µm,吹塑薄膜 25 µ m, blow molded film |
% | ASTM D1003 |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
超耐寒塑料初次在俄罗斯研制出
2018-07-04 俄媒称,莫斯科国立科技大学的专家研制出可在不低于零下80摄氏度的严寒中使用的耐摩擦聚合材料。在北极大规模开采矿物需要复杂的工业设备和有大量摩擦单元的重型装备。在雅库特的所谓寒极地带曾经记录过零下67摄氏度的低温。 据俄罗斯《消息报》网站7月2日报道,北极的气候条件对设备的稳定性提出了苛刻的要求。在交通不便的情况下,一旦机械轴承因经受不住严寒而损坏,就可能意味着重大经济损失。对开采机构来说,在机器中使用能够长期经受非标准环境考验的可活动部件至关重要。 报道称, |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |