牌号简介 About |
---|
注塑成型,未增强 |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
成型收缩率 Molding shrinkage Molding shrinkage |
|||
平行 parallel,150x105x3; 270 °C / WZ 80 °C; 500 bar Parallel, 150x105x3; 270 ° C/WZ 80 ° C; 500 bar |
1.02 | % | ISO 2577 |
横向 transverse,150x105x3; 270 °C / WZ 80 °C; 500 bar Horizontal translation, 150x105x3; 270 ° C/WZ 80 ° C; 500 bar |
1.06 | % | ISO 2577 |
后期收缩率 Post- shrinkage Post shrinkage |
|||
平行 parallel,150x105x3; 120 °C; 4 h Parallel, 150x105x3; 120 ° C; 4 hours |
0.32 | % | ISO 2577 |
横向 transverse,150x105x3; 120 °C; 4 h Horizontal translation, 150x105x3; 120 ° C; 4 hours |
0.4 | % | ISO 2577 |
吸水率 Water absorption Water absorption |
|||
饱和值 Saturation value,23 °C Saturation value, 23 ° C |
10 | % | ISO 62 |
平衡值 Equilibrium value,23 °C; 50 % RH Equilibrium value, 23 ° C; 50% RH |
% | ISO 62 | |
密度 Density Density |
kg/m³ | ISO 1183 | |
堆积密度 Bulk density Bulk density |
kg/m³ | ISO 60 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus Tensile modulus |
|||
1 mm/min,干燥 dry 1 mm/min, dry |
MPa | ISO 527-2 | |
1 mm/min,湿润 cond. 1 mm/min, moist cond |
MPa | ISO 527-2 | |
蠕变 creep,1h Creep, 1h |
MPa | ISO 899-1 | |
蠕变 creep,1000h Creep, 1000h |
MPa | ISO 899-1 | |
拉伸应力 Tensile Stress Tensile Stress |
|||
50 mm/min,干燥 dry,屈服 yld 50 mm/min, dry, yield yld |
MPa | ISO 527-2 | |
50 mm/min,湿润 cond.,屈服 yld 50 mm/min, moist cond, Yield yld |
MPa | ISO 527-2 | |
拉伸应变 Tensile Strain Tensile Strain |
|||
50 mm/min,干燥 dry,断裂 break |
% | ISO 527-2 | |
50 mm/min,湿润 cond.,断裂 break 50 mm/min, moist cond, Break |
% | ISO 527-2 | |
50 mm/min,干燥 dry,屈服 yld |
% | ISO 527-2 | |
50 mm/min,湿润 cond.,屈服 yld 50 mm/min, moist cond, Yield yld |
% | ISO 527-2 | |
弯曲模量 Flexural Modulus Flexural Modulus |
|||
2 mm/min,干燥 dry 2 mm/min, dry |
MPa | ISO 178 | |
2 mm/min,湿润 cond. 2 mm/min, moist cond |
MPa | ISO 178 | |
弯曲强度 Flexural Strength |
|||
2 mm/min ,湿润 cond. 2 mm/min, moist cond |
MPa | ISO 178 | |
2 mm/min ,干燥 dry 2 mm/min, dry |
MPa | ISO 178 | |
2 mm/min ,3.5% 应力 Strain,干燥 dry 2 mm/min, 3.5% stress Strain, dry dry |
MPa | ISO 178 | |
2 mm/min ,3.5% 应力 Strain,湿润 cond. 2 mm/min, 3.5% Stress Strain, Wet Cond |
MPa | ISO 178 | |
弯曲应变 Flexural Strain Flexural Strain |
|||
2 mm/min ,干燥 dry 2 mm/min, dry |
% | ISO 178/A | |
2 mm/min ,湿润 cond. 2 mm/min, moist cond |
% | ISO 178/A | |
穿刺最大力 Puncture maximum force Puncture maximum force |
|||
23℃ 23℃ |
N | ISO 6603-2 | |
-30℃ -30℃ |
N | ISO 6603-2 | |
穿刺能量 Puncture energy Puncture energy |
|||
23℃ 23℃ |
J | ISO 6603-2 | |
-30℃ -30℃ |
J | ISO 6603-2 | |
球压硬度 Ball indentation hardness Ball indentation hardness |
|||
干燥 dry Dry |
N/mm² | ISO 2039-1 | |
湿润 cond. Wet Cond |
N/mm² | ISO 2039-1 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
熔融温度 Melting temperature Melting temperature |
℃ | ISO 11357-3 | |
热变形温度 HDT Hot deformation temperature HDT |
|||
1.8 MPa 1.8 MPa |
℃ | ISO 75-1,-2 | |
0.45 MPa 0.45 MPa |
℃ | ISO 75-1,-2 | |
8.0 MPa 8.0 MPa |
℃ | ISO 75-1,-2 | |
维卡软化温度 Vicat softening temperature Vicat softening temperature |
|||
50 N; 120 °C/h 50 N; 120 °C/h |
℃ | ISO 306/B | |
50 N; 50 °C/h 50 N; 50 °C/h |
℃ | ISO 306/B | |
线性热膨胀系数 Coefficient of linear thermal expansion |
|||
平行 parallel Parallel |
×10-4/℃ | ISO 11359-2 | |
横向 transverse Horizontal transformation |
×10-4/℃ | ISO 11359-2 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
|||
1.5 mm 1.5 mm |
calss | UL 94 | |
0.4 mm 0.4 mm |
calss | UL 94 | |
极限氧指数 Extreme oxygen index |
% | ISO 4589-2 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy notched impact strength Charpy notched impact strength |
|||
23℃,干燥 dry 23 ℃, dry |
kJ/m² | ISO 179/1eA | |
23℃,湿润 cond. 23 ℃, moist cond |
kJ/m² | ISO 179/1eA | |
-30℃,干燥 dry -30 ℃, dry |
kJ/m² | ISO 179/1eA | |
-30℃,湿润 cond. -30 ℃, moist cond |
kJ/m² | ISO 179/1eA | |
悬臂梁缺口冲击强度 Izod notched impact strength |
|||
23℃,干燥 dry 23 ℃, dry |
KJ/m² | ISO 180/1A | |
23℃,湿润 cond. 23 ℃, moist cond |
KJ/m² | ISO 180/1A | |
电气性能 ELECTRICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
介电常数 Relative permittivity |
|||
100 Hz,干燥 dry 100 Hz, dry |
IEC 60250 | ||
100 Hz,湿润 cond. 100 Hz, moist cond |
IEC 60250 | ||
1 MHz,干燥 dry 1 MHz, dry |
IEC 60250 | ||
1 MHz,湿润 cond. 1 MHz, moist cond |
IEC 60250 | ||
耗散因数 Dissipation factor Dissipation factor |
|||
100 Hz,干燥 dry 100 Hz, dry |
IEC 60250 | ||
100 Hz,湿润 cond. 100 Hz, moist cond |
IEC 60250 | ||
1 MHz,干燥 dry 1 MHz, dry |
IEC 60250 | ||
1 MHz,湿润 cond. 1 MHz, moist cond |
IEC 60250 | ||
体积电阻率 Volume resistivity |
|||
干燥 dry Dry |
ohm·m | IEC 60093 | |
湿润 cond. Wet Cond |
ohm·m | IEC 60093 | |
表面电阻率 Surface resistivity Surface resistivity |
|||
干燥 dry Dry |
ohm | IEC 60093 | |
湿润 cond. Wet Cond |
ohm | IEC 60093 | |
介电强度 Electric strength Electric strength |
|||
干燥 dry,1 mm |
kV/mm | IEC 60243-1 | |
湿润 cond. ,1 mm |
kV/mm | IEC 60243-1 | |
相比漏电起痕指数 Comparative tracking index Compared tracking index |
|||
方法A,CIT Method A, CIT |
IEC 60112 | ||
方法B,CIT M Method B, CIT M |
IEC 60112 |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
禁塑为生物降解材料带来风口
2020-09-21 搜料网资讯: 南澳大利亚州议会近日通过了禁止使用一次性塑料的法案,虽然受疫情影响,新规定推迟至2021年实施,但世界各地频现禁塑令还是引起业界极大关注。 塑料垃圾一直是困 |
禁塑为生物降解材料带来风口 搜料网资讯:南澳大利亚州议会近日通过了禁止使用一次性塑料的法案,虽然受疫情影响,新规定推迟至2021年实施,但世界各地频现“禁塑令”还是引起业界极大关注。
塑料垃圾一直是困扰全球的环境问题。据统计,每年约有800万吨的塑料进入到海洋中。这意味着,全球平均每1米的海岸线就会新增大约15个塑料袋,而这些塑料若要在自然环境下完全分解,需要470年。触目惊心的塑料垃圾污染给海洋生态以及地球环境造成了严重的伤害。塑料垃圾污染每年也给全球经济造成巨额损失。在此背景下,生物降解材料逐渐成为世界各国追捧的缓解塑料污染的有效方式。 据不完全统计,全球已有60多个国家出台了限制塑料使用的政策或法令,通过对塑料袋征税、自愿协议、全面禁令等方式推广使用生物可降解材料。随着对一次性不易回收塑料制品禁限政策的出台,生物降解塑料的发展得到了进一步推动。 发达国家中以美国、欧盟、日本的废塑料回收利用率高达50%以上。发展中以及不发达国家废塑料的回收利用率只有20%左右。不完善的废弃塑料垃圾处理所造成的污染已成为社会关注焦点,这促使生物降解塑料成为研发热点。全球生物基材料产能约3300万吨,生物基聚合物约650万吨,年复合增长率为27%。 聚乳酸市场蓝海显现也是生物降解塑料迎来风口的一个特征。生物降解塑料作为塑料的一个种类,具有传统塑料优异的加工性能,同时还具备生物降解特性。在可降解塑料中,最常见也是应用最广的当属聚乳酸(PLA)。而随着生物降解塑料的发展提速,日前,聚乳酸价格飞速上涨,一货难求。全球缺口为10万~15万吨。 可以说,禁/限塑令为生物降解材料带来了黄金发展机遇,与此同时,兼具塑料特质并能满足环保要求的生物可降解材料岂不是也成为行业转型、保持可持续发展、保护大环境的“利器”? |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
抱歉!该牌号暂无认证数据。
- 电动汽车零件壳体的轻量化
- 2022-07-20 0
- Durethan® BKV 50 H3.0 000000 含有50%的玻璃纤维增强的PA 6材料,用注射成型的方式进行加工,具有良好的热老化稳定性。
- 阅读全文
电动汽车零件壳体的轻量化
2-满足轻量化需求
3-拥有良好的强度与刚度
4-对冷却剂有更好的耐受性
5-优异的耐热性,能长期承受85℃的温度
6-热稳定性好
7-对水乙二醇混合物的长期耐受性好
8-爆破载荷高达10bar
抱歉!暂无数据。