牌号简介 About |
---|
冷热水管道用高密度湿固化聚乙烯复合材料。适用于在140°F和80 psi工作条件下连续工作的DR 9管道应用。pexidan l/t(包括l/t-uv和l/t eclipse)是一种高密度pex系统,由硅烷接枝碱化合物A-1001和催化剂母粒cat-003(或a-1022和cat-117)组成。当以适当比例混合和挤压时,双组分系统会产生一种材料,该材料可通过暴露于水分或在90-95°C的热水中浸泡而交联。根据NSF国际标准14和61以及加拿大标准协会标准B137.5,pexidan L/T被列为可交联材料。NSFI对ASTM F876和ASTM F2023的认证证明其具有优异的耐高温氯化水氧化性能。西单L/T可用于国内连续循环系统,被NSF列为NSF PW CL5/PEX 5006材料。 High density moisture-curable PE compound for hot & cold water plumbing pipe. Suitable for DR 9 pipe applications in continuous service at operating conditions of 140°F and 80 psi. PEXIDAN ® L/T (including L/T-UV and L/T Eclipse) is a high density PEX system consisting of a silane grafted base-compound A-1001 and a catalyst masterbatch CAT-003 (or A-1022 and CAT-117). When mixed and extruded in the proper proportions, the two-component system results in a material that is crosslinkable by exposure to moisture or by immersion in hot water at 90-95°C. PEXIDAN ® L/T is listed by NSF International to standards 14 and 61 and to Canadian Standards Association standard B137.5. NSFI certification to ASTM F876 and ASTM F2023 testifies to its superior resistance to oxidation by hot, chlorinated water. PEXIDAN ® L/T is permitted to be used in domestic continuous re-circulation systems and is listed by NSF as a NSF-pw CL5 / PEX 5006 material. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density 2 |
0.946 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
0.70 | g/10min | ASTM D1238 |
交叉结合的程度 The degree of cross combination |
> 70 | % | ASTM D2765 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
-40℃ -40℃ |
2310 | MPa | |
0℃ 0℃ |
1690 | MPa | |
23℃ 23℃ |
MPa | ||
拉伸强度 tensile strength |
|||
屈服,23℃ Yield, 23 ℃ |
MPa | ||
屈服,82℃ Yield, 82 ℃ |
MPa | ||
屈服,93℃ Yield, 93 ℃ |
MPa | ||
断裂,23℃ Fracture, 23 ℃ |
MPa | ||
断裂,82℃ Fracture, 82 ℃ |
MPa | ||
断裂,93℃ Fracture, 93 ℃ |
MPa | ||
拉伸应变 Tensile strain |
|||
屈服,23℃ Yield, 23 ℃ |
% | ||
屈服,34℃ Yield, 34 ℃ |
% | ||
屈服,82℃ Yield, 82 ℃ |
% | ||
断裂,23℃ Fracture, 23 ℃ |
% | ||
断裂,82℃ Fracture, 82 ℃ |
% | ||
断裂,93℃ Fracture, 93 ℃ |
% | ||
弯曲模量 Bending modulus |
|||
-40℃ -40℃ |
MPa | ||
0℃ 0℃ |
MPa | ||
23℃ 23℃ |
MPa | ||
流体静力学设计基础 - @ 68% DOC Fundamentals of Hydrostatic Design - @ 68% DOC |
|||
23℃ 23℃ |
MPa | ||
82℃ 82℃ |
MPa | ||
93℃ 93℃ |
MPa | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:-100~85℃ MD:-100~85℃ |
1/℃ | ASTM D696 | |
比热 specific heat |
|||
23℃ 23℃ |
J/kg/℃ | ||
氧感应时间 Oxygen sensing time |
|||
220℃ 220℃ |
min | ASTM D3895 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
高温伸长率 High temperature elongation 3 |
|||
负荷下伸长率:150℃ Elongation under load: 150 ℃ |
% | ||
permanent elongation(set) after cooling:150℃ permanent elongation(set) after cooling:150℃ |
% | ||
|
备注 |
---|
2. 23°C |
3. 15 minutes, 0.2 N/mm² load |
【新闻资讯】查看全部
双易塑料制品“回”字标识启用
2021-07-20 搜料网资讯: 7月16日,在绿色再生塑料供应链(GRPG)论坛新闻发布会上,易回收易再生塑料制品回字标识(简称双易标识)正式启用,这将使更多塑料废弃物回到循环体系中,助力塑料循环 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |