牌号简介 About |
---|
Sepaz LW8842FR是一种gf/mf 35%增强改性PPO产品。该产品具有高模量、低翘曲、加工性好等特点。 LNP LUBRICOMP OFL36 is a compound based on PPS - Linear resin containing 30% Glass Fiber, 15% PTFE. Added features of this grade include: Wear Resistant. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.69 | g/cm³ | ASTM D792 |
密度 Density |
1.70 | g/cm³ | ISO 1183 |
收缩率 Shrinkage rate |
ISO 294-4 | ||
TD:24 hrs TD:24 hrs |
0.60 to 0.80 | % | ASTM D955 |
MD:24 hrs MD:24 hrs |
0.10 to 0.20 | % | ASTM D955 |
TD:24 hrs TD:24 hrs |
0.30 to 0.48 | % | ISO 294-4 |
MD:24 hrs MD:24 hrs |
% | ISO 294-4 | |
吸水率 Water absorption rate |
|||
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
24hr,50% RH 24hr,50% RH |
% | ASTM D570 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus 2 |
MPa | ASTM D638 | |
拉伸模量 Tensile modulus |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength 3 |
|||
断裂 fracture |
MPa | ISO 527-2/5 | |
断裂 fracture 3 |
MPa | ASTM D638 | |
拉伸应变 Tensile strain 4 |
|||
断裂 fracture |
% | ISO 527-2/5 | |
断裂 fracture 4 |
% | ASTM D638 | |
弯曲模量 Bending modulus 5 |
MPa | ISO 178 | |
50 mm跨距 50 mm span 4 |
MPa | ASTM D790 | |
弯曲强度 bending strength |
MPa | ISO 178 | |
断裂,50 mm跨度 Fracture, 50 mm span 5 |
MPa | ASTM D790 | |
摩擦系数 friction coefficient |
ASTM D3702 Modified | ||
动态 dynamic |
ASTM D3702 Modified | ||
静态 static state |
ASTM D3702 Modified | ||
磨损因数 Wear factor |
ASTM D3702 Modified | ||
Ring Ring |
10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified | |
Washer Washer |
10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
J/m | ASTM D256 | |
23℃ 23℃ 6 |
kJ/m² | ISO 180-1A | |
23℃ 23℃ |
J/m | ASTM D4812 | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam 5 |
|||
23℃ 23℃ 5 |
kJ/m² | ISO 180/1U | |
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
ASTM D3763 | ||
23℃,Energy at Peak Load 23℃,Energy at Peak Load |
J | ASTM D3763 | |
23℃,Total Energy 23℃,Total Energy |
J | ASTM D3763 | |
多轴向仪器化冲击能量 Multi axial instrumented impact energy |
J | ISO 6603-2 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火,64 mm跨距 1.8 MPa, unannealed, 64 mm span 7 |
℃ | ISO 75-2/Af | |
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
0.45 MPa,未退火,64 mm跨距 0.45 MPa, unannealed, 64 mm span 7 |
℃ | ISO 75-2/Bf | |
0.45 MPa,未退火,3.2 mm 0.45 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD:-40~40℃ TD:-40~40℃ |
1/℃ | ISO 11359-2 | |
TD:-40~40℃ TD:-40~40℃ |
1/℃ | ASTM E831 | |
TD:-30~30℃ TD:-30~30℃ |
1/℃ | ASTM D696 | |
MD:-40~40℃ MD:-40~40℃ |
1/℃ | ISO 11359-2 | |
MD:-40~40℃ MD:-40~40℃ |
1/℃ | ASTM E831 | |
MD:-30~30℃ MD:-30~30℃ |
1/℃ | ASTM D696 |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
前8月国有控股企业完成利润总额13473亿元
2018-09-28 国家统计局9月27日发布的工业企业财务数据显示,2018年1-8月份,全国规模以上工业企业利润总额同比增长16.2%。其中,化学原料和化学制品制造业增长25%。 1-8月份,规模以上工业企业中,国有控股企业实现利润总额13473亿元,同比增长26.7%;集体企业实现利润总额139.2亿元,增长3.2%;股份制企业实现利润总额31323.9亿元,增长20.1%;外商及港澳台商投资企业实现利润总额10906.4亿元,增长7.6%;私营企业实现利润总额11485.6亿元,增长10 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |