牌号简介 About |
---|
高流量PPO+PA。配电箱应用。 High flow PPO+PA. Power distribution box applications. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.10 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
280℃,5.0kg 280℃,5.0kg |
97 | g/10min | ASTM D1238 |
收缩率 Shrinkage rate |
|||
MD:3.2 mm MD:3.2 mm |
1.2 到 1.4 | % | |
TD:3.2 mm TD:3.2 mm |
1.1 到 1.4 | % | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus 2 |
1950 | MPa | ASTM D638 |
拉伸强度 tensile strength |
|||
屈服 yield 3 |
MPa | ASTM D638 | |
屈服 yield |
MPa | ISO 527-2/50 | |
断裂 fracture 3 |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
屈服 yield 3 |
% | ASTM D638 | |
断裂 fracture 3 |
% | ASTM D638 | |
断裂 fracture |
% | ISO 527-2/5 | |
弯曲模量 Bending modulus |
|||
100 mm跨距 100 mm span 4 |
MPa | ASTM D790 | |
-- -- 5 |
MPa | ISO 178 | |
弯曲强度 bending strength 4 |
|||
屈服,100 mm跨度 Yield, 100 mm span 4 |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
-30℃ -30℃ |
J/m | ASTM D256 | |
23℃ 23℃ |
J/m | ASTM D256 | |
-40℃ -40℃ 6 |
kJ/m² | ISO 180-1A | |
-20℃ -20℃ 6 |
kJ/m² | ISO 180-1A | |
23℃ 23℃ 6 |
kJ/m² | ISO 180-1A | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
-30℃ -30℃ |
J/m | ||
23℃ 23℃ |
J/m | ||
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
|||
-30℃,Total Energy -30℃,Total Energy |
J | ||
23℃,Total Energy 23℃,Total Energy |
J | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火,3.2 mm 0.45 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
0.45 MPa,未退火,6.4 mm 0.45 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
0.45 MPa,未退火,4.0 mm,64 mm跨距 0.45 MPa, unannealed, 4.0 mm, 64 mm span 6 |
℃ | ISO 75-2/Bf | |
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火,6.4 mm 1.8 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火,4.0 mm,64 mm跨距 1.8 MPa, unannealed, 4.0 mm, 64 mm span 6 |
℃ | ISO 75-2/Af | |
维卡软化温度 Vicat Softening Temp |
|||
-- -- |
℃ | ASTM D1525 7 | |
B50 B50 |
℃ | ISO 306 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:-40~40℃ MD:-40~40℃ |
1/℃ | ||
TD:-40~40℃ TD:-40~40℃ |
1/℃ |
备注 |
---|
2. 50 mm/min |
3. 类型 1, 50 mm/min |
4. 2.6 mm/min |
5. 2.0 mm/min |
6. 80*10*4 mm |
7. 速率 A (50°C/h), 载荷2 (50N) |
【新闻资讯】查看全部
长岭炼化聚丙烯成品包装线改造项目中交
2021-04-02 搜料网资讯: 3月28日,长岭炼化聚丙烯装置成品包装线改造项目通过安全、环保、质量等多项验收,顺利中交进入设备调试阶段,为企业多产快出聚丙烯产品提供了硬件支撑。 长岭炼化 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |