牌号简介 About |
---|
TC-300 A/B聚氨酯泡沫系统是一系列具有多种密度的刚性、闭孔泡沫材料。TC-300可以通过快速、剧烈的混合作用,或通过在钻头中使用快速搅拌器,以提供小到大数量的高剪切混合料,方便手工小批量混合。对于低到高的生产,这些泡沫系统也可以使用BJB的中心点仪表混合设备来分配机器。可在脱模后的短时间内用砂纸打磨、钉合、涂漆或染色。还提供6_、10_和16_密度。易于手工混合或机械铸造,流入型腔,快速脱模,物理性能优异。 The TC-300 A/B polyurethane foam system is a series of rigid, closed cell foams available in a variety of densities. The TC-300 can be easily mixed by hand in small batches using a rapid, vigorous mixing action or by using a Jiffy Mixer® in a drill to provide a high-shear mix in small to large quantities. For low to high production, these foam systems can also be machine dispensed using BJB's Centerpointe Meter-Mix equipment. Cured parts can be sanded, stapled, painted or stained within a short time after demolding. Also available in 6#, 10#, and 16# densities. Easy to hand mix or machine cast Flows well into mold cavities Fast Demolds Excellent physical properties |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
|||
-- -- 2 |
1.07 | g/cm³ | |
-- -- 3 |
1.23 | g/cm³ | |
K(磨损)系数(25℃) K (wear) coefficient (25 ℃) |
0.150 | ASTM C177 | |
密度 Density 4 |
0.0400 到 0.0561 | g/cm³ | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
0.552 | MPa | ASTM D1623 |
弯曲强度 bending strength |
MPa | ASTM D790 | |
压缩强度 compressive strength |
MPa | ASTM D1621 | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
水气透过率 Water vapor transmittance |
perm/in | ASTM E96 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
介电常数 Dielectric constant |
|||
1 MHz 1 MHz |
ASTM D150 | ||
耗散因数 Dissipation factor |
|||
1 MHz 1 MHz |
ASTM D150 | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热固组件 Thermosetting components |
|||
部件 A Component A |
|||
部件 B Component B |
|||
贮藏期限 Storage period |
wk | ||
热固性混合粘度 Thermosetting mixed viscosity |
|||
25℃ 25℃ 5 |
cP | ||
25℃ 25℃ 6 |
cP | ||
Cream Time Cream Time |
sec | ||
脱模时间 stripping time |
min | ||
胶凝时间 Gelation time |
min | ||
Tack Free Time Tack Free Time |
min | ||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Closed Cell Content Closed Cell Content |
% | ASTM D2856 |
备注 |
---|
2. Part B, 77°F |
3. Part A, 77°F |
4. Free rise |
5. Part A |
6. Part B |
【新闻资讯】查看全部
模具尺寸和塑料膨胀率经典引见!
2017-02-14 设计塑料模时,确定了模具结构之後即可对模具的各部分进行详细设计,即确定各模板和零件的尺寸,型腔和型芯尺寸等。这时将涉及有关材料收缩率等主要的设计参数。因而只有具体地掌握成形塑料的收缩率才能确定型腔各部分的尺寸。即使所选模具结构正确,但所用参数不当,就不可能生产出品质合格的塑件。 一、塑料收缩率及其影响因素 热塑性塑料的特性是在加热後膨胀,冷却後收缩,当然加压以後体积也将缩小。 在注塑成形过程中,首先将熔融塑料注射入模具型腔内,充填结束後熔料冷却固化,从模具中 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
电邮一份说明书
PDF文档名:搜料网-BJB Polyurethane TC-300 A/B 3# Density证书
发送至:(多个地址,中间以逗号隔开)
发送一份副本给我:您还没有填写邮箱!(点击完善资料)