牌号简介 About |
---|
Formolene® HB5502B是专为需要优良的刚度和应力抗裂性能的应用而设计的。可作为通用吹塑树脂或片材挤出热成型树脂。Formolene® HB5502B符合美国食品和药物管理局在21CFR 177.1520中规定的所有要求,包括用于直接食品接触的聚烯烃制品的安全使用。 Formolene® HB5502B is designed for applications requiring excellent stiffness and stress crack resistance properties. It may be used as a general-purpose blow molding resin or sheet extrusion thermoforming resin. Formolene® HB5502B meets all requirements of the U.S. Food and Drug Administration as specified in 21 CFR 177.1520, covering safe use of polyolefin articles intended for direct food contact. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.955 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
0.35 | g/10min | ASTM D1238 |
抗环境应力开裂 ESCR(Environmental Stress Cracking Resistance) |
|||
模压成型,F50 Molded into shape, F50 |
35.0 | hr | ASTM D1693B |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength 2 |
|||
屈服,模压成型 Yield, molding 2 |
28.0 | MPa | ASTM D638 |
拉伸应变 Tensile strain 2 |
|||
断裂,模压成型 Fracture, molded 2 |
> 600 | % | ASTM D638 |
弯曲模量 Bending modulus |
|||
模压成型 Compression Molding |
MPa | ASTM D790 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
℃ | ASTM D746 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 类型 4, 2.0 in/min |
【新闻资讯】查看全部
中塑协XPS专委会举行一届二次理事会暨行业开展研讨会
2016-01-20 2016年1月11日至13日,“中国塑协聚苯乙烯挤出发泡板材(XPS)专委会一届二次理事会暨行业发展研讨会”在山东寿光晨鸣国际大酒店隆重召开。本次会议由中国塑料加工工业协会主办,中国塑协聚苯乙烯挤出发泡板材(XPS)专委会承办,山东旭锐新材有限公司协办。南京越升挤出机械有限公司、林德集团、郑州兆明机械有限公司为本次会议提供支持。中国塑料加工工业协会常务副理事长曹俭出席大会并发表重要讲话。一百五十余位来自XPS相关领域的专家学者和企业代表参加了此次会议,大会在欢乐祥和的气氛中圆满结束。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |