| 牌号简介 About |
|---|
| Lofex A5110聚酯薄膜经拉伸强度、适当的延伸率和热收缩率等性能优异的单侧电晕处理后,薄膜呈雾状。因其具有优异的运行性能,易于用合适的产品进行处理,故可采用离型膜。另外,它是一种可以根据客户需求进行厚度控制的产品。 LOFEX ® A5110 Polyester film is hazy and one side corona treated with excellent properties by tensile strength, proper elongation and the thermal contraction rate. It can use by release film because it has excellent run, easy treatment by suitable product. Also, it is a product that thickness control is possible according to customer needs. |
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
表面张力 surface tension |
|||
|
50.0 µm 50.0 µm |
52 | mN/m | |
|
75.0 µm 75.0 µm |
52 | mN/m | |
|
100.0 µm 100.0 µm |
52 | mN/m | |
|
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸强度 tensile strength |
注册或登录后
所有资料免费
|
ASTM D882 | |
|
MD,屈服,50 µm MD, yield, 50 µ m |
注册或登录后
所有资料免费
|
MPa | ASTM D882 |
|
MD,屈服,75 µm MD, yield, 75 µ m |
注册或登录后
所有资料免费
|
MPa | ASTM D882 |
|
MD,屈服,100 µm MD, yield, 100 µ m |
注册或登录后
所有资料免费
|
MPa | ASTM D882 |
|
TD,屈服,50 µm TD, yield, 50 µ m |
注册或登录后
所有资料免费
|
MPa | ASTM D882 |
|
TD,屈服,75 µm TD, yield, 75 µ m |
注册或登录后
所有资料免费
|
MPa | ASTM D882 |
|
TD,屈服,100 µm TD, yield, 100 µ m |
注册或登录后
所有资料免费
|
MPa | ASTM D882 |
|
拉伸应变 Tensile strain |
注册或登录后
所有资料免费
|
ASTM D882 | |
|
MD,断裂,50 µm MD, fracture, 50 µ m |
注册或登录后
所有资料免费
|
% | ASTM D882 |
|
MD,断裂,75 µm MD, fracture, 75 µ m |
注册或登录后
所有资料免费
|
% | ASTM D882 |
|
MD,断裂,100 µm MD, fracture, 100 µ m |
注册或登录后
所有资料免费
|
% | ASTM D882 |
|
TD,断裂,50 µm TD, fracture, 50 µ m |
注册或登录后
所有资料免费
|
% | ASTM D882 |
|
TD,断裂,75 µm TD, fracture, 75 µ m |
注册或登录后
所有资料免费
|
% | ASTM D882 |
|
TD,断裂,100 µm TD, fracture, 100 µ m |
注册或登录后
所有资料免费
|
% | ASTM D882 |
|
F5 F5 |
注册或登录后
所有资料免费
|
ASTM D882 | |
|
MD:50.0 µm MD:50.0 µm |
注册或登录后
所有资料免费
|
MPa | ASTM D882 |
|
MD:75.0 µm MD:75.0 µm |
注册或登录后
所有资料免费
|
MPa | ASTM D882 |
|
MD:100.0 µm MD:100.0 µm |
注册或登录后
所有资料免费
|
MPa | ASTM D882 |
|
TD:50.0 µm TD:50.0 µm |
注册或登录后
所有资料免费
|
MPa | ASTM D882 |
|
TD:75.0 µm TD:75.0 µm |
注册或登录后
所有资料免费
|
MPa | ASTM D882 |
|
TD:100.0 µm TD:100.0 µm |
注册或登录后
所有资料免费
|
MPa | ASTM D882 |
|
光学性能 OPTICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
光泽度 gloss |
注册或登录后
所有资料免费
|
ASTM D523 | |
|
60°,50.0 µm 60°,50.0 µm |
注册或登录后
所有资料免费
|
ASTM D523 | |
|
60°,75.0 µm 60°,75.0 µm |
注册或登录后
所有资料免费
|
ASTM D523 | |
|
60°,100 µm 60°,100 µm |
注册或登录后
所有资料免费
|
ASTM D523 | |
|
透光率 Light Transmission |
注册或登录后
所有资料免费
|
ASTM D1003 | |
|
50.0 µm 50.0 µm |
注册或登录后
所有资料免费
|
% | ASTM D1003 |
|
75.0 µm 75.0 µm |
注册或登录后
所有资料免费
|
% | ASTM D1003 |
|
100 µm 100 µm |
注册或登录后
所有资料免费
|
% | ASTM D1003 |
|
雾度 Haze |
注册或登录后
所有资料免费
|
ASTM D1003 | |
|
50 µm 50 µm |
注册或登录后
所有资料免费
|
% | ASTM D1003 |
|
75.0 µm 75.0 µm |
注册或登录后
所有资料免费
|
% | ASTM D1003 |
|
100 µm 100 µm |
注册或登录后
所有资料免费
|
% | ASTM D1003 |
|
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热收缩 Thermal shrinkage |
注册或登录后
所有资料免费
|
内部方法 | |
|
MD,30 min:150℃,50.0 µm MD,30 min:150℃,50.0 µm |
注册或登录后
所有资料免费
|
% | 内部方法 |
|
MD,30 min:150℃,75.0 µm MD,30 min:150℃,75.0 µm |
注册或登录后
所有资料免费
|
% | 内部方法 |
|
MD,30 min:150℃,100.0 µm MD,30 min:150℃,100.0 µm |
注册或登录后
所有资料免费
|
% | 内部方法 |
|
TD,30 min:150℃,50.0 µm TD,30 min:150℃,50.0 µm |
注册或登录后
所有资料免费
|
% | 内部方法 |
|
TD,30 min:150℃,75.0 µm TD,30 min:150℃,75.0 µm |
注册或登录后
所有资料免费
|
% | 内部方法 |
|
TD,30 min:150℃,100.0 µm TD,30 min:150℃,100.0 µm |
注册或登录后
所有资料免费
|
% | 内部方法 |
|
Surface Treatment Surface Treatment |
注册或登录后
所有资料免费
|
||
| 备注 |
|---|
| 1 一般属性:这些不能被视为规格。 |
|