牌号信息	ALCOM® PA66 910/1.1 CF10 PTFE10IM 物性表 PA66 & 德国爱彼斯指导价格：暂无塑料库存：缺货	LNP™ LUBRICOMP™ REL22 compound 物性表 PA66 & 沙特沙伯基础指导价格：暂无塑料库存：缺货
牌号简介	ALCOM® PA66 910/1.1 CF10 PTFE10IM是一种聚酰胺66（尼龙66）产品,含有的填充物为10% ptfe 纤维和 10% 碳纤维增强材料。它可以通过注射成型进行加工,在北美洲、欧洲或亚太地区有供货。典型应用领域为:汽车行业。特性包括: 通过 ROHS 认证冲击改性传导性耐磨耐热 ALCOM® PA66 910/1.1 CF10 PTFE10IM is a Polyamide 66 (Nylon 66) product filled with 10% carbon fiber and 10% ptfe fiber. It can be processed by injection molding and is available in Asia Pacific, Europe, or North America. Typical application: Automotive. Characteristics include: RoHS Compliant Conductive Heat Resistant Impact Modified Wear Resistant	LNP Lubricomp Rel22是一种基于尼龙66树脂的化合物，含有10%的碳纤维和10%的聚四氟乙烯。这种材料的附加特性包括：耐磨、导电。又名：lnplubricomp化合物RCL-4022产品再订购名称：rel22 LNP LUBRICOMP REL22 is a compound based on Nylon 66 resin containing 10% Carbon Fiber, 10% PTFE. Added features of this material include: Wear Resistant, Electrically Conductive.

产品描述
厂家：	德国爱彼斯 ALBIS	沙特沙伯基础 SABIC
类别：	PA66 PA66	PA66 PA66
填料：	PTFE/碳纤维 10	PTFE/碳纤维 10
用途：	汽车领域的应用
性能特点：	耐老化,冲击性能好,导电,耐磨 Good heat aging resistance,High impact resistance,Conductive,Good wear resistance	导电,润滑性,耐磨 Conductive,Lubricating,Good wear resistance
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL ALCOM® PA66 910/1.1 CF10 PTFE10IM LNP™ LUBRICOMP™ REL22 compound 单位
UNIT 测试方法
TEST METHOD

吸水率(24hr，50% RH)
Water absorption rate % ASTM D570

吸水率(平衡，23℃，50% RH)
Water absorption rate % ISO 62

密度
Density g/cm³ ASTM D792

密度
Density g/cm³ ISO 1183

收缩率(MD：24 hrs)
Shrinkage rate %

收缩率(TD：24 hrs)
Shrinkage rate %

机械性能
MECHANICAL ALCOM® PA66 910/1.1 CF10 PTFE10IM LNP™ LUBRICOMP™ REL22 compound 单位
UNIT 测试方法
TEST METHOD

弯曲强度
bending strength MPa ISO 178

弯曲强度(--)
bending strength MPa ISO 178

弯曲强度(断裂，50 mm跨度)
bending strength MPa ASTM D790

弯曲模量
Bending modulus MPa ISO 178

弯曲模量(--)
Bending modulus MPa ISO 178

弯曲模量(50 mm跨距)
Bending modulus MPa ASTM D790

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2

拉伸应变(断裂)
Tensile strain % ISO 527-2/5

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ISO 527-2

拉伸强度(断裂)
tensile strength MPa ISO 527-2/5

拉伸模量
Tensile modulus MPa ISO 527-2

拉伸模量(--)
Tensile modulus MPa ASTM D638

拉伸模量(--)
Tensile modulus MPa ISO 527-1-2

摩擦系数(与自身 - 动态)
friction coefficient

摩擦系数(与自身 - 静态)
friction coefficient

磨损因数(Ring)
Wear factor 10^-10 in^5-min/ft-lb-hr

磨损因数(Washer)
Wear factor 10^-10 in^5-min/ft-lb-hr

冲击性能
IMPACT ALCOM® PA66 910/1.1 CF10 PTFE10IM LNP™ LUBRICOMP™ REL22 compound 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam J/m ASTM D4812

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam kJ/m² ISO 180/1U

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

简支梁无缺口冲击强度
Charpy Unnotch Impact strength kJ/m² ISO 179/1eU

简支梁缺口冲击强度
Charpy Notched Impact Strength kJ/m² ISO 179-1eA

装有测量仪表的落镖冲击(--)
Dart impact equipped with measuring instruments J ISO 6603-2

装有测量仪表的落镖冲击(23℃，Total Energy)
Dart impact equipped with measuring instruments J ASTM D3763

热性能
THERMAL ALCOM® PA66 910/1.1 CF10 PTFE10IM LNP™ LUBRICOMP™ REL22 compound 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(0.45 MPa，未退火，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Bf

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/A

热变形温度(1.8 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Af

熔融温度(DSC)
Melting temperature ℃ ISO 11357

线性热膨胀系数(MD：-30~30℃)
Linear coefficient of thermal expansion 1/℃

线性热膨胀系数(TD：-30~30℃)
Linear coefficient of thermal expansion 1/℃

维卡软化温度(B50)
Vicat Softening Temp ℃ ISO 306

电气性能
ELECTRICAL ALCOM® PA66 910/1.1 CF10 PTFE10IM LNP™ LUBRICOMP™ REL22 compound 单位
UNIT 测试方法
TEST METHOD

表面电阻率
Surface resistivity ohms IEC 60093

加工方式

注射 ALCOM® PA66 910/1.1 CF10 PTFE10IM LNP™ LUBRICOMP™ REL22 compound 单位测试方法

加工熔体温度 °C

干燥时间 hr

干燥时间 - 热风干燥机 hr

干燥温度 °C

干燥温度 - 热风干燥机 °C

建议的最大水分含量 %

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

背压 MPa

螺杆转速 rpm

备注

1 一般属性：这些不能被视为规格。

2 0,20 in/min

3 类型 1, 0,20 in/min

4 0,051 in/min

5 0,079 in/min

6 80*10*4

7 80*10*4 mm


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
电气性能
加工方式
注射
备注
返回顶部