PEEK，WDF® PEEK K900CF30-HV对比PEEK，WDF® PEEK K900CF30-MV物性表,价格行情_搜料

牌号信息	WDF® PEEK K900CF30-HV 物性表 PEEK & 上海沃德夫指导价格：暂无塑料库存：缺货	WDF® PEEK K900CF30-MV 物性表 PEEK & 上海沃德夫指导价格：暂无塑料库存：缺货
牌号简介	K900CF30-HV是一种30%碳纤维增强的高粘度聚醚醚酮。该材料具有优异的耐磨性、耐化学性、高强度、尺寸稳定性和高耐热性。 K900CF30-HV is a 30% carbon fiber reinforced Polyetheretherketone with highviscosity. The material has excellent wear resistance, chemical resistance, high strength, dimensional stabilityand high heat resistance.	K900CF30-MV是一种30%碳纤维增强的中粘度聚醚醚酮。该材料具有优异的耐磨性、耐化学性、高强度、尺寸稳定性和高耐热性。 K900CF30-MV is a 30% carbon fiber reinforced Polyetheretherketone with medium viscosity. The material has excellent wear resistance, chemical resistance, high strength, dimensional stability and high heat resistance.

产品描述
厂家：	上海沃德夫 Worldful	上海沃德夫 Worldful
类别：	PEEK PEEK	PEEK PEEK
填料：	碳纤维 30	碳纤维 30
用途：	医疗/护理用品,工业应用,航空航天应用,汽车领域的应用	医疗/护理用品,航空航天应用,工业应用,汽车领域的应用
性能特点：	机械强度好,高粘度,尺寸稳定性好,耐高温,耐磨,耐化学性 Good Rigidity,High Viscosity,Good Dimensional Stability,High Heat Resistance,Good wear resistance,Solvent resistance	机械强度好,尺寸稳定性好,耐高温,耐磨,耐化学性 Good Rigidity,Good Dimensional Stability,High Heat Resistance,Good wear resistance,Solvent resistance
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL WDF® PEEK K900CF30-HV WDF® PEEK K900CF30-MV 单位
UNIT 测试方法
TEST METHOD

吸水率(平衡)
Water absorption rate % ASTM D570

密度
Density g/cm³ ASTM D792

收缩率(MD)
Shrinkage rate %

收缩率(TD)
Shrinkage rate %

熔体质量流动速率(380℃，5.0kg)
Melt Flow Rate g/10min ASTM D1238

冲击性能
IMPACT WDF® PEEK K900CF30-HV WDF® PEEK K900CF30-MV 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度
Impact strength of cantilever beam notch J/m ASTM D256

简支梁无缺口冲击强度
Charpy Unnotch Impact strength J/m ASTM D256

热性能
THERMAL WDF® PEEK K900CF30-HV WDF® PEEK K900CF30-MV 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃

熔融温度
Melting temperature ℃ ASTM D2133

维卡软化温度
Vicat Softening Temp ℃ ASTM D1525 5

电气性能
ELECTRICAL WDF® PEEK K900CF30-HV WDF® PEEK K900CF30-MV 单位
UNIT 测试方法
TEST METHOD

体积电阻率
Volume resistivity ohms·cm IEC 60093

阻燃性能
FLAMMABILITY WDF® PEEK K900CF30-HV WDF® PEEK K900CF30-MV 单位
UNIT 测试方法
TEST METHOD

阻燃等级(1.60 mm)
Flame retardant level

阻燃等级(3.20 mm)
Flame retardant level

机械性能
MECHANICAL WDF® PEEK K900CF30-HV WDF® PEEK K900CF30-MV 单位
UNIT 测试方法
TEST METHOD

弯曲强度
bending strength MPa ASTM D790

弯曲模量
Bending modulus MPa ASTM D790

抗张强度
Tensile strength MPa ASTM D638

拉伸应变(断裂)
Tensile strain % ASTM D638

洛氏硬度(R 级)
Rockwell hardness ASTM D785

加工方式

注射 WDF® PEEK K900CF30-HV WDF® PEEK K900CF30-MV 单位测试方法

加工熔体温度 °C

干燥时间 hr

干燥温度 °C

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

注射速度

背压 MPa

备注

2、50 mm/min

3、20 mm/min

4、.125"

5、速率 A (50°C/h)

2、50 mm/min

3、20 mm/min

4、.125"

5、速率 A (50°C/h)


相关资讯

牌号简介
产品描述
技术参数
物理性能
冲击性能
热性能
电气性能
阻燃性能
机械性能
加工方式
注射
备注