TPC-ET，Arnitel® EL740-08对比TPC-ET，Arnitel® EL740物性表,价格行情_搜料

牌号信息	Arnitel® EL740-08 物性表 TPC-ET & 德国恩骅力指导价格：暂无塑料库存：缺货	Arnitel® EL740 物性表 TPC-ET & 德国恩骅力指导价格：暂无塑料库存：缺货
牌号简介	Arnitel®是高性能热塑性聚酯，此材料非常奇特，集柔韧性、耐高温、强度以及完美的加工性于一身。从汽车行业到电子电气行业，Arnitel®以更轻、更智能、更环保的姿态逐步替代传统橡胶，有效降低对环境的影响，最终降低系统成本。我们拥有一支知识专业、经验丰富的全球团队持续专注于此材料的新设计、新应用以及新市场的开发。让我们倾听你们的需要，了解你们的产品和工艺，我们定能给你不一样的解决方案。 Arnitel® is a high-performance thermoplastic polyester, a very unique material combining flexibility, high-temperature resistance, strength, and perfect processability. From the automotive industry to the electrical and electronics industry, Arnitel® is gradually replacing traditional rubber with a lighter, smarter, and more environmentally friendly posture, effectively reducing environmental impact and ultimately lowering system costs. We have a knowledgeable and experienced global team continuously focused on developing new designs, applications, and markets for this material. Let us listen to your needs, understand your products and processes, and we can surely provide you with a different solution.	Arnitel® EL740是一种热塑性聚酯弹性体 (TPC-ET)材料,。该产品在北美洲、欧洲或亚太地区有供货,加工方式为:注射成型。 Arnitel® EL740的主要特性为:阻燃/额定火焰。 Injection Molding

产品描述
厂家：	德国恩骅力 Envalior	德国恩骅力 Envalior
类别：	TPC-ET	TPC-ET
填料：
用途：	电子电气,汽车领域的应用
性能特点：		防火阻燃等级HB HB
加工条件：		注射成型 Injection Molding

技术参数

物理性能
PHYSICAL Arnitel® EL740-08 Arnitel® EL740 单位
UNIT 测试方法
TEST METHOD

吸水率(平衡，23℃，50% RH)
Water Absorption % ISO 62

吸水率(饱和，23℃)
Water Absorption % ISO 62

密度
Density g/cm³ ISO 1183

收缩率(MD)
Shrinkage % ISO 294-4

收缩率(TD)
Shrinkage % ISO 294-4

熔体体积流动速度(温度)
Melt volume flow velocity °C ISO 1133

熔体体积流动速度(负荷)
Melt volume flow velocity kg ISO 1133

熔体体积流动速率(230℃，2.16 kg)
Melt Volume Rate cm³/10min ISO 1133

表观密度
Apparent density g/cm³ ISO 60

电气性能
ELECTRICAL Arnitel® EL740-08 Arnitel® EL740 单位
UNIT 测试方法
TEST METHOD

介电强度
Dielectric strength kV/mm IEC 60243-1

体积电阻率
Volume resistivity ohms·cm IEC 60093

相对电容率(1 MHz)
Relative permittivity IEC 60250

相对电容率(100 Hz)
Relative permittivity IEC 60250

相比漏电起痕指数
Comparative Tracking Index V IEC 60112

耗散因数(1 MHz)
Dissipation factor IEC 60250

耗散因数(100 Hz)
Dissipation factor E-4 IEC 60250

其它性能
Arnitel® EL740-08 Arnitel® EL740 单位
UNIT 测试方法
TEST METHOD

吸水率
Water Absorption % ISO 62

吸湿率
Moisture absorption rate % Sim. to ISO 62

冲击性能
IMPACT Arnitel® EL740-08 Arnitel® EL740 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度(23℃)
Izod Notched Impact strength kJ/m² ISO 180-1A

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

机械性能
MECHANICAL Arnitel® EL740-08 Arnitel® EL740 单位
UNIT 测试方法
TEST METHOD

10%应变时的应力
Stress at 10% strain MPa ISO 527-1/-2

100%应变时的应力
Stress at 100% strain MPa ISO 527-1/-2

23°C时恒定应变下的永久变形
Permanent deformation under constant strain at 23 ° C % ISO 815

5%应变时的应力
Stress at 5% strain MPa ISO 527-1/-2

50%应变时的应力
Stress at 50% strain MPa ISO 527-1/-2

70°C时恒定应变下的永久变形
Permanent deformation under constant strain at 70 ° C % ISO 815

屈服应力
Yield stress MPa ISO 527-1/-2

拉伸应变(断裂)
Tensile strain % ISO 527-1/2

拉伸强度(10% 应变)
tensile strength MPa ISO 527-2

拉伸强度(100% 应变)
tensile strength MPa ISO 527-2

拉伸强度(5% 应变)
tensile strength MPa ISO 527-2

拉伸强度(50% 应变)
tensile strength MPa ISO 527-2

拉伸强度(断裂)
tensile strength MPa ISO 527-2

拉伸模量
Tensile modulus MPa ISO 527-1-2

拉伸模量
Tensile modulus MPa ISO 527-2

撕裂强度
tear strength kN/m ISO 34-1

断裂应力
Fracture stress MPa ISO 527-1/-2

断裂应变
Fracture strain % ISO 527-1/-2

标称拉伸断裂应变
Nominal tensile fracture strain % ISO 527-2

标称断裂应变
Nominal fracture strain % ISO 527-1/-2

绍氏硬度D (3s)
Shore hardness D (3s) - ISO 868

邵氏硬度(邵氏 D，3 秒)
Shore hardness ISO 868

热性能
THERMAL Arnitel® EL740-08 Arnitel® EL740 单位
UNIT 测试方法
TEST METHOD

灼热丝引燃温度GWIT(GWIT (厚度(1)))
Glow wire ignition temperature GWIT mm IEC 60695-2-13

热变形温度(0.45 MPa)
HDT ℃ ISO 75-1/2

热变形温度(0.45 MPa，未退火)
HDT ℃ ISO 75-2/B

热扩散率
Thermal diffusivity m²/s -

熔体密度
Melt density g/cm³ -

熔体热导率
Melt thermal conductivity W/(m K) -

熔体的比热
Specific heat of melt J/(kg K) -

熔融温度
Melting temperature ℃ ISO 11357-3

熔融温度(10℃ / min)
Melting temperature ℃ ISO 11357-1/-3

燃烧性(1.5mm厚度)(UL认证)
Combustibility (1.5mm thickness) - -

燃烧性(1.5mm厚度)(测试厚度)
Combustibility (1.5mm thickness) mm IEC 60695-11-10

相对温度指数-冲击(相对温度指数-冲击，厚度1)
Relative Temperature Index - Impact mm UL746B

相对温度指数-电气(相对温度指数-电气，厚度1)
Relative Temperature Index - Electrical mm UL746B

相对温度指数-非冲击(相对温度指数-非冲击，厚度1 )
Relative temperature index - non impact mm UL746B

线性热膨胀系数(MD)
Coeff.of linear therm expansion /℃ ISO 11359-1/-2

线性热膨胀系数(MD)
Coeff.of linear therm expansion 1/℃ ISO 11359-2

线性热膨胀系数(TD)
Coeff.of linear therm expansion 1/℃ ISO 11359-2

维卡软化温度(B50)
Vicat Softening Temperature ℃ ISO 306

Arnitel® EL740-08 Arnitel® EL740 单位
UNIT 测试方法
TEST METHOD

阻燃性能
FLAMMABILITY Arnitel® EL740-08 Arnitel® EL740 单位
UNIT 测试方法
TEST METHOD

可燃性等级(1.6 mm)
Flammability level IEC 60695-11-10, -20

加工方式

注射 Arnitel® EL740-08 Arnitel® EL740 单位测试方法

加工熔体温度 °C

射嘴温度 °C

干燥时间 hr

干燥温度 °C

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

注射速度

背压 MPa

螺杆压缩比

挤出 Arnitel® EL740-08 Arnitel® EL740 单位测试方法

熔体温度 °C

备注

1 一般属性：这些不能被视为规格。

2 10°C/min


相关资讯

牌号简介
产品描述
技术参数
物理性能
电气性能
其它性能
冲击性能
机械性能
热性能
阻燃性能
加工方式
注射
挤出
备注
返回顶部

TPC-ET，Arnitel® EL740-08对比TPC-ET，Arnitel® EL740对比物性表,价格行情_搜料_soliao

询价回复情况说明

牌号	厂家
类别