PPA，Amodel® AT-1116 HS对比PPA，Amodel® AT-6115 HS物性表,价格行情_搜料

牌号信息	Amodel® AT-1116 HS 物性表 PPA & 比利时索尔维指导价格：94500.0元/吨塑料库存： 10625kg	Amodel® AT-6115 HS 物性表 PPA & 比利时索尔维指导价格：81900.0元/吨塑料库存： 3750kg
牌号简介	Amodel AT- 1116 HS是16％玻纤增强聚邻苯二甲酰胺（PPA）增韧热稳定型树脂，专门为了适应需要高刚度、高尺寸稳定性、耐化学性和延展性的高成本效益产品而设计。具有高热变形温度、高弯曲弹性模量。断裂伸长比非增韧玻纤增强PPA高。常规应用包括轴承、轴承保持架/轴承罩、外壳、化学处理设备用组件、电动机架、运动器材、草坪及园艺设备和需要压接或卡扣装配的部件。 - 黑色： AT-1116 HS BK 324 本色：AT-1116 HS NT Amodel® AT-1116 HS polyphthalamide (PPA) is a toughened, heat stabilized 16% glass reinforced resin, designed as a cost effective solution for applications requiring stiffness, good dimensional stability, chemical resistance and ductility. This resin has a high heat deflection temperature and a high flexural modulus, with greater tensile elongation than untoughened glass reinforced PPA. Typical applications include bearings, bearing retainers/cages, housings, chemical processing equipment components, motor frames, sporting equipment, lawn and garden equipment and components that require press-fit or snap-fit assembly. Black: AT-1116 HS BK 324 Natural: AT-1116 HS NT	Amodel AT- 6115 HS是15％玻纤增强增韧级聚邻苯二甲酰胺（PPA）树脂，伸长率高于其它15％玻纤增强牌号AMODEL树脂。专为汽车卡扣式电子连接器开发。流动性好，成型周期短。 - 黑色： AT-6115 HS BK 324 本色：AT-6115 HS NT Amodel® AT-6115 HS is a 15% glass-fiber reinforced, toughened grade of polyphthalamide (PPA) resin designed to possess more elongation than other 15% glass-fiber reinforced grades of Amodel resin. This grade was developed for automotive snap-fit electronic connectors. It offers high flow and short molding cycles. Black: AT-6115 HS BK 324 Natural: AT-6115 HS NT

产品描述
厂家：	比利时索尔维 Solvay	比利时索尔维 Solvay
类别：	PPA PPA	PPA
填料：	玻璃纤维 16	玻璃纤维 15
用途：	线轴,连接器,汽车的发动机罩下的零件,轴承,机器/机械部件,工业应用,汽车领域的应用,金属取代,工业部件,通用,汽车电子	工业应用,通用,机器/机械部件,汽车电子,工业部件,阀门/阀门部件,连接器,外壳,汽车的发动机罩下的零件,汽车领域的应用,金属取代
性能特点：	冲击性能好,尺寸稳定性好,耐高温,耐化学性,热稳定性好 High impact resistance,Good Dimensional Stability,High Heat Resistance,Solvent resistance,Heat Stabilized	拉伸性能好,成型周期快,冲击性能好,热稳定性好,流动性高,润滑性,含脱模剂 Good Tensile Strength,Quick molding cycle,High impact resistance,Heat Stabilized,High liquidity,Lubricating,Good stripping performance
加工条件：	注射成型 Injection Molding	水温模具注塑成型

技术参数

物理性能
PHYSICAL Amodel® AT-1116 HS Amodel® AT-6115 HS 单位
UNIT 测试方法
TEST METHOD

吸水率(24hr)
Water absorption rate % ASTM D570

密度
Density g/cm³ ISO 1183/A

收缩率(MD)
Shrinkage rate % ASTM D955

收缩率(TD)
Shrinkage rate % ASTM D955

机械性能
MECHANICAL Amodel® AT-1116 HS Amodel® AT-6115 HS 单位
UNIT 测试方法
TEST METHOD

剪切强度
shear strength MPa ASTM D732

压缩强度
compressive strength MPa ASTM D695

弯曲强度
bending strength MPa ASTM D790

弯曲强度(100℃)
bending strength MPa ISO 178

弯曲强度(23℃)
bending strength MPa ISO 178

弯曲模量
Bending modulus MPa ASTM D790

弯曲模量(100℃)
Bending modulus MPa ISO 178

弯曲模量(23℃)
Bending modulus MPa ISO 178

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂，23℃)
Tensile strain % ISO 527-2

拉伸应变(断裂，24℃)
Tensile strain % ISO 527-2

拉伸强度
tensile strength MPa ASTM D638

拉伸强度(断裂，23℃)
tensile strength MPa ISO 527-2

拉伸强度(断裂，24℃)
tensile strength MPa ISO 527-2

拉伸模量
Tensile modulus MPa ASTM D638

拉伸模量(100℃)
Tensile modulus MPa ISO 527-2

拉伸模量(23℃)
Tensile modulus MPa ISO 527-2

冲击性能
IMPACT Amodel® AT-1116 HS Amodel® AT-6115 HS 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam kJ/m² ISO 180/1U

悬臂梁缺口冲击强度
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength kJ/m² ISO 179/1eU

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

装有测量仪表的落镖冲击(Energy at Maxumum Load)
Dart impact equipped with measuring instruments J ASTM D3763

装有测量仪表的落镖冲击(Total Energy)
Dart impact equipped with measuring instruments J ASTM D3763

热性能
THERMAL Amodel® AT-1116 HS Amodel® AT-6115 HS 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/B

热变形温度(0.45 MPa，退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/A

热变形温度(1.8 MPa，退火)
Hot deformation temperature ℃ ASTM D648

熔融峰值温度
Melting peak temperature ℃ ASTM D3418

熔融温度
Melting temperature ℃ ISO 11357-3

线性热膨胀系数(0 到 100℃)
Linear coefficient of thermal expansion cm/cm/℃ ASTM E831

线性热膨胀系数(100 到 200℃)
Linear coefficient of thermal expansion cm/cm/℃ ASTM E831

线性热膨胀系数(MD)
Linear coefficient of thermal expansion ASTM E831

线性热膨胀系数(MD，0到100℃)
Linear coefficient of thermal expansion cm/cm/℃ ASTM E831

线性热膨胀系数(MD，100到200℃)
Linear coefficient of thermal expansion cm/cm/℃ ASTM E831

线性热膨胀系数(TD)
Linear coefficient of thermal expansion ASTM E831

线性热膨胀系数(TD，0到100℃)
Linear coefficient of thermal expansion cm/cm/℃ ASTM E831

线性热膨胀系数(TD，100到200℃)
Linear coefficient of thermal expansion cm/cm/℃ ASTM E831

加工方式

注射 Amodel® AT-1116 HS Amodel® AT-6115 HS 单位测试方法

加工熔体温度 °C

干燥时间 hr

干燥温度 °C

建议的最大水分含量 %

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

注塑成型 Amodel® AT-1116 HS Amodel® AT-6115 HS 单位测试方法

加工熔体温度 °C

干燥时间 hr

干燥温度 °C

建议的最大水分含量 %

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

备注

1 一般属性：这些不能被视为规格。

2 Maximum Load: 200 lb (890 N)

3 最大负载：240 lb (1070 N)

1 一般属性：这些不能被视为规格。