LLDPE，LINATHENE® LL115C对比LLDPE，HANWHA LLDPE 3121UV物性表,价格行情_搜料

牌号信息	LINATHENE® LL115C 物性表 LLDPE & 台湾台聚指导价格：暂无塑料库存：缺货	HANWHA LLDPE 3121UV 物性表 LLDPE & 韩国韩华指导价格：暂无塑料库存：缺货
牌号简介	LINATHENE® LL115C是一种用于槽铸薄膜挤出的丁烯线性低密度聚乙烯。由LINATHENE® LL115C制成的薄膜具有优异的韧性、拉伸强度、延伸率、穿透强度和透明度。推荐LINATHENE® LL115C用于拉伸膜、保鲜膜和农用膜的生产。 LINATHENE LL115C is a butene linear low density polyethylene developed for slot cast film extrusion. Films made from LINATHENE LL115C have excellent toughness, tensile strength, elongation, puncture strength and transparency. LINATHENE LL115C is recommended for the manufacture of stretch film, cling film and agricultural film.	HANWHA LLDPE 3121UV采用滚圆法制造，适用于一般覆盖膜。LLDPE 3121uV具有良好的机械性能、光学性能和耐候性。 HANWHA LLDPE 3121UV is manufactured by Spherilene process and designed for general mulch film. LLDPE 3121UV has good mechanical property, optical property and weatherability.

产品描述
厂家：	台湾台聚 USI	韩国韩华 HANWHA
类别：	LLDPE Linear low density polyethylene	LLDPE Linear low density polyethylene
填料：
用途：	薄膜,农业应用	薄膜
性能特点：	透光性好,韧性好,拉伸性能好,低密度,抗穿孔性 Good Clarity,Good flexibility,Good Tensile Strength,Low density,Puncture Resistant	耐候抗UV,高光滑性,光学性能,抗结块性,抗氧化 Weather resistance is good,Smoothness,Optical performance,High anti-blocking,Inoxidizability
加工条件：	薄膜挤出 Film extrusion	吹塑薄膜

技术参数

物理性能
PHYSICAL LINATHENE® LL115C HANWHA LLDPE 3121UV 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³ ASTM D1505

密度
Density g/cm³ ASTM D792

熔体质量流动速率
Melt Flow Rate g/10min ASTM D1238

熔体质量流动速率(190℃，2.16kg)
Melt Flow Rate g/10min ASTM D1238

薄膜
LINATHENE® LL115C HANWHA LLDPE 3121UV 单位
UNIT 测试方法
TEST METHOD

拉伸应变(MD，断裂)
Tensile strain % ASTM D882

拉伸应变(MD，断裂，30 µm)
Tensile strain % ASTM D882

拉伸应变(TD，断裂)
Tensile strain % ASTM D882

拉伸应变(TD，断裂，30 µm)
Tensile strain % ASTM D882

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸强度(MD，断裂)
tensile strength MPa ASTM D882

拉伸强度(MD，断裂，30 µm)
tensile strength MPa ASTM D882

拉伸强度(TD，断裂)
tensile strength MPa ASTM D882

拉伸强度(TD，断裂，30 µm)
tensile strength MPa ASTM D882

拉伸强度(断裂)
tensile strength MPa ASTM D638

撕裂强度(MD，30 µm)
tear strength kN/m ASTM D1004

撕裂强度(TD，30 µm)
tear strength kN/m ASTM D1004

落锤冲击
Drop hammer impact g ASTM D1709

落锤冲击(30 µm)
Drop hammer impact g ASTM D1709

薄膜厚度(测试)
film thickness µm

热性能
THERMAL LINATHENE® LL115C HANWHA LLDPE 3121UV 单位
UNIT 测试方法
TEST METHOD

熔融峰值温度
Melting peak temperature ℃ ASTM D3418

熔融峰值温度
Melting peak temperature ℃ 内部方法

维卡软化温度
Vicat Softening Temp ℃ ASTM D1525

脆化温度
Embrittlement temperature ℃ ASTM D746

光学性能
OPTICAL LINATHENE® LL115C HANWHA LLDPE 3121UV 单位
UNIT 测试方法
TEST METHOD

雾度(30 µm)
Haze % ASTM D1003

加工方式

挤出 LINATHENE® LL115C HANWHA LLDPE 3121UV 单位测试方法

熔体温度 °C

备注

1 一般属性：这些不能被视为规格。

2 F50

1 一般属性：这些不能被视为规格。


相关资讯

牌号简介
产品描述
技术参数
物理性能
薄膜
热性能
光学性能
加工方式
挤出
备注
返回顶部