技术参数
物理性能 PHYSICAL
LNP™ THERMOCOMP™ UF00ASW compound
LNP™ VERTON™ UX06451 compound
单位 UNIT
测试方法 TEST METHOD
吸水率(24hr,50% RH)
Water absorption rate
%
ASTM D570
吸水率(平衡,23℃,50% RH)
Water absorption rate
%
ISO 62
密度
Density
g/cm³
ASTM D792
密度
Density
g/cm³
ISO 1183
收缩率(MD:24 hrs)
Shrinkage rate
%
ASTM D955
收缩率(MD:24 hrs)
Shrinkage rate
%
ISO 294
收缩率(TD:24 hrs)
Shrinkage rate
%
ASTM D955
机械性能 MECHANICAL
LNP™ THERMOCOMP™ UF00ASW compound
LNP™ VERTON™ UX06451 compound
单位 UNIT
测试方法 TEST METHOD
吸水率(24hr,50% RH )
Water absorption rate
%
ASTM D570
弯曲强度
bending strength
MPa
ISO 178
弯曲强度(屈服,50 mm跨度)
bending strength
MPa
ASTM D790
弯曲强度(断裂,50 mm跨度)
bending strength
MPa
ASTM D790
弯曲模量
Bending modulus
MPa
ISO 178
弯曲模量(50 mm跨距)
Bending modulus
MPa
ASTM D790
拉伸应变(屈服)
Tensile strain
%
ISO 527-2/5
拉伸应变(断裂)
Tensile strain
%
ASTM D638
拉伸应变(断裂)
Tensile strain
%
ISO 527
拉伸应变(断裂)
Tensile strain
%
ISO 527-2/5
拉伸强度(屈服)
tensile strength
MPa
ISO 527-2/5
拉伸强度(断裂)
tensile strength
MPa
ASTM D638
拉伸强度(断裂)
tensile strength
MPa
ISO 527
拉伸强度(断裂)
tensile strength
MPa
ISO 527-2/5
拉伸模量
Tensile modulus
MPa
ISO 527-1-2
拉伸模量(1 mm/min)
Tensile modulus
MPa
ISO 527
拉伸模量(50 mm/min)
Tensile modulus
MPa
ASTM D638
冲击性能 IMPACT
LNP™ THERMOCOMP™ UF00ASW compound
LNP™ VERTON™ UX06451 compound
单位 UNIT
测试方法 TEST METHOD
多轴向仪器化冲击能量
Multi axial instrumented impact energy
J
ISO 6603-2
悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam
J/m
ASTM D4812
悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam
kJ/m²
ISO 180/1U
悬臂梁无缺口冲击强度(23℃,80*10*4)
Notched impact strength of cantilever beam
kJ/m²
ISO 180/1U
悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch
J/m
ASTM D256
悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch
J/m
ASTM D4812
悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch
kJ/m²
ISO 180-1A
悬臂梁缺口冲击强度(23℃,80*10*4)
Impact strength of cantilever beam notch
kJ/m²
ISO 180-1A
装有测量仪表的落镖冲击(23℃,Total Energy)
Dart impact equipped with measuring instruments
J
ASTM D3763
热性能 THERMAL
LNP™ THERMOCOMP™ UF00ASW compound
LNP™ VERTON™ UX06451 compound
单位 UNIT
测试方法 TEST METHOD
热变形温度(0.45 MPa,未退火,3.2 mm)
Hot deformation temperature
℃
ASTM D648
热变形温度(0.45 MPa,未退火,64 mm跨距)
Hot deformation temperature
℃
ISO 75-2/Bf
热变形温度(1.8 MPa,未退火,3.2 mm)
Hot deformation temperature
℃
ASTM D648
热变形温度(1.8 MPa,未退火,64 mm跨距)
Hot deformation temperature
℃
ISO 75-2/Af
线性热膨胀系数(MD:-40~40℃)
Linear coefficient of thermal expansion
1/℃
ASTM E831
线性热膨胀系数(MD:-40~40℃)
Linear coefficient of thermal expansion
1/℃
ISO 11359-2
线性热膨胀系数(TD:-40~40℃)
Linear coefficient of thermal expansion
1/℃
ASTM E831
线性热膨胀系数(TD:-40~40℃)
Linear coefficient of thermal expansion
1/℃
ISO 11359-2
冲击强度
LNP™ THERMOCOMP™ UF00ASW compound
LNP™ VERTON™ UX06451 compound
单位 UNIT
测试方法 TEST METHOD
多轴冲击
Multiaxial impact
cm-kgf
ISO 6603