PA66，WELLAMID Nylon 6600 GV 40 HWCP对比PA66，Ultramid® A3WG8 BK20560物性表,价格行情_搜料

牌号信息	WELLAMID Nylon 6600 GV 40 HWCP 物性表 PA66 & 德国CP 指导价格：暂无塑料库存：缺货	Ultramid® A3WG8 BK20560 物性表 PA66 & 德国巴斯夫指导价格：暂无塑料库存： 9000kg
牌号简介	WELLAMID Nylon 6600 GV 40 HWCP是一种聚酰胺66（尼龙66）材料,含有的填充物为40% 玻璃纤维增强材料。该产品在欧洲有供货,。 WELLAMID Nylon 6600 GV 40 HWCP的主要特性有: 阻燃/额定火焰热稳定剂。 WELLAMID Nylon 6600 GV 40 HWCP is a Polyamide 66 (Nylon 66) material filled with 40% glass fiber. It is available in Europe. Important attributes of WELLAMID Nylon 6600 GV 40 HWCP are: Flame Rated Heat Stabilizer	Ultramid® A3WG8 BK20560是一种40%的玻璃纤维增强黑色PA66。这一等级提供优良的耐热性和高强度。它设计用于需要优良强度和刚度的工业应用。典型应用包括齿轮、电磁阀外壳、电缆附件、汽车燃油分配器、踏板和汽车换档部件。 Ultramid A3WG8 BK20560 is a 40% glass fiber reinforced, pigmented black PA66. This grade offers excellent heat resistance and high strength. It is designed for industrial applications requiring excellent strength and stiffness. Applications Typical applications include gear wheels, solenoid valve housings, cable attachments, automotive fuel distributors, pedals and components for automotive gear shifts.

产品描述
厂家：	德国CP	德国巴斯夫 BASF
类别：	PA66 PA66	PA66 PA66
填料：	玻璃纤维 40	玻璃纤维 40
用途：		汽车领域的应用,工业应用,燃料管线,齿轮,外壳
性能特点：	热稳定性好 Heat Stabilized	机械强度好,耐高温,耐油 Good Rigidity,High Heat Resistance,Grease resistance
加工条件：		注射成型 Injection Molding

技术参数

机械性能
MECHANICAL WELLAMID Nylon 6600 GV 40 HWCP Ultramid® A3WG8 BK20560 单位
UNIT 测试方法
TEST METHOD

弯曲模量 Flexural Modulus
Flexural Modulus MPa ISO 178

弯曲模量(23℃)
Bending modulus MPa ISO 178

拉伸应变 Tensile Strain(断裂 brk，干燥 dry)
Tensile Strain MPa ISO 527

拉伸应变 Tensile Strain(断裂 brk，湿润 cond.)
Tensile Strain MPa ISO 527

拉伸应变(断裂，23℃)
Tensile strain % ISO 527-2

拉伸强度 Tensile Strength(干燥 dry)
Tensile Strength % ISO 527-2

拉伸强度 Tensile Strength(湿润 cond.)
Tensile Strength % ISO 527-2

拉伸强度(断裂，23℃)
tensile strength MPa ISO 527-2

拉伸模量 Tensile Modulus(干燥 dry)
Tensile Modulus MPa ISO 527

拉伸模量 Tensile Modulus(湿润 cond.)
Tensile Modulus MPa ISO 527

拉伸模量(23℃)
Tensile modulus MPa ISO 527-2

冲击性能
IMPACT WELLAMID Nylon 6600 GV 40 HWCP Ultramid® A3WG8 BK20560 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度(-40℃)
Impact strength of cantilever beam notch kJ/m² ISO 180

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180

简支梁无缺口冲击强度 Charpy Unnotched Impact strength(23℃，干燥 dry)
Charpy Unnotch Impact strength kJ/m² ISO 179

简支梁无缺口冲击强度 Charpy Unnotched Impact strength(23℃，湿润 cond.)
Charpy Unnotch Impact strength kJ/m² ISO 179

简支梁无缺口冲击强度(-30℃)
Charpy Unnotch Impact strength kJ/m² ISO 179

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength kJ/m² ISO 179

简支梁缺口冲击强度 Charpy notched Impact strength(23℃，干燥 dry)
Charpy Notched Impact Strength kJ/m² ISO 179

简支梁缺口冲击强度 Charpy notched Impact strength(23℃，湿润 cond.)
Charpy Notched Impact Strength kJ/m² ISO 179

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m² ISO 179

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179

热性能
THERMAL WELLAMID Nylon 6600 GV 40 HWCP Ultramid® A3WG8 BK20560 单位
UNIT 测试方法
TEST METHOD

热变形温度 HDT(A)
Hot deformation temperature HDT ℃ ISO 75-1/-2

热变形温度 HDT(B)
Hot deformation temperature HDT ℃ ISO 75-1/-2

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/B

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/A

熔融温度 Melting temperature
Melting temperature ℃

熔融温度(DSC)
Melting temperature ℃ ISO 3146

线性热膨胀系数 Coeff.of linear therm expansion(23℃-80℃)
Coeff. of linear thermal expansion ×10-4/K DIN 53752

维卡软化温度 Vicat Softening Temperature
Vicat Softening Temperature ℃ ISO 306/B

电气性能
ELECTRICAL WELLAMID Nylon 6600 GV 40 HWCP Ultramid® A3WG8 BK20560 单位
UNIT 测试方法
TEST METHOD

体积电阻率 Volume Resistivity(干燥 dry)
Volume Resistance ohm·cm IEC 60093

体积电阻率 Volume Resistivity(湿润 cond.)
Volume Resistance ohm·cm IEC 60093

相对电容率 Relative Permittivity(干燥 dry)
Relative permittivity 1 MHz IEC 60250

相对电容率 Relative Permittivity(湿润 cond.)
Relative permittivity 1 MHz IEC 60250

相比漏电起痕指数 Comparative Tracking Index(干燥 dry)
Compared Tracking Index V IEC 60112

耐电强度 Electric strength(干燥 dry)
Electric strength kV/mm IEC 60243-1

耐电强度 Electric strength(湿润 cond.)
Electric strength kV/mm IEC 60243-1

耗散因数 Dissipation Factor(干燥 dry)
Dissipation Factor 1 MHz IEC 60250

耗散因数 Dissipation Factor(湿润 cond.)
Dissipation Factor 1 MHz IEC 60250

表面电阻率 Surface Resistivity(干燥 dry)
Surface Resistivity ohm IEC 60093

表面电阻率 Surface Resistivity(湿润 cond.)
Surface Resistivity ohm IEC 60093

物理性能
PHYSICAL WELLAMID Nylon 6600 GV 40 HWCP Ultramid® A3WG8 BK20560 单位
UNIT 测试方法
TEST METHOD

吸水率(平衡，23℃，50% RH)
Water absorption rate % ISO 62

密度
Density g/cm³ ISO 1183

密度 Density
Density g/cm³ ISO 1183

模具收缩率 Mold Shrinkage
Mold Shrinkage %

饱和值 saturation value at
Saturation value at % DIN 53495

阻燃性能
FLAMMABILITY WELLAMID Nylon 6600 GV 40 HWCP Ultramid® A3WG8 BK20560 单位
UNIT 测试方法
TEST METHOD

阻燃等级 Flame Class Rating(1.6 mm)
Flame Class Rating UL 94

阻燃等级 Flame Class Rating(3.2 mm)
Flame Class Rating UL 94

加工方式

注塑成型 Injection Molding WELLAMID Nylon 6600 GV 40 HWCP Ultramid® A3WG8 BK20560 单位测试方法

模具温度 Mold Temperature °C

熔体温度 Melt Temperature °C

注射 WELLAMID Nylon 6600 GV 40 HWCP Ultramid® A3WG8 BK20560 单位测试方法

加工熔体温度 °C

干燥时间 hr

干燥温度 °C

建议的最大水分含量 %

模具温度 °C

注塑压力 MPa

注射速度

备注

1 一般属性：这些不能被视为规格。


相关资讯

牌号简介
产品描述
技术参数
机械性能
冲击性能
热性能
电气性能
物理性能
阻燃性能
加工方式
注塑成型 Injection Molding
注射
备注
返回顶部

PA66，WELLAMID Nylon 6600 GV 40 HWCP对比PA66，Ultramid® A3WG8 BK20560对比物性表,价格行情_搜料_soliao