PEEK，VICTREX™ PEEK 150FW30对比PEEK，LNP™ LUBRICOMP™ LFL36E compound物性表,价格行情_搜料

牌号信息	VICTREX™ PEEK 150FW30 物性表 PEEK & 英国威格斯指导价格：1344000.0元/吨塑料库存： 25kg	LNP™ LUBRICOMP™ LFL36E compound 物性表 PEEK & 沙特沙伯基础指导价格：暂无塑料库存：缺货
牌号简介	高性能热塑性材料，30%碳纤维/聚四氟乙烯-聚醚醚酮（PEEK）增强，半结晶，注射成型颗粒，易流动，符合FDA食品接触标准，颜色为黑色。具有薄截面或高强度长流动长度的摩擦学应用。优异的耐磨性，极低的摩擦系数，低的热膨胀系数。抗腐蚀环境的化学反应。 High performance thermoplastic material, 30% reinforced with carbon fibre / PTFE PolyEtherEtherKetone (PEEK), semi crystalline, granules for injection moulding, easy flow, FDA food contact compliant, colour black. Tribological applications with thin cross sections or long flow lengths for high strength. Excellent wear resistance, very low coefficient of friction, low coefficient of thermal expansion. Chemically resistant to aggressive environments.	LNP Lubricomp LFL36E是一种基于聚醚醚酮的化合物，含有30%的玻璃纤维和15%的聚四氟乙烯。这种材料的附加特点是：耐磨，容易成型。也称为：lnplubricomp化合物LFL-4036 EM产品再订购名称：LFL36E LNP LUBRICOMP LFL36E is a compound based on Polyetheretherketone containing 30% Glass Fiber, 15% PTFE. Added features of this material are: Wear Resistant, Easy Molding. Also known as: LNP* LUBRICOMP* Compound LFL-4036 EM Product reorder name: LFL36E

产品描述
厂家：	英国威格斯 Victrex	沙特沙伯基础 SABIC
类别：	PEEK	PEEK PEEK
填料：	PTFE/玻璃纤维 30	PTFE/玻璃纤维 30
用途：
性能特点：	低摩擦系数,食品接触,耐化学性,耐磨,半结晶,易流动,机械强度好 Low coefficient of friction,Food contact compliance,Solvent resistance,Good wear resistance,Hypocrystalline,Good liquidity,Good Rigidity	易加工,润滑性,耐磨 Excellent Processability,Lubricating,Good wear resistance
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

冲击性能
IMPACT VICTREX™ PEEK 150FW30 LNP™ LUBRICOMP™ LFL36E compound 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam kJ/m² ISO 180

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D4812

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-A

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength kJ/m² ISO 179/1U

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

装有测量仪表的落镖冲击(23℃，Total Energy)
Dart impact equipped with measuring instruments J ASTM D3763

热性能
THERMAL VICTREX™ PEEK 150FW30 LNP™ LUBRICOMP™ LFL36E compound 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(0.45 MPa，未退火，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Bf

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/Af

热变形温度(1.8 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Af

熔融温度
Melting temperature ℃ ISO 11357-3

玻璃化转变温度(--)
Glass transition temperature ℃ ISO 11357-2

线性热膨胀系数(MD：-30~30℃)
Linear coefficient of thermal expansion 1/℃ ASTM D696

线性热膨胀系数(MD：< 143℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数(MD：> 143℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数(TD：-30~30℃)
Linear coefficient of thermal expansion 1/℃ ASTM D696

线性热膨胀系数(TD：< 143℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数(TD：> 143℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

电气性能
ELECTRICAL VICTREX™ PEEK 150FW30 LNP™ LUBRICOMP™ LFL36E compound 单位
UNIT 测试方法
TEST METHOD

体积电阻率(23℃)
Volume resistivity ohms·cm IEC 60093

机械性能
MECHANICAL VICTREX™ PEEK 150FW30 LNP™ LUBRICOMP™ LFL36E compound 单位
UNIT 测试方法
TEST METHOD

压缩强度(120℃)
compressive strength MPa ISO 604

压缩强度(200℃)
compressive strength MPa ISO 604

压缩强度(23℃)
compressive strength MPa ISO 604

弯曲强度(125℃)
bending strength MPa ISO 178

弯曲强度(175℃)
bending strength MPa ISO 178

弯曲强度(23℃)
bending strength MPa ISO 178

弯曲强度(275℃)
bending strength MPa ISO 178

弯曲强度(断裂，50 mm跨度)
bending strength MPa ASTM D790

弯曲模量(23℃)
Bending modulus MPa ISO 178

弯曲模量(50 mm跨距)
Bending modulus MPa ASTM D790

拉伸应变(屈服)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2/5

拉伸应变(断裂，23℃)
Tensile strain % ISO 527-2

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ISO 527-2/5

拉伸强度(断裂，125℃)
tensile strength MPa ISO 527-2

拉伸强度(断裂，23℃)
tensile strength MPa ISO 527-2

拉伸模量
Tensile modulus MPa ISO 527-1-2

拉伸模量(23℃)
Tensile modulus MPa ISO 527-2

摩擦系数(动态)
friction coefficient ASTM D3702 Modified

摩擦系数(静态)
friction coefficient ASTM D3702 Modified

磨损因数(Ring)
Wear factor 10^-10 in^5-min/ft-lb-hr ASTM D3702 Modified

磨损因数(Washer)
Wear factor 10^-10 in^5-min/ft-lb-hr ASTM D3702 Modified

邵氏硬度(邵氏 D，23℃)
Shore hardness ISO 868

物理性能
PHYSICAL VICTREX™ PEEK 150FW30 LNP™ LUBRICOMP™ LFL36E compound 单位
UNIT 测试方法
TEST METHOD

吸水率(饱和，23℃)
Water absorption rate % ISO 62

密度
Density g/cm³ ASTM D792

密度
Density g/cm³ ISO 1183

收缩率(MD)
Shrinkage rate % ISO 294-4

收缩率(TD)
Shrinkage rate % ISO 294-4

熔体表观粘度(400℃)
Apparent viscosity of melt Pa·s ISO 11443

螺旋流动长度
Spiral flow length cm 内部方法

加工方式

注射 VICTREX™ PEEK 150FW30 LNP™ LUBRICOMP™ LFL36E compound 单位测试方法

加工熔体温度 °C

射嘴温度 °C

干燥时间 hr

干燥温度 °C

建议的最大水分含量 %

料斗温度 °C

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

背压 MPa

螺杆转速 rpm

备注

1 一般属性：这些不能被视为规格。

2 Crystalline

3 模具温度: 356°F, 熔体温度: 725°F

4 1 mm

5 385°C nozzle, 180°C tool

6 Onset

7 Midpoint

8 1V

1 一般属性：这些不能被视为规格。

2 类型 1, 0.20 in/min

3 0.051 in/min

4 0.079 in/min

5 80*10*4 mm


相关资讯

牌号简介
产品描述
技术参数
冲击性能
热性能
电气性能
机械性能
物理性能
加工方式
注射
备注
返回顶部

PEEK，VICTREX™ PEEK 150FW30对比PEEK，LNP™ LUBRICOMP™ LFL36E compound对比物性表,价格行情_搜料_soliao

询价回复情况说明

牌号	厂家
类别