AS(SAN)，CYCOLAC™ INP564 resin对比AS(SAN)，CYCOLAC™ INP581 resin物性表,价格行情_搜料

牌号信息	CYCOLAC™ INP564 resin 物性表 AS(SAN) & 沙特沙伯基础指导价格：暂无塑料库存：缺货	CYCOLAC™ INP581 resin 物性表 AS(SAN) & 沙特沙伯基础指导价格：暂无塑料库存：缺货
牌号简介	cycolac inp564树脂高流量，低分子量粉末SAN，用于颜色浓缩物和合金。cycolac inp564树脂sabic inp564提供了比许多颜色浓缩物基础更广泛的ABS等级的兼容性；允许比颗粒更好的分散；允许浓缩物制造商生产颗粒化和干混合浓缩物。Te；提供比颗粒具有更少热历史的基树脂；适用于直接暴露于天气；可用于所有需要细颗粒尺寸的SAN应用中。 CYCOLAC™ INP564 resin High flow, low molecular weight powder SAN for color concentrates & alloys. CYCOLAC™ INP564 resin SABIC INP564 provides compatibility with a wider range of ABS grades than many color concentrate bases; allows better dispersion than pellets; allows concentrate manufacturers to produce both pelletized and dry blend concentrate; provides a base resin with less heat history than pellets; suitable for direct weather exposure; can be used in all SAN applications where a fine particle size is desired	cycolac inp581树脂高流量SAN颗粒。cycolac inp581树脂高流量，低分子量SAN。可作为聚合物共混物的复合添加剂。可与高橡胶接枝改性树脂混合生产定制的ABS性能。适合直接暴露于天气。为要求严格的注射成型应用提供良好的流动性。 High flow SAN pellets.

产品描述
厂家：	沙特沙伯基础 SABIC	沙特沙伯基础 SABIC
类别：	AS(SAN) SAN	AS(SAN) SAN
填料：
用途：	色母料	添加剂
性能特点：	耐候抗UV,流动性高,低分子量 Weather resistance is good,High liquidity,Low molecular weight	耐候抗UV,流动性高,低分子量 Weather resistance is good,High liquidity,Low molecular weight
加工条件：

技术参数

物理性能
PHYSICAL CYCOLAC™ INP564 resin CYCOLAC™ INP581 resin 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³ ASTM D792

密度
Density g/cm³ ISO 1183

熔体质量流动速率(220℃，10.0kg)
Melt Flow Rate g/10min ISO 1133

熔体质量流动速率(230℃，3.80kg)
Melt Flow Rate g/10min ASTM D1238

冲击性能
IMPACT CYCOLAC™ INP564 resin CYCOLAC™ INP581 resin 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/2C

热性能
THERMAL CYCOLAC™ INP564 resin CYCOLAC™ INP581 resin 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Af

维卡软化温度(B120)
Vicat Softening Temp ℃ ISO 306/B120

维卡软化温度(B50)
Vicat Softening Temp ℃ ISO 306

机械性能
MECHANICAL CYCOLAC™ INP564 resin CYCOLAC™ INP581 resin 单位
UNIT 测试方法
TEST METHOD

弯曲强度
bending strength MPa ISO 178

弯曲强度(屈服，50 mm跨度)
bending strength MPa ASTM D790

弯曲模量(50 mm跨距)
Bending modulus MPa ASTM D790

拉伸应变(屈服)
Tensile strain % ASTM D638

拉伸应变(屈服)
Tensile strain % ISO 527-2/50

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2/50

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸强度(屈服)
tensile strength MPa ISO 527-2/50

拉伸强度(断裂)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ISO 527-2/50

拉伸模量
Tensile modulus MPa ASTM D638

拉伸模量
Tensile modulus MPa ISO 527-1-2

洛氏硬度(R 级)
Rockwell hardness ASTM D785

光学性能
OPTICAL CYCOLAC™ INP564 resin CYCOLAC™ INP581 resin 单位
UNIT 测试方法
TEST METHOD

黄度指数
Yellowness index YI ASTM D1925

备注

1 一般属性：这些不能被视为规格。

2 0.20 in/min

3 类型 1, 0.20 in/min

4 0.051 in/min

5 0.079 in/min

6 Yield

7 80*10*4

8 80*10*4 mm