PPO(PPE)+PS+PA，NORYL GTX™ GTX918WR resin对比PPO(PPE)+PS+PA，NORYL GTX™ GTX678 resin物性表,价格行情_搜料

牌号信息	NORYL GTX™ GTX918WR resin 物性表 PPO(PPE)+PS+PA & 沙特沙伯基础指导价格：暂无塑料库存：缺货	NORYL GTX™ GTX678 resin 物性表 PPO(PPE)+PS+PA & 沙特沙伯基础指导价格：暂无塑料库存：缺货
牌号简介	高流量PPE+PA，用于发动机罩下和电气应用。带模具释放 High flow PPE+PS+PA for under-the-hood and electrical applications. With mold release	Noryl GTX678树脂是一种高性能的PPE/PA混合物，在非卤化阻燃性、导电性、延展性和高耐热性方面表现出良好的平衡。该等级可以静电喷涂或粉末喷涂，无需导电底漆。 NORYL GTX678 resin is a high performance blend of PPE/PA that exhibits an excellent balance on non-halogenated flame retardance, conductivity, ductility, and high-heat resistance. This grade can be electro-statically painted or powder coated without the need for a conductive primer.

产品描述
厂家：	沙特沙伯基础 SABIC	沙特沙伯基础 SABIC
类别：	PPO(PPE)+PS+PA PPO(PPE)+PS+PA	PPO(PPE)+PS+PA PPO(PPE)+PS+PA
填料：
用途：	汽车电子,汽车的发动机罩下的零件
性能特点：	流动性高 High liquidity	导电,机械强度好-延展,可表面喷涂,无卤,阻燃,耐高温,防火阻燃等级V-1 Conductive,Ductility,Sprayable,Halogen free,Flame Characteristics,High Heat Resistance,V-1
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL NORYL GTX™ GTX918WR resin NORYL GTX™ GTX678 resin 单位
UNIT 测试方法
TEST METHOD

吸水率(平衡，23℃，50% RH)
Water absorption rate % ISO 62

吸水率(饱和，23℃)
Water absorption rate % ASTM D570

吸水率(饱和，23℃)
Water absorption rate % ISO 62

密度
Density g/cm³ ASTM D792

密度
Density g/cm³ ASTM D792 , ISO 1183

收缩率(MD：3.2 mm)
Shrinkage rate % 内部方法

收缩率(TD：3.2 mm)
Shrinkage rate % 内部方法

熔体体积流动速率(300℃，1.2 kg)
Melt Volume Rate cm³/10min ISO 1133

熔体体积流动速率(300℃，5 kg)
Melt Volume Rate cm³/10min ISO 1133

熔体质量流动速率(280℃，5.0kg)
Melt Flow Rate g/10min ASTM D1238

熔体质量流动速率(300℃，5.0kg)
Melt Flow Rate g/10min ASTM D1238

机械性能
MECHANICAL NORYL GTX™ GTX918WR resin NORYL GTX™ GTX678 resin 单位
UNIT 测试方法
TEST METHOD

弯曲强度(--)
bending strength MPa ISO 178

弯曲强度(屈服，50 mm跨度)
bending strength MPa ASTM D790

弯曲模量(--)
Bending modulus MPa ISO 178

弯曲模量(50 mm跨距)
Bending modulus MPa ASTM D790

拉伸应变(屈服)
Tensile strain % ASTM D638

拉伸应变(屈服)
Tensile strain % ISO 527-2/50

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2/50

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸强度(屈服)
tensile strength MPa ISO 527-2/50

拉伸强度(断裂)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ISO 527-2/50

拉伸模量
Tensile modulus MPa ASTM D638

拉伸模量(--)
Tensile modulus MPa ASTM D638

拉伸模量(--)
Tensile modulus MPa ISO 527-1-2

冲击性能
IMPACT NORYL GTX™ GTX918WR resin NORYL GTX™ GTX678 resin 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

装有测量仪表的落镖冲击(23℃，Energy at Peak Load)
Dart impact equipped with measuring instruments J ASTM D3763

装有测量仪表的落镖冲击(23℃，Total Energy)
Dart impact equipped with measuring instruments J ASTM D3763

热性能
THERMAL NORYL GTX™ GTX918WR resin NORYL GTX™ GTX678 resin 单位
UNIT 测试方法
TEST METHOD

导热系数
Thermal conductivity coefficient W/m/K ASTM C177

比热
specific heat J/kg/℃ ASTM C351

热变形温度(0.45 MPa，未退火，100 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Be

热变形温度(0.45 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(0.45 MPa，未退火，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Bf

热变形温度(1.8 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

球压测试(125℃)
Ball pressure test IEC 60695-10-2

线性热膨胀系数(MD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831

线性热膨胀系数(MD：23~60℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数(TD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831

线性热膨胀系数(TD：23~60℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

维卡软化温度(--)
Vicat Softening Temp ℃ ASTM D1525 11

维卡软化温度(A50)
Vicat Softening Temp ℃ ISO 306/A50

维卡软化温度(B120)
Vicat Softening Temp ℃ ISO 306/B120

维卡软化温度(B50)
Vicat Softening Temp ℃ ISO 306

电气性能
ELECTRICAL NORYL GTX™ GTX918WR resin NORYL GTX™ GTX678 resin 单位
UNIT 测试方法
TEST METHOD

体积电阻率
Volume resistivity ohms·cm ASTM D257

阻燃性能
FLAMMABILITY NORYL GTX™ GTX918WR resin NORYL GTX™ GTX678 resin 单位
UNIT 测试方法
TEST METHOD

灼热丝可燃性指数(2.0 mm)
Glowing wire flammability index ℃ IEC 60695-2-12

灼热丝起燃温度(1 mm)
Igniting temperature of the hot wire ℃ IEC 60695-2-13

阻燃等级(1.50 mm)
Flame retardant level UL 94

阻燃等级(2.00 mm)
Flame retardant level UL 94

加工方式

注射 NORYL GTX™ GTX918WR resin NORYL GTX™ GTX678 resin 单位测试方法

干燥时间 hr

干燥时间，最大 hr

干燥温度 °C

建议的最大水分含量 %

建议注射量 NORYL GTX™ GTX918WR resin NORYL GTX™ GTX678 resin 单位测试方法

加工熔体温度 °C

射嘴温度 °C

排气孔深度 mm

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

背压 MPa

螺杆转速 rpm

挤出 NORYL GTX™ GTX918WR resin NORYL GTX™ GTX678 resin 单位测试方法

口模温度 °C

干燥时间 hr

干燥温度 °C

建议的最大水分含量 %

接头温度 °C

料筒1区温度 °C

料筒2区温度 °C

料筒3区温度 °C

料筒4区温度 °C

校准温度，首次 °C

熔体温度 °C

备注

3 50 mm/min

4 类型 1, 50 mm/min

5 1.3 mm/min

6 2.0 mm/min

7 Yield

8 80*10*4 sp=62mm

9 80*10*4

10 120*10*4 mm

11 标准 B (120°C/h), 载荷2 (50N)

3 5.0 mm/min