TPEE，LNP™ LUBRICOMP™ YL003C compound对比TPEE，LNP™ LUBRICOMP™ YL003 compound物性表,价格行情_搜料

牌号信息	LNP™ LUBRICOMP™ YL003C compound 物性表 TPEE & 沙特沙伯基础指导价格：暂无塑料库存：缺货	LNP™ LUBRICOMP™ YL003 compound 物性表 TPEE & 沙特沙伯基础指导价格：暂无塑料库存：缺货
牌号简介	LNP Lubricomp YL003C化合物LubricompYL003C是一种基于含15%聚四氟乙烯的聚酯弹性体树脂的化合物。这一级别的附加功能包括：清洁的复合系统，耐磨性。又名：lnplubricomp化合物yl-4030 ccs产品再订购名称：yl003c lnp lubricomp yl003c化合物lubricompyl-4030 ccs是一种基于聚酯弹性体树脂的聚四氟乙烯润滑化合物，具有低离子性和低排气性能，适用于分号和内部硬盘驱动器应用。 LNP™ LUBRICOMP™ YL003C compound LUBRICOMP* YL003C is a compound based on Polyester Elastomer resin containing 15% PTFE. Added features of this grade include: Clean Compound System, Wear Resistant. Also known as: LNP* LUBRICOMP* Compound YL-4030 CCS Product Reorder name: YL003C LNP™ LUBRICOMP™ YL003C compound LUBRICOMP* YL-4030 CCS is a PTFE Lubricated Compound based on Polyester Elastomer resin which has low ionic and low outgassing performance for the Semicon and Internal Hard Disk Drive applications.	lnp lubricomp yl003化合物lnplubricompyl003是基于含有15%聚四氟乙烯的聚酯弹性体树脂的化合物。这一等级的附加特征是：耐磨。也称为：LNPLubricomp化合物YL-4030产品再订购名称：YL003LNP Lubricomp YL003化合物LNP Lubricomp YL003是一种基于含有聚四氟乙烯的聚酯弹性体的化合物。附加功能包括；内部润滑。又名：LNPLubricomp化合物YL-4030产品再订购名称：YL003 LNP™ LUBRICOMP™ YL003 compound LNP* LUBRICOMP* YL003 is a compound based on Polyester Elastomer resin containing 15% PTFE. Added feature of this grade is: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound YL-4030 Product reorder name: YL003 LNP™ LUBRICOMP™ YL003 compound LNP LUBRICOMP YL003 is a compound based on Polyester Elastomer containing PTFE. Added features include; Internally Lubricated. Also known as: LNP* LUBRICOMP* Compound YL-4030 Product reorder name: YL003

产品描述
厂家：	沙特沙伯基础 SABIC	沙特沙伯基础 SABIC
类别：	TPEE TPEE	TPEE TPEE
填料：	PTFE 15	PTFE 15
用途：	电气/电子应用领域
性能特点：	低离子含量,低VOC,润滑性,耐磨,防火阻燃等级HB Low (to None) Ion Content,Low odor,Lubricating,Good wear resistance,HB	润滑性,耐磨 Lubricating,Good wear resistance
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL LNP™ LUBRICOMP™ YL003C compound LNP™ LUBRICOMP™ YL003 compound 单位
UNIT 测试方法
TEST METHOD

吸水率(23℃，24hr)
Water absorption rate % ASTM D570

吸水率(24hr，50% RH)
Water absorption rate % ASTM D570

吸水率(平衡，23℃，50% RH)
Water absorption rate % ISO 62

吸水率(饱和，23℃)
Water absorption rate % ISO 62

密度
Density g/cm³ ASTM D792

密度
Density g/cm³ ISO 1183

收缩率(MD：24 hrs)
Shrinkage rate % ASTM D955

收缩率(MD：24 hrs)
Shrinkage rate % ISO 294-4

收缩率(TD：24 hrs)
Shrinkage rate % ASTM D955

收缩率(TD：24 hrs)
Shrinkage rate % ISO 294-4

机械性能
MECHANICAL LNP™ LUBRICOMP™ YL003C compound LNP™ LUBRICOMP™ YL003 compound 单位
UNIT 测试方法
TEST METHOD

弯曲强度
bending strength MPa ASTM D790

弯曲强度
bending strength MPa ISO 178

弯曲模量
Bending modulus MPa ASTM D790

弯曲模量
Bending modulus MPa ISO 178

弯曲模量(50 mm跨距)
Bending modulus MPa ASTM D790

拉伸应变(屈服)
Tensile strain % ASTM D638

拉伸应变(屈服)
Tensile strain % ISO 527-2/5

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2/50

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸强度(屈服)
tensile strength MPa ISO 527-2/5

拉伸强度(断裂)
tensile strength MPa ASTM D638

拉伸模量
Tensile modulus MPa ASTM D638

拉伸模量
Tensile modulus MPa ISO 527-1-2

邵氏硬度(邵氏 D)
Shore hardness ASTM D2240

冲击性能
IMPACT LNP™ LUBRICOMP™ YL003C compound LNP™ LUBRICOMP™ YL003 compound 单位
UNIT 测试方法
TEST METHOD

多轴向仪器化冲击能量
Multi axial instrumented impact energy J ISO 6603-2

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam kJ/m² ISO 180/1U

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D4812

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

装有测量仪表的落镖冲击(23℃，Total Energy)
Dart impact equipped with measuring instruments J ASTM D3763

热性能
THERMAL LNP™ LUBRICOMP™ YL003C compound LNP™ LUBRICOMP™ YL003 compound 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火，6.4 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(0.45 MPa，未退火，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Bf

热变形温度(1.8 MPa，未退火，6.4 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Af

线性热膨胀系数(MD：-30~30℃)
Linear coefficient of thermal expansion 1/℃ ASTM D696

线性热膨胀系数(MD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831

线性热膨胀系数(MD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数(TD：-30~30℃)
Linear coefficient of thermal expansion 1/℃ ASTM D696

线性热膨胀系数(TD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831

线性热膨胀系数(TD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

阻燃性能
FLAMMABILITY LNP™ LUBRICOMP™ YL003C compound LNP™ LUBRICOMP™ YL003 compound 单位
UNIT 测试方法
TEST METHOD

1.00 mm
1.00 mm UL 94

加工方式

注射 LNP™ LUBRICOMP™ YL003C compound LNP™ LUBRICOMP™ YL003 compound 单位测试方法

加工熔体温度 °C

干燥时间 hr

干燥温度 °C

建议的最大水分含量 %

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

背压 MPa

螺杆转速 rpm

备注

1 一般属性：这些不能被视为规格。

2 Results measured at 48 hrs

3 2.0 in/min

4 80*10*3

5 80*10*4

6 80*10*4 mm

1 一般属性：这些不能被视为规格。

2 2.0 in/min

3 类型 1, 0.20 in/min

4 0.051 in/min

5 0.079 in/min

6 Yield

7 80*10*4


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
阻燃性能
加工方式
注射
备注
返回顶部