技术参数
物理性能
PHYSICAL
LNP™ THERMOCOMP™ 2X04505 compound
RTP ESD 3284
单位
UNIT
测试方法
TEST METHOD
密度
Density
g/cm³
ASTM D792
密度
Density
g/cm³
ISO 1183
收缩率(MD：24 hrs)
Shrinkage rate
%
ASTM D955
收缩率(MD：24 hrs)
Shrinkage rate
%
ISO 294-4
收缩率(MD：3.2 mm)
Shrinkage rate
%
ASTM D955
收缩率(TD：24 hrs)
Shrinkage rate
%
ASTM D955
收缩率(TD：24 hrs)
Shrinkage rate
%
ISO 294-4
机械性能
MECHANICAL
LNP™ THERMOCOMP™ 2X04505 compound
RTP ESD 3284
单位
UNIT
测试方法
TEST METHOD
弯曲强度
bending strength
MPa
ASTM D790
弯曲强度
bending strength
MPa
ISO 178
弯曲模量
Bending modulus
MPa
ASTM D790
弯曲模量
Bending modulus
MPa
ISO 178
弯曲模量(--)
Bending modulus
MPa
ASTM D790
弯曲模量(50 mm跨距)
Bending modulus
MPa
ASTM D790
拉伸应变(屈服)
Tensile strain
%
ASTM D638
拉伸应变(屈服)
Tensile strain
%
ISO 527-2
拉伸应变(断裂)
Tensile strain
%
ASTM D638
拉伸应变(断裂)
Tensile strain
%
ISO 527-2
拉伸强度
tensile strength
MPa
ASTM D638
拉伸强度(屈服)
tensile strength
MPa
ASTM D638
拉伸强度(屈服)
tensile strength
MPa
ISO 527-2
拉伸强度(断裂)
tensile strength
MPa
ASTM D638
拉伸强度(断裂)
tensile strength
MPa
ISO 527-2
拉伸模量
Tensile modulus
MPa
ASTM D638
拉伸模量
Tensile modulus
MPa
ISO 527-1-2
冲击性能
IMPACT
LNP™ THERMOCOMP™ 2X04505 compound
RTP ESD 3284
单位
UNIT
测试方法
TEST METHOD
多轴向仪器化冲击能量
Multi axial instrumented impact energy
J
ISO 6603-2
悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam
kJ/m²
ISO 180/1U
悬臂梁无缺口冲击强度(3.2 mm)
Notched impact strength of cantilever beam
J/m
ASTM D4812
悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch
J/m
ASTM D256
悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch
J/m
ASTM D4812
悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch
kJ/m²
ISO 180-1A
悬臂梁缺口冲击强度(3.2mm)
Impact strength of cantilever beam notch
J/m
ASTM D256
装有测量仪表的落镖冲击(23℃，Energy at Peak Load)
Dart impact equipped with measuring instruments
J
ASTM D3763
热性能
THERMAL
LNP™ THERMOCOMP™ 2X04505 compound
RTP ESD 3284
单位
UNIT
测试方法
TEST METHOD
热变形温度(0.45 MPa，未退火，3.2 mm)
Hot deformation temperature
℃
ASTM D648
热变形温度(0.45 MPa，未退火，64 mm跨距)
Hot deformation temperature
℃
ISO 75-2/Bf
热变形温度(1.8 MPa，未退火)
Hot deformation temperature
℃
ASTM D648
热变形温度(1.8 MPa，未退火，3.2 mm)
Hot deformation temperature
℃
ASTM D648
热变形温度(1.8 MPa，未退火，64 mm跨距)
Hot deformation temperature
℃
ISO 75-2/Af
线性热膨胀系数(MD：-40~40℃)
Linear coefficient of thermal expansion
1/℃
ASTM E831
线性热膨胀系数(MD：-40~40℃)
Linear coefficient of thermal expansion
1/℃
ISO 11359-2
线性热膨胀系数(TD：-40~40℃)
Linear coefficient of thermal expansion
1/℃
ASTM E831
线性热膨胀系数(TD：-40~40℃)
Linear coefficient of thermal expansion
1/℃
ISO 11359-2
电气性能
ELECTRICAL
LNP™ THERMOCOMP™ 2X04505 compound
RTP ESD 3284
单位
UNIT
测试方法
TEST METHOD
体积电阻率
Volume resistivity
ohms·cm
ASTM D257
表面电阻率(--)
Surface resistivity
ohms
ASTM D257
表面电阻率(--)
Surface resistivity
ohms
ESD STM11.11
静电衰减
Electrostatic attenuation
sec
FTMS 101C 4046.1
阻燃性能
FLAMMABILITY
LNP™ THERMOCOMP™ 2X04505 compound
RTP ESD 3284
单位
UNIT
测试方法
TEST METHOD
阻燃等级(1.50 mm)
Flame retardant level
UL 94
补充信息
LNP™ THERMOCOMP™ 2X04505 compound
RTP ESD 3284
单位
UNIT
测试方法
TEST METHOD
Primary Additive
Primary Additive
%
高亮区别
隐藏相同