牌号信息	Kalix® 5950 HFFR 物性表 HPPA & 比利时索尔维指导价格：暂无塑料库存：缺货	RTP 4409 物性表 HPPA & 美国RTP 指导价格：暂无塑料库存：缺货
牌号简介	Kalix® 5950 HFFR是一种无卤阻燃剂（ul-94v0，0.4 mm），高度增强的聚酰胺材料，专门为高强度和刚度应用而设计，要求具有良好的抗冲击性和成型后的尺寸稳定性。该公式还解决了与玻璃纤维增强材料的各向异性收缩有关的翘曲问题，以便更容易实现精密公差成型。它的低粘度和优良的流动性能使这种材料非常适合于填充具有薄壁截面的部件，如移动电子工业中遇到的部件。黑色：Kalix 5950 BK 000 HFFR白色：Kalix 5950 WH 000 HFFR Kalix® 5950 HFFR is a halogen-free, flame retardant (UL-94 V0 at 0.4 mm), highly reinforced polyamide material specifically formulated for high strength and stiffness applications where good impact resistance and excellent dimensional stability after molding are required. The formulation also addresses warpage issues associated with the anisotropic shrinkage of glass fiber reinforced materials so that close tolerance molding is more easily achieved. Its low viscosity and excellent flow properties make the material ideal for filling parts with thin-walled sections such as those encountered in the mobile electronics industry. Black: Kalix® 5950 BK 000 HFFR White: Kalix® 5950 WH 000 HFFR	玻璃纤维 Glass Fiber

产品描述
厂家：	比利时索尔维 Solvay	美国RTP
类别：	HPPA HPPA	HPPA HPPA
填料：	玻璃纤维	玻璃纤维
用途：	电气元件,手机,电气/电子应用领域,薄壁部件
性能特点：	机械强度好,低翘曲性,表面光泽度好,冲击性能好,尺寸稳定性好,流动性高,可表面喷涂,无卤,阻燃,电镀,低吸湿性,防火阻燃等级V-0,防火阻燃等级5VA Good Rigidity,Low warping,Good surface appearance,High impact resistance,Good Dimensional Stability,High liquidity,Sprayable,Halogen free,Flame Characteristics,Electroplating,Low moisture absorption,V-0,5VA
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL Kalix® 5950 HFFR RTP 4409 单位
UNIT 测试方法
TEST METHOD

含水量
water content %

吸水率(23℃，24hr)
Water absorption rate % ISO 62

密度
Density g/cm³ ASTM D792

密度
Density g/cm³ ISO 1183

收缩率(MD)
Shrinkage rate % 内部方法

收缩率(MD：3.2 mm)
Shrinkage rate % ASTM D955

收缩率(TD)
Shrinkage rate % 内部方法

机械性能
MECHANICAL Kalix® 5950 HFFR RTP 4409 单位
UNIT 测试方法
TEST METHOD

弯曲强度
bending strength MPa ASTM D790

弯曲强度
bending strength MPa ISO 178

弯曲模量
Bending modulus MPa ASTM D790

弯曲模量
Bending modulus MPa ISO 178

拉伸应变(屈服)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2

拉伸应变(断裂，平衡，50% RH)
Tensile strain % ISO 527-2

拉伸强度
tensile strength MPa ASTM D638

拉伸强度(50% RH，平衡)
tensile strength MPa ISO 527-2

拉伸强度(屈服)
tensile strength MPa ISO 527-2

拉伸模量
Tensile modulus MPa ASTM D638

拉伸模量(平衡，50% RH )
Tensile modulus MPa ISO 527-2

断裂弯曲应变
Fracture bending strain % ISO 178

洛氏硬度(R 级)
Rockwell hardness ASTM D785

冲击性能
IMPACT Kalix® 5950 HFFR RTP 4409 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度
Notched impact strength of cantilever beam kJ/m² ISO 180

悬臂梁无缺口冲击强度(3.2 mm)
Notched impact strength of cantilever beam J/m ASTM D4812

悬臂梁缺口冲击强度
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(3.2mm)
Impact strength of cantilever beam notch J/m ASTM D256

热性能
THERMAL Kalix® 5950 HFFR RTP 4409 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/B

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/A

玻璃化转变温度
Glass transition temperature ℃ ASTM D3418

电气性能
ELECTRICAL Kalix® 5950 HFFR RTP 4409 单位
UNIT 测试方法
TEST METHOD

介电常数(2.40 GHz)
Dielectric constant ASTM D2520

耗散因数(2.4 GHz)
Dissipation factor ASTM D2520

阻燃性能
FLAMMABILITY Kalix® 5950 HFFR RTP 4409 单位
UNIT 测试方法
TEST METHOD

阻燃等级(0.40 mm，所有颜色)
Flame retardant level UL 94

阻燃等级(1.50 mm，所有颜色)
Flame retardant level UL 94

补充信息
Kalix® 5950 HFFR RTP 4409 单位
UNIT 测试方法
TEST METHOD

Primary Additive
Primary Additive %

加工方式

注射 Kalix® 5950 HFFR RTP 4409 单位测试方法

Dew Point °C

加工熔体温度 °C

干燥时间 hr

干燥温度 °C

建议的最大水分含量 %

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

注塑压力 MPa

备注

1 一般属性：这些不能被视为规格。

2 索尔维测试方法。收缩率会根据部件的设计和加工条件而改变。请接洽索尔维技术代表，获取更多信息。

3 方法 B


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
电气性能
阻燃性能
补充信息
加工方式
注射
备注
返回顶部

HPPA，Kalix® 5950 HFFR对比HPPA，RTP 4409对比物性表,价格行情_搜料_soliao

询价回复情况说明

牌号	厂家
类别