环氧树脂，BR® 623-1对比环氧树脂，Epocast 1622 FST A/B物性表,价格行情_搜料

牌号信息	BR® 623-1 物性表环氧树脂 & 美国氰特指导价格：暂无塑料库存：缺货	Epocast 1622 FST A/B 物性表环氧树脂 & 美国亨斯迈指导价格：暂无塑料库存：缺货
牌号简介	BR® 623-1封装化合物是一种单组分环氧材料，设计用于蜂窝结构的嵌件或边缘填充。它的配方具有低粘度，特别适合手工填充小蜂窝尺寸的蜂窝。BR® 623-1在75°F（24°C）下具有较长的工作寿命。测试表明，即使在75°F（24°C）下放置1个月后，产品仍然可以手动使用。BR® 623-1的触变性质确保了当用于填充蜂窝板和封闭件时，在封装化合物固化期间没有坍落度或树脂分离。建议应用：蜂窝结构的插入和边缘填充 BR® 623-1 potting compound is a one-part epoxy material designed for use in insert or edge filling of honeycomb structure. It has been formulated to have low viscosity making it especially suitable for hand- filling small cell size honeycomb. BR 623-1 has a long working outlife at 75°F (24°C). Test show the product is still hand-usable even after 1 month at 75°F (24°C). The thixotropic nature of BR 623-1 ensures that there is no slump or resin separation during the cure of the potting compound when it is used to fill honeycomb panels and closeouts. Suggested Applications: Insert and edge filling of honeycomb structures	说明：EPOCAST1622FST A/B是一种双组分、低密度、可泵送的FST环氧复合材料，设计用于封装紧固件和航空航天内部应用中蜂窝结构的面板连接。它很容易通过Semco分配喷嘴挤压出来，但涂抹后不会流动。EPOCAST1622 FST A/B在室温下快速设置，非常适合需要快速组件组装的航空应用。 DESCRIPTION: EPOCAST® 1622 FST A/B is a two-component, low density, pumpable FST epoxy syntactic material designed for potting fasteners and panel joining of honeycomb structures used in aerospace interior applications. It is easily extruded through Semco ® dispensing nozzles, yet does not flow after it has been applied. EPOCAST® 1622 FST A/B sets quickly at room temperature and is well suited for aerospace applications requiring a rapid component assembly.

产品描述
厂家：	美国氰特 Cytec Industries	美国亨斯迈 Huntsman
类别：	环氧树脂环氧树脂	环氧树脂环氧树脂
填料：
用途：	构件,填充应用	粘合剂,构件,紧固件,航空航天应用
性能特点：	低烟,低粘度,触变,自熄,低密度 Low smoke,Low Viscosity,Thixotropic,Self-extinguishing,Low density	机械强度好,低密度 Good Rigidity,Low density
加工条件：	灌封	灌封

技术参数

物理性能
PHYSICAL BR® 623-1 Epocast 1622 FST A/B 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³

密度(--)
Density g/cm³ ASTM D1622

收缩率
Shrinkage rate % ASTM D6289

粘度(25℃)
viscosity ASTM D2196

机械性能
MECHANICAL BR® 623-1 Epocast 1622 FST A/B 单位
UNIT 测试方法
TEST METHOD

剪切强度(24℃)
shear strength MPa

剪切强度(82℃)
shear strength MPa

压缩强度(-55℃)
compressive strength MPa

压缩强度(23℃)
compressive strength MPa ASTM D695

压缩强度(24℃)
compressive strength MPa

压缩强度(70℃)
compressive strength MPa ASTM D695

压缩强度(79℃)
compressive strength MPa

压缩模量
Compression modulus MPa ASTM D695

补充信息
BR® 623-1 Epocast 1622 FST A/B 单位
UNIT 测试方法
TEST METHOD

Tensile Lap Shear(AL/AL，23℃)
Tensile Lap Shear（AL/AL，23℃） MPa ASTM D1002

挥发性
volatility %

阻燃性能
FLAMMABILITY BR® 623-1 Epocast 1622 FST A/B 单位
UNIT 测试方法
TEST METHOD

阻燃等级(12秒垂直燃烧(熄灭时间))
Flame retardant level sec

阻燃等级(12秒垂直燃烧(燃烧长度))
Flame retardant level cm

阻燃等级(at 4 minutes)
Flame retardant level ASTM E662

阻燃等级(烟雾密度)
Flame retardant level

热固性混合粘度
BR® 623-1 Epocast 1622 FST A/B 单位
UNIT 测试方法
TEST METHOD

25℃(55.7g，25℃)
25℃ min ASTM D2471

25℃(胶凝时间)
25℃

热性能
THERMAL BR® 623-1 Epocast 1622 FST A/B 单位
UNIT 测试方法
TEST METHOD

热固组件(部件 A)
Thermosetting components

热固组件(部件 B)
Thermosetting components

玻璃化转变温度
Glass transition temperature ℃ ASTM E1545

线性热膨胀系数(--)
Linear coefficient of thermal expansion cm/cm/℃ ASTM E831

线性热膨胀系数(MD)
Linear coefficient of thermal expansion ASTM E831

贮藏期限(25℃)
Storage period wk

备注

1 一般属性：这些不能被视为规格。

2 Tube shear

1 一般属性：这些不能被视为规格。

2 Part A

3 System

4 Part B

5 below Tg

6 above Tg