PPO(PPE)+PS+PA，LNP™ STAT-LOY™ 9X03508 compound对比PPO(PPE)+PS+PA，NORYL GTX™ GTX6203 resin物性表,价格行情_搜料

牌号信息	LNP™ STAT-LOY™ 9X03508 compound 物性表 PPO(PPE)+PS+PA & 沙特沙伯基础指导价格：暂无塑料库存：缺货	NORYL GTX™ GTX6203 resin 物性表 PPO(PPE)+PS+PA & 沙特沙伯基础指导价格：47250.0元/吨塑料库存： 2350kg
牌号简介	LNPSTAT-LOY9X03508是一种基于PPO+PA66树脂的化合物，含有专有填料。这种材料的附加特性包括：抗静电、阻燃、高冲击。又名：LNPSTAT-LOY化合物PDX-03508产品再订购名称：9X03508 LNP* STAT-LOY* 9X03508 is a compound based on PPO+PA66 resin containing Proprietary Filler(s). Added features of this material include: Antistatic, Flame Retardant, High Impact. Also known as: LNP* STAT-LOY* Compound PDX-03508 Product reorder name: 9X03508	Noryl GTX6203是一种20%滑石填充材料，具有优异的尺寸稳定性、良好的加工性能和表面外观。 NORYL GTX6203 is a 20% talc filled material with superior dimensional stability, excellent processability and surface appearance.

产品描述
厂家：	沙特沙伯基础 SABIC	沙特沙伯基础 SABIC
类别：	PPO(PPE)+PS+PA PPO(PPE)+PS+PA	PPO(PPE)+PS+PA PPO(PPE)+PS+PA
填料：	其他	滑石粉 20
用途：
性能特点：	冲击性能好,阻燃,抗静电 High impact resistance,Flame Characteristics,Antistatic property	易加工,表面光泽度好,尺寸稳定性好 Excellent Processability,Good surface appearance,Good Dimensional Stability
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL LNP™ STAT-LOY™ 9X03508 compound NORYL GTX™ GTX6203 resin 单位
UNIT 测试方法
TEST METHOD

吸水率(24hr，50% RH)
Water absorption rate % ASTM D570

吸水率(平衡，23℃，50% RH)
Water absorption rate % ISO 62

吸水率(饱和，23℃)
Water absorption rate % ISO 62

密度
Density g/cm³ ASTM D792, ISO 1183

密度(--)
Density g/cm³ ASTM D792

密度(--)
Density g/cm³ ISO 1183

收缩率(MD：3.2 mm)
Shrinkage rate % 内部方法

收缩率(TD：3.2 mm)
Shrinkage rate % 内部方法

熔体体积流动速率(280℃，5 kg)
Melt Volume Rate cm³/10min ISO 1133

熔体质量流动速率(280℃，5.0kg)
Melt Flow Rate g/10min ASTM D1238

机械性能
MECHANICAL LNP™ STAT-LOY™ 9X03508 compound NORYL GTX™ GTX6203 resin 单位
UNIT 测试方法
TEST METHOD

弯曲强度(--)
bending strength MPa ASTM D790

弯曲强度(--)
bending strength MPa ISO 178

弯曲强度(屈服，50 mm跨度)
bending strength MPa ASTM D790

弯曲模量(--)
Bending modulus MPa ASTM D790

弯曲模量(--)
Bending modulus MPa ISO 178

弯曲模量(50 mm跨距)
Bending modulus MPa ASTM D790

拉伸应变(屈服)
Tensile strain % ASTM D638

拉伸应变(屈服)
Tensile strain % ISO 527-2

拉伸应变(屈服)
Tensile strain % ISO 527-2/5

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2

拉伸应变(断裂)
Tensile strain % ISO 527-2/5 , ISO 527-2/50

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸强度(屈服)
tensile strength MPa ISO 527-2

拉伸强度(屈服)
tensile strength MPa ISO 527-2/50

拉伸强度(断裂)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ISO 527-2

拉伸强度(断裂)
tensile strength MPa ISO 527-2/50

拉伸模量(--)
Tensile modulus MPa ASTM D638

拉伸模量(--)
Tensile modulus MPa ISO 527-1-2

冲击性能
IMPACT LNP™ STAT-LOY™ 9X03508 compound NORYL GTX™ GTX6203 resin 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam J/m ASTM D4812

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam kJ/m² ISO 180/1U

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

装有测量仪表的落镖冲击(--)
Dart impact equipped with measuring instruments J ISO 6603-2

装有测量仪表的落镖冲击(23℃，Energy at Peak Load)
Dart impact equipped with measuring instruments J ASTM D3763

装有测量仪表的落镖冲击(23℃，Total Energy)
Dart impact equipped with measuring instruments J ASTM D3763

热性能
THERMAL LNP™ STAT-LOY™ 9X03508 compound NORYL GTX™ GTX6203 resin 单位
UNIT 测试方法
TEST METHOD

导热系数
Thermal conductivity coefficient W/m/K ISO 8302

热变形温度(0.45 MPa，未退火，100 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Be

热变形温度(0.45 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(0.45 MPa，未退火，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Bf

热变形温度(1.8 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Af

球压测试(125℃)
Ball pressure test IEC 60695-10-2

线性热膨胀系数(MD：-40~40℃)
Linear coefficient of thermal expansion 1/℃

线性热膨胀系数(MD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831

线性热膨胀系数(MD：23~80℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数(TD：-40~40℃)
Linear coefficient of thermal expansion 1/℃

线性热膨胀系数(TD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831

线性热膨胀系数(TD：23~80℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

维卡软化温度(--)
Vicat Softening Temp ℃ ASTM D1525 10

维卡软化温度(B50)
Vicat Softening Temp ℃ ISO 306/B50 , ISO 306/B120

电气性能
ELECTRICAL LNP™ STAT-LOY™ 9X03508 compound NORYL GTX™ GTX6203 resin 单位
UNIT 测试方法
TEST METHOD

表面电阻率
Surface resistivity ohms ASTM D257

加工方式

注射 LNP™ STAT-LOY™ 9X03508 compound NORYL GTX™ GTX6203 resin 单位测试方法

加工熔体温度 °C

射嘴温度 °C

干燥时间 hr

干燥温度 °C

建议的最大水分含量 %

料斗温度 °C

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

背压 MPa

螺杆转速 rpm

备注

1 一般属性：这些不能被视为规格。

2 2.0 in/min

3 80*10*4

4 80*10*4 mm

2 5.0 mm/min

3 类型 1, 5.0 mm/min

4 1.3 mm/min

5 2.0 mm/min

6 Yield

7 80*10*4 sp=62mm

8 80*10*4

9 120*10*4 mm

10 标准 B (120°C/h), 载荷2 (50N)


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
电气性能
加工方式
注射
备注
返回顶部

PPO(PPE)+PS+PA，LNP™ STAT-LOY™ 9X03508 compound对比PPO(PPE)+PS+PA，NORYL GTX™ GTX6203 resin对比物性表,价格行情_搜料_soliao

询价回复情况说明

牌号	厂家
类别