PC+聚酯，Iupilon® GMB1110对比PC+聚酯，XENOY™ X2420 resin物性表,价格行情_搜料

牌号信息	Iupilon® GMB1110 物性表 PC+聚酯 & 日本三菱指导价格：暂无塑料库存：缺货	XENOY™ X2420 resin 物性表 PC+聚酯 & 沙特沙伯基础指导价格：65100.0元/吨塑料库存：缺货
牌号简介	Iupilon® GMB1110是一种聚碳酸脂 + 聚酯（PC+聚酯）材料,含有的填充物为10% 玻璃纤维增强材料。该产品在北美洲、欧洲或亚太地区有供货,加工方式为:注射成型。 Iupilon® GMB1110的主要特性为:耐化学品。 Iupilon® GMB1110的典型应用领域为:汽车行业 Iupilon® GMB1110 is a Polycarbonate + Polyester (PC+Polyester) material filled with 10% glass fiber. It is available in Asia Pacific, Europe, or North America for injection molding. Primary attribute of Iupilon® GMB1110: Chemical Resistant. Typical application of Iupilon® GMB1110: Automotive	Xenoyx220是一种10%玻璃填充、高流动性、冲击改性、注射成型的等级，设计用于高流动性和冲击强度。X2420具有增强的熔体流动性、冲击韧性和广阔的色彩空间。 XENOYX2420 is a 10% glass filled, high flow, impact modified, injection moldable grade designed for high flow and impact strength. X2420 has enhanced melt flowability, impact ductility and broad color space.

产品描述
厂家：	日本三菱 Mitsubishi	沙特沙伯基础 SABIC
类别：	PC+聚酯 PC + Polyester	PC+聚酯 PC + Polyester
填料：	玻璃纤维 10	玻璃纤维 10
用途：
性能特点：	耐化学性 Solvent resistance	冲击性能好,流动性高,机械强度好-延展,易流动,防火阻燃等级HB High impact resistance,High liquidity,Ductility,Good liquidity,HB
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL Iupilon® GMB1110 XENOY™ X2420 resin 单位
UNIT 测试方法
TEST METHOD

吸水率(平衡，23℃，50% RH)
Water absorption rate %

吸水率(饱和，23℃)
Water absorption rate %

密度
Density g/cm³ ASTM D792, ISO 1183

密度
Density g/cm³ ISO 1183

收缩率(MD：3.2 mm)
Shrinkage rate %

收缩率(TD：3.2 mm)
Shrinkage rate %

熔体体积流动速率(265℃，2.16 kg)
Melt Volume Rate cm³/10min

熔体体积流动速率(300℃，1.2 kg)
Melt Volume Rate cm³/10min

熔体体积流动速率(300℃，1.2 kg)
Melt Volume Rate cm³/10min ISO 1133

熔体质量流动速率(300℃，1.20kg)
Melt Flow Rate g/10min ISO 1133

机械性能
MECHANICAL Iupilon® GMB1110 XENOY™ X2420 resin 单位
UNIT 测试方法
TEST METHOD

弯曲强度
bending strength MPa ISO 178

弯曲强度(屈服，50 mm跨度)
bending strength MPa ASTM D790

弯曲模量
Bending modulus MPa ISO 178

弯曲模量(50 mm跨距)
Bending modulus MPa ASTM D790

拉伸应变(屈服)
Tensile strain % ASTM D638

拉伸应变(屈服)
Tensile strain % ISO 527-2/5

拉伸应变(断裂)
Tensile strain % ISO 527-2

拉伸应变(断裂)
Tensile strain % ISO 527-2/5

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸强度(屈服)
tensile strength MPa ISO 527-2/5

拉伸强度(断裂)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ISO 527-2

拉伸强度(断裂)
tensile strength MPa ISO 527-2/5

拉伸模量
Tensile modulus MPa ASTM D638

拉伸模量
Tensile modulus MPa ISO 527-2

冲击性能
IMPACT Iupilon® GMB1110 XENOY™ X2420 resin 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度(-30℃)
Notched impact strength of cantilever beam kJ/m² ISO 180/1U

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam J/m ASTM D4812

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam kJ/m² ISO 180/1U

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

简支梁无缺口冲击强度(-30℃)
Charpy Unnotch Impact strength kJ/m²

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength kJ/m²

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength kJ/m² ISO 179

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m²

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m²

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179

装有测量仪表的落镖冲击(23℃，Total Energy)
Dart impact equipped with measuring instruments J ASTM D3763

热性能
THERMAL Iupilon® GMB1110 XENOY™ X2420 resin 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/B

热变形温度(0.45 MPa，未退火，3.2 mm)
Hot deformation temperature ℃

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/A

热变形温度(1.8 MPa，未退火，3.2 mm)
Hot deformation temperature ℃

相对温度指数(冲击机械性能)
Relative temperature index ℃ UL 746

相对温度指数(电气性能)
Relative temperature index ℃ UL 746

线性热膨胀系数(MD)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数(MD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831

线性热膨胀系数(MD：23~80℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数(TD)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数(TD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831

线性热膨胀系数(TD：23~80℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

维卡软化温度(B120)
Vicat Softening Temp ℃ ISO 306/B120

阻燃性能
FLAMMABILITY Iupilon® GMB1110 XENOY™ X2420 resin 单位
UNIT 测试方法
TEST METHOD

0.40 mm
0.40 mm UL 94

加工方式

注射 Iupilon® GMB1110 XENOY™ X2420 resin 单位测试方法

射嘴温度 °C

干燥时间 hr

干燥时间，最大 hr

干燥温度 °C

建议的最大水分含量 %

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

注塑压力 MPa

螺杆转速 rpm

建议注射量 Iupilon® GMB1110 XENOY™ X2420 resin 单位测试方法

加工熔体温度 °C

射嘴温度 °C

排气孔深度 mm

料斗温度 °C

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

背压 MPa

螺杆转速 rpm

备注

1 一般属性：这些不能被视为规格。

2 0,20 in/min

3 类型 1, 0,20 in/min

4 0,051 in/min

5 80*10*4 sp=62mm

6 80*10*4


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
阻燃性能
加工方式
注射
建议注射量
备注