牌号信息	Torlon® 4601 物性表 PAI & 比利时索尔维指导价格：暂无塑料库存： 1000kg	Torlon® 4301 物性表 PAI & 比利时索尔维指导价格：892500.0元/吨塑料库存： 3050kg
牌号简介	Torlon® 4601是一种特殊的耐磨级聚酰胺酰亚胺（PAI）。大多数Torlon-Pai等级不能在底切模具中成功成型。Torlon® 4601已经被设计成可在具有较小咬边的工具中成型，并且在润滑磨损应用中具有非常好的性能。Torlon Pai具有最高强度和刚度的热塑性塑料高达275°C（525°F）。它具有优异的耐磨性、抗蠕变性和耐化学腐蚀性。Torlon® 4601聚酰胺酰亚胺的潜在应用包括滚珠轴承保持架和其他需要咬边加工的成型制品。 Torlon® 4601 is a specialty wear-resistant grade of polyamide-imide (PAI). Most Torlon® PAI grades cannot be molded successfully in molds with undercuts. Torlon® 4601 has been formulated to be moldable in tools with minor undercuts and give very good performance in lubricated wear applications. Torlon® PAI has the highest strength and stiffness of any thermoplastic up to 275°C (525°F). It has outstanding resistance to wear, creep, and chemicals. Potential applications for Torlon® 4601 polyamide-imide include ball bearing cages and other molded articles that require undercut tooling.	Torlon 4301是一种耐磨级聚酰胺 - 酰亚胺（PAI）树脂。机械性能和耐磨损性取得了良好的平衡。具有高挠曲强度和抗压强度，在高流速和高压条件下，摩擦系数低，耐磨损性优异。在所有能耐受275 ℃（ 525°F ）高温的热塑性树脂中，Torlon PAI具有最高的强度和刚度。并具有优异的耐磨损性、抗蠕变性和耐化学性。 Torlon 4301聚酰胺 - 酰亚胺可用于止推垫圈、花键衬、阀座、衬套、轴承、耐磨环、凸轮和其它需要在高温条件下保持强度和耐磨损的产品中。注塑成型级：高流动：Torlon 4301 HF 低流动： Torlon 4301 LF 低流动小颗粒： Torlon 4301 LFSP 挤塑级：高流动： Torlon 4301-EXT 更高流动：Torlon 4301-HQ Torlon® 4301 is a wear-resistant grade of polyamide-imide (PAI) resin. It has a good balance of mechanical properties and wear resistance. It offers high flexural and compressive strength with a low coefficient of friction and outstanding wear resistance at both high velocity and high pressure conditions. Torlon® PAI has the highest strength and stiffness of any thermoplastic up to 275°C (525°F). It has outstanding resistance to wear, creep, and chemicals. Potential applications for Torlon® 4301 polyamide-imide include thrust washers, spline liners, valve seats, bushings, bearings, wear rings, cams and other applications requiring strength at high temperature and resistance to wear. Injection Molding Grades: High Flow: Torlon® 4301 HF Low Flow: Torlon® 4301 LF Low Flow Small Pellets: Torlon® 4301 LFSP Extrustion Grades: High Flow: Torlon® 4301-EXT Higher Flow: Torlon® 4301-HQ

产品描述
厂家：	比利时索尔维 Solvay	比利时索尔维 Solvay
类别：	PAI PAI	PAI PAI
填料：
用途：	轴承,工业应用	汽车领域的应用,传递应用,垫圈,金属取代,密封装置,止推垫圈,工业应用,滚轴,飞机应用,轴承,齿轮,机器/机械部件,密封件,航空航天应用,凸轮,石油/天然气用品,衬套,工业部件
性能特点：	机械强度好,韧性好,阻燃,耐高温,耐磨,耐化学性 Good Rigidity,Good flexibility,Flame Characteristics,High Heat Resistance,Good wear resistance,Solvent resistance	机械强度好,韧性好,导电,低摩擦系数,阻燃,自润滑,耐高温,耐磨,耐化学性 Good Rigidity,Good flexibility,Conductive,Low coefficient of friction,Flame Characteristics,Self-lubricating,High Heat Resistance,Good wear resistance,Solvent resistance
加工条件：	注射成型 Injection Molding	型材挤出成型 Profile extrusion

技术参数

物理性能
PHYSICAL Torlon® 4601 Torlon® 4301 单位
UNIT 测试方法
TEST METHOD

吸水率(24hr)
Water absorption rate % ASTM D570

密度
Density g/cm³ ASTM D792

收缩率(MD)
Shrinkage rate % ASTM D955

机械性能
MECHANICAL Torlon® 4601 Torlon® 4301 单位
UNIT 测试方法
TEST METHOD

剪切强度
shear strength MPa ASTM D732

压缩强度
compressive strength MPa ASTM D695

压缩模量
Compression modulus MPa ASTM D695

弯曲强度
bending strength MPa ASTM D790

弯曲强度(232℃)
bending strength MPa ASTM D790

弯曲强度(23℃)
bending strength MPa ASTM D790

弯曲模量
Bending modulus MPa ASTM D790

弯曲模量(232℃)
Bending modulus MPa ASTM D790

弯曲模量(23℃)
Bending modulus MPa ASTM D790

拉伸应变(断裂)
Tensile strain % ASTM D1708

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸强度
tensile strength MPa ASTM D1708

拉伸强度
tensile strength MPa ASTM D638

拉伸模量
Tensile modulus MPa ASTM D638

拉伸模量(--)
Tensile modulus MPa ASTM D1708

拉伸模量(--)
Tensile modulus MPa ASTM D638

摩擦系数(--)
friction coefficient ASTM D3702

磨损因数(干燥： 4 m/s，0.2 MPa(800 fpm，31.25 psi))
Wear factor in³·min^-10/ft·lb·hr ASTM D3702

磨损因数(干燥：0.25 m/s，3.4 MPa(50 fpm，500 psi))
Wear factor in³·min^-10/ft·lb·hr ASTM D3702

磨损因数(润滑： 0.25 m/s，6.9 MPa(75 fpm，1000 psi))
Wear factor in³·min^-10/ft·lb·hr ASTM D3702

磨损因数(润滑： 4 m/s，5.2 MPa(800 fpm，750 psi))
Wear factor in³·min^-10/ft·lb·hr ASTM D3702

冲击性能
IMPACT Torlon® 4601 Torlon® 4301 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度
Notched impact strength of cantilever beam J/m ASTM D256

悬臂梁缺口冲击强度
Impact strength of cantilever beam notch J/m ASTM D256

热性能
THERMAL Torlon® 4601 Torlon® 4301 单位
UNIT 测试方法
TEST METHOD

导热系数
Thermal conductivity coefficient W/m/K ASTM C177

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

线性热膨胀系数
Linear coefficient of thermal expansion cm/cm/℃ ASTM D696

电气性能
ELECTRICAL Torlon® 4601 Torlon® 4301 单位
UNIT 测试方法
TEST METHOD

体积电阻率
Volume resistivity ohms·cm ASTM D257

表面电阻率
Surface resistivity ohms ASTM D257

加工方式

注射 Torlon® 4601 Torlon® 4301 单位测试方法

射嘴温度 °C

干燥时间 hr

干燥温度 °C

建议的最大水分含量 %

料筒后部温度 °C

模具温度 °C

背压 MPa

螺杆转速 rpm

螺杆长径比

备注

1 一般属性：这些不能被视为规格。

1 Material should be Tempered (Cured).

2 一般属性：这些不能被视为规格。

3 以前，ASTM标准试验方法D1708用于测量PAI和类似材料的拉伸性能，因为小试样能节约材料。现在使用最广泛的是ASTM D638 1 Bar 试样。所含D1708数值仅用作历史参考，不与D638值作对照用。

4 以前，ASTM标准试验方法D1708用于测量PAI和类似材料的拉伸性能，因为小试样能节省材料。现在使用最广泛的是ASTM D638 1 Bar 试样。所含D1708数值仅用作历史参考，不与D638值作对照用。

5 润滑： 0.25 m/s, 6.9 MPa (75 fpm, 1000 psi)

6 润滑： 4 m/s, 5.2 MPa (800 fpm, 750 psi)

7 干燥：0.25 m/s, 3.4 MPa (50 fpm, 500 psi)

8 干燥： 4 m/s, 0.2 MPa, (800 fpm, 31.25 psi)