ABS，ELIX™ ABS Ultra HH 4115 PG对比ABS，ELIX™ ABS Ultra HH 4115 HI物性表,价格行情_搜料

牌号信息	ELIX™ ABS Ultra HH 4115 PG 物性表 ABS & 西班牙ELIX 指导价格：暂无塑料库存：缺货	ELIX™ ABS Ultra HH 4115 HI 物性表 ABS & 西班牙ELIX 指导价格：暂无塑料库存：缺货
牌号简介	Elix Ultra HH 4115 PG超高耐热ABS电镀等级ISO shortname:ISO 2580-1 ABS 2-X，MG，115-15-35-20主要优点是具有极强的抗冲击性，低温延展性非常高，冲击温度高达-30°C，流动性、耐热性和柔韧性良好，在注塑过程中排放和气味等级较低的模具沉积物。加工应用尺寸精度好，收缩率低，CLTE。密度低于PC/ABS化学成分聚碳酸酯改性丙烯腈-丁二烯-苯乙烯共聚物 ELIX ULTRA HH 4115 PG Very high heat resistance ABS plating grade ISO shortname: ISO 2580-1 ABS 2-X, MG, 115-15-35-20 Major Benefits Extreme impact resistance with low temperature ductility Very high impact up to -30°C Well balanced flowability, heat resistance and flexibility Low emission and odor grade Lower mould deposits in injection molding processing applications Good dimensional precision, low shrinkage and CLTE. Lower density than PC/ABS Chemical composition Acrylonitrile-butadiene-styrene (ABS) copolymer modified with polycarbonate and poly(styrene-co-maleimide)	Elix Ultra HH 4115 Hi超高耐热abs，具有极强的抗冲击性，iso shortname:iso 2580-1 abs 2-x，mg，115-15-35-20主要优点：具有极强的抗冲击性，低温延展性，极强的抗冲击性，高达-30°C，流动性和耐热性良好，比pc/abs低密度，低排放和气味等级，低模具在注塑加工应用中的沉积物在高温下具有更好的尺寸化学成分：聚碳酸酯和聚（苯乙烯-马来酰亚胺）改性的丙烯腈-丁二烯-苯乙烯共聚物 ELIX ULTRA HH 4115 HI Very high heat resistance ABS with extreme impact resistance ISO shortname: ISO 2580-1 ABS 2-X, MG, 115-15-35-20 Major Benefits: Extreme impact resistance with low temperature ductility Very high impact up to -30°C Well balanced flowability and heat resistance Lower density than PC/ABS Low emission and odor grade Lower mould deposits in injection molding processing applications Better dimensional under heat Chemical Composition: Acrylonitrile-butadiene-styrene (ABS) copolymer modified with polycarbonate and poly(styrene-co-maleimide)

产品描述
厂家：	西班牙ELIX	西班牙ELIX Spain ELIX
类别：	ABS ABS	ABS
填料：
用途：		汽车内部装备,汽车领域的应用,汽车内部零件
性能特点：	韧性好,冲击性能好,尺寸稳定性好,易流动,收缩性低,耐高温,低VOC,低密度,电镀 Good flexibility,High impact resistance,Good Dimensional Stability,Good liquidity,Low contractility,High Heat Resistance,Low odor,Low density,Electroplating	耐高温,冲击性能好,低密度,易流动,耐低温冲击,低VOC High Heat Resistance,High impact resistance,Low density,Good liquidity,low-temperature impact resistance,Low odor
加工条件：

技术参数

物理性能
PHYSICAL ELIX™ ABS Ultra HH 4115 PG ELIX™ ABS Ultra HH 4115 HI 单位
UNIT 测试方法
TEST METHOD

密度(25℃)
Density g/cm³ ISO 1183

收缩率(MD)
Shrinkage %

收缩率(TD)
Shrinkage %

熔体体积流动速率(260℃，5 kg)
Melt Volume Rate cm³/10min ISO 1133

熔体质量流动速率(230℃，3.80kg)
Melt Flow Rate g/10min ASTM D1238

冲击性能
IMPACT ELIX™ ABS Ultra HH 4115 PG ELIX™ ABS Ultra HH 4115 HI 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度(-30℃)
Izod Notched Impact strength kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(-30℃，3.2mm)
Izod Notched Impact strength J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Izod Notched Impact strength kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(23℃，3.2mm)
Izod Notched Impact strength J/m ASTM D256

悬臂梁缺口冲击强度(23℃，6.4mm)
Izod Notched Impact strength J/m ASTM D256

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m²

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m²

热性能
THERMAL ELIX™ ABS Ultra HH 4115 PG ELIX™ ABS Ultra HH 4115 HI 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，退火)
HDT ℃ ISO 75-2/B

热变形温度(1.8 MPa，退火)
HDT ℃ ISO 75-2/A

线性热膨胀系数(MD：23~55℃)
Coeff.of linear therm expansion 1/℃ ISO 11359-2

维卡软化温度(--)
Vicat Softening Temperature ℃ ASTM D1525 6

维卡软化温度(B120)
Vicat Softening Temperature ℃ ISO 306/B120

阻燃性能
FLAMMABILITY ELIX™ ABS Ultra HH 4115 PG ELIX™ ABS Ultra HH 4115 HI 单位
UNIT 测试方法
TEST METHOD

1.60 mm
1.60 mm UL 94

燃烧速率(2.0 mm)
Burning Speed mm/min ISO 3795

碳排放(23℃)
carbon emission µgC/g VDA 277

机械性能
MECHANICAL ELIX™ ABS Ultra HH 4115 PG ELIX™ ABS Ultra HH 4115 HI 单位
UNIT 测试方法
TEST METHOD

弯曲强度
Flexural Strength MPa ISO 178

弯曲模量(--)
Flexural Modulus MPa ASTM D790

弯曲模量(--)
Flexural Modulus MPa ISO 178

拉伸应变(屈服)
Tensile strain % ISO 527-2/50

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2/50

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸强度(屈服)
tensile strength MPa ISO 527-2/50

拉伸模量(--)
Tensile modulus MPa ASTM D638

拉伸模量(--)
Tensile modulus MPa ISO 527-1-2

球压硬度
ball-indentation hardness MPa ISO 2039-1

补充信息
ELIX™ ABS Ultra HH 4115 PG ELIX™ ABS Ultra HH 4115 HI 单位
UNIT 测试方法
TEST METHOD

排放(FOG：23℃)
discharge µg/g

排放(VOC：23℃)
discharge µg/g

加工方式

注射 ELIX™ ABS Ultra HH 4115 PG ELIX™ ABS Ultra HH 4115 HI 单位测试方法

Injection Velocity m/min ISO 294

加工熔体温度 °C

模具温度 °C

备注

2、60x60x2 mm

3、5.0 mm/min

4、1.3 mm/min

5、2.0 mm/min

6、速率 A (50°C/h), 载荷2 (50N)

7、US-FMVSS