牌号简介 About |
---|
警告:此材料的状态为“商业:限量发行”。此材料的数据最近尚未验证。在指定此等级之前,请联系RTP公司以获取当前信息。玻璃纤维增强聚氨酯弹性体提供比基础树脂更大的尺寸稳定性。它们具有出色的冲击强度,并且仍然保持其弹性特性。 Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. Glass fiber reinforced polyurethane elastomers offer greater dimensional stability than the base resin. They offer outstanding impact strength and still remain their elastomeric characteristics. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.27 | g/cm³ | ASTM D792 |
吸水率 Water absorption rate |
|||
23℃,24hr 23℃,24hr |
0.40 | % | ASTM D570 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
3.2mm 3.2mm |
640 | J/m | ASTM D256 |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
3.2 mm 3.2 mm |
1300 | J/m | ASTM D4812 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
ASTM D648 | ||
0.45 MPa,未退火 0.45 MPa, unannealed |
110 | ℃ | ASTM D648 |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1/℃ | ASTM D696 | |
导热系数 Thermal conductivity coefficient |
W/m/K | ASTM C177 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
|||
1 MHz 1 MHz |
ASTM D150 | ||
耗散因数 Dissipation factor |
|||
1 MHz 1 MHz |
ASTM D150 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
1.60 mm 1.60 mm |
UL 94 | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A Shaw's A |
ASTM D2240 | ||
拉伸模量 Tensile modulus |
MPa | ASTM D638 | |
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲强度 bending strength |
|||
屈服 yield |
MPa | ASTM D790 | |
压缩强度 compressive strength |
MPa | ASTM D695 |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
PA66价钱又要涨 索尔维-英威达聚合工厂发作不可抗力
2016-10-17 10月6日,尼龙制造巨头索尔维(Solvay)正式宣布,其合成尼龙所需的重要原材料:HMD(己二胺)装置遭遇不可抗力,正在给其现有客户实行销售配给,具体销售配给情况并未透露 索尔维称,不可抗力是由于其装置所需的ADN(己二腈)供应严重不足导致的,发生供应不足的工厂(Butachimie)位于法国,是索尔维和英威达(Invista)各占50%股权建立的合资企业,虽然目前具体故障原因并未透露,但可以肯定是一个严重的技术故障,而且短期内无法解决。 实际上,Buta |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |