牌号简介 About |
---|
该FP33树脂是一种线性中等密度聚乙烯,丁烯-1共聚物,溶液法生产,用于薄膜挤出,具有良好的机械性能。添加剂:加工助剂防滑应用:薄膜和要求较高硬度的自动包装:纺织产品、卫生纸等。建议膜厚:0.025至0.100 mm。 Braskem PE FP 33 is a Linear Low Density Polyethylene product. It is available in Europe or Latin America. Typical application: Food Contact Applications. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.932 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
1.8 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
割线模量 Secant modulus |
|||
1% 正割,TD,40 µm,吹塑薄膜 1% secant, TD, 40 µ m, blow molded film |
320 | MPa | ASTM D882 |
1% 正割,MD,40 µm,吹塑薄膜 1% secant, MD, 40 µ m, blow molded film |
280 | MPa | ASTM D882 |
拉伸强度 tensile strength |
|||
TD,断裂,40 µm,吹塑薄膜 TD, fracture, 40 µ m, blow molded film |
30.0 | MPa | ASTM D882 |
MD,断裂,40 µm,吹塑薄膜 MD, fracture, 40 µ m, blow molded film |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
|||
TD,断裂,40 µm,吹塑薄膜 TD, fracture, 40 µ m, blow molded film |
% | ASTM D882 | |
MD,断裂,40 µm,吹塑薄膜 MD, fracture, 40 µ m, blow molded film |
% | ASTM D882 | |
撕裂强度 tear strength |
|||
TD,40 µm,吹塑薄膜 TD, 40 µ m, blow molded film |
g | ASTM D1922 | |
MD,40 µm,吹塑薄膜 MD, 40 µ m, blow molded film |
g | ASTM D1922 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
雾度 Haze |
|||
40 µm,吹塑薄膜 40 µ m, blow molded film |
% | ASTM D1003 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
模具加工如何选择适宜的铣刀和铣削方式?
2017-08-18 选择合适的铣削刀具,在面铣加工中采用滚动切入法,以及在条件适合时用铣刀进行孔加工,制造商可以在无需投资购买新设备的情况下,大幅提高生产能力,提高加工效率而节省大量时间和成本。 在选择适合加工任务的铣刀时,必须考虑被加工零件的几何形状、尺寸和工件材质的各种问题。 铣刀主偏角 主偏角为切削刃与切削平面的夹角。主 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |