牌号简介 About |
---|
CONATHANE® EN-2521是一种由两部分填充的聚氨酯树脂系统。该系统具有良好的操作性能和使用寿命。EN-2521可以在室温或高温下固化,而不会形成空隙。固化后的化合物具有优异的耐水性和极强的抗热震性。该系统的其他突出性能包括:低温、固化过程中的极低应力、低收缩和非常好的电性能。CONATHANE® EN-2521建议用于需要在-65°C至130°C温度范围内具有特殊性能的封装应用。它特别适用于模块、应变敏感电路、变压器和线圈的封装。 CONATHANE EN-2521 is a two-part filled polyurethane resin system. The system features good handling properties and working life. EN-2521 can be cured at room or elevated temperatures without the formation of voids. The cured compound has excellent water resistance and is exceptionally resistant to thermal shock. Other outstanding properties of this system include low exotherm, very low stresses during cure, low shrinkage, and very good electrical properties. CONATHANE EN-2521 is recommended for potting applications where exceptional performance in the temperature range of -65°C to 130°C is required. It is particularly useful in the encapsulation of modules, strain sensitive circuitry, transformers, and coils. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
|||
-- -- 3 |
1.10 到 1.30 | g/cm³ | |
-- -- 4 |
1.53 | g/cm³ | |
-- -- 5 |
1.40 到 1.70 | g/cm³ | |
吸水率 Water absorption rate |
|||
25℃,24hr ,水中 25 ℃, 24 hours, in water |
0.19 | % | |
25℃,60days 25℃,60days |
0.94 | % | |
7days 7days |
% | ||
固体含量 Solid content |
|||
-- -- 3 |
% | ||
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
|||
-- -- 6 |
ohms | ||
-- -- 7 |
ohms | ||
-- -- 8 |
ohms | ||
体积电阻率 Volume resistivity |
|||
25 ℃ 25 ℃ |
ohms·cm | ||
60 ℃ 60 ℃ |
ohms·cm | ||
90 ℃ 90 ℃ |
ohms·cm | ||
介电强度 Dielectric strength |
|||
1.59 mm 1.59 mm |
kV/mm | ||
3.18 mm 3.18 mm |
kV/mm | ||
介电常数 Dielectric constant |
|||
25 ℃,100 Hz 25 ℃,100 Hz |
|||
25 ℃,1 kHz 25 ℃,1 kHz |
|||
25 ℃,1 MHz 25 ℃,1 MHz |
|||
60 ℃,100 Hz 60 ℃,100 Hz |
|||
60 ℃,1 kHz 60 ℃,1 kHz |
|||
60 ℃,1 MHz 60 ℃,1 MHz |
|||
90 ℃,100 Hz 90 ℃,100 Hz |
|||
90 ℃,1 kHz 90 ℃,1 kHz |
|||
90 ℃,1 MHz 90 ℃,1 MHz |
|||
耗散因数 Dissipation factor |
|||
25℃,100 Hz 25℃,100 Hz |
|||
25℃,1 kHz 25℃,1 kHz |
|||
25℃,1 MHz 25℃,1 MHz |
|||
60℃,100 Hz 60℃,100 Hz |
|||
60℃,1 kHz 60℃,1 kHz |
|||
60℃,1 MHz 60℃,1 MHz |
|||
90℃,100 Hz 90℃,100 Hz |
|||
90℃,1 kHz 90℃,1 kHz |
|||
90℃,1 MHz 90℃,1 MHz |
|||
耐电弧性 Arc resistance |
sec | ||
相比漏电起痕指数 Compared to the leakage tracing index |
V | UL 746 | |
相比漏电起痕指数 Compared to the leakage tracing index |
UL 746 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
热固性混合粘度 Thermosetting mixed viscosity |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
25℃ 25℃ 3 |
cP | ||
25℃ 25℃ 5 |
cP | ||
25℃ 25℃ 4 |
cP | ||
60℃ 60℃ 4 |
cP | ||
脱模时间 stripping time |
|||
25℃ 25℃ |
min | ||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Isocyanate Content Isocyanate Content 3 |
% | ||
冷热冲击测试 Test - 10 cycles,-65℃ to 130℃ Cold and hot shock test -10 cycles, -65 ℃ to 130 ℃ |
|||
工作期限 - 1 lb. mass Work term -1 lb. mass |
|||
25℃ 25℃ |
hr | ||
60℃ 60℃ |
hr | ||
抗真菌性 Antifungal activity |
|||
Cured Properties Cured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Linear Shrinkage Linear Shrinkage |
% | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
|||
拉伸强度 tensile strength |
MPa | ||
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1/℃ | ||
导热系数 Thermal conductivity coefficient |
W/m/K | ||
热稳定性 thermal stability |
|||
% Wt. Loss after 7 days @ 130℃ % Wt. Loss after 7 days @ 130℃ |
% | ||
% Wt. Loss after 7 days @ 155℃ % Wt. Loss after 7 days @ 155℃ |
% | ||
热固组件 Thermosetting components |
|||
树脂 resin |
|||
硬化法 Hardening method |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Resin |
3 Mix |
4 Hardener |
5 90°C |
6 60°C |
7 25°C |
【新闻资讯】查看全部
可穿戴资料高机能化:用浆料和薄膜完成弹性布线
2016-03-08 提高布线弹性的方法不只是导电针织材料。使弹性强的薄膜和浆料具备导电性也是一种不错的方法。通过在衣服上粘贴这些材料,可以实现穿着比较舒适的可穿戴终端。 比如说,粘合剂制造商Cemedine提议使用导电粘合剂作为可穿戴终端的布线。采用了该公司销售的低温硬化型导电粘合剂“Cemedine SXECA”系列。 该系列粘合剂的柔软性好,而且对于温度变化的耐久度高,过去一直作为焊锡的替代品使用。近年来,为了满足“绘制电路”的要求,该公司逐步进行改进,增加了导电浆料的产品 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |