牌号简介 About |
---|
POM共聚物产品,具有低排放特性,尤其适用于汽车内饰。具有高硬度、硬度和韧性等标准注射成型等级的良好性能;对溶剂、燃料和强碱具有良好的耐化学性以及良好的抗水解性;厚度大于1 mm时,具有较高的耐热性和氧化降解性,燃烧速率保持在ISO 3795和FMVSS 302<75 mm/min。VDA 275排放量<10 ppm应用范围:汽车工程,fmvss=联邦机动车安全标准(美国) POM copolymer Product with reduced emissions especially for automotive interior application. Good properties of the standard-injection molding grades like high rigidity, hardness and toughness; good chemical resistance to solvents, fuel and strong alkalis as well as good hydrolysis resistance; high resistance to thermal and oxidative degradation are maintained Burning rate ISO 3795 and FMVSS 302 < 75 mm/min for a thickness more than 1 mm. VDA 275 Emissions < 10 ppm Ranges of applications: automotive engineering, FMVSS = Federal Motor Vehicle Safety Standard (USA) |
技术参数 Technical Data | |||
---|---|---|---|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
-30℃ -30℃ |
6.0 | kJ/m² | |
23℃ 23℃ |
6.5 | kJ/m² | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
-30℃ -30℃ |
200 | kJ/m² | |
23℃,局部断裂 23 ℃, localized fracture |
200 | kJ/m² | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
104 | ℃ | ISO 75-2/A |
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ISO 306 | |
熔融温度 Melting temperature 3 |
℃ | ISO 11357-3 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1/℃ | ||
TD TD |
1/℃ | ||
Effective Thermal Diffusivity Effective Thermal Diffusivity |
m²/s | 内部方法 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength |
kV/mm | IEC 60243-1 | |
相对电容率 Relative permittivity |
|||
100 Hz 100 Hz |
|||
1 MHz 1 MHz |
|||
耗散因数 Dissipation factor |
|||
100 Hz 100 Hz |
|||
1 MHz 1 MHz |
|||
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
球压硬度 Ball hardness 2 |
MPa | ISO 2039-1 | |
拉伸模量 Tensile modulus |
MPa | ISO 527-2/1A | |
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ISO 527-2/1A/50 | |
拉伸应变 Tensile strain |
|||
屈服 yield |
% | ISO 527-2/1A/50 | |
标称拉伸断裂应变 Nominal tensile fracture strain |
% | ISO 527-2/1A/50 | |
拉伸蠕变模量 Tensile creep modulus |
|||
1 hr 1 hr |
MPa | ||
1000 hr 1000 hr |
MPa | ||
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
MPa | ISO 178 | |
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
g/cm³ | ISO 1183 | |
熔体体积流动速率 Melt Volume Rate |
|||
190℃,2.16 kg 190℃,2.16 kg |
cm³/10min | ISO 1133 | |
收缩率 Shrinkage rate |
|||
TD TD |
% | ||
MD MD |
% | ||
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
% | ||
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ||
熔体密度 Melt density |
g/cm³ | 内部方法 | |
熔体导热性 Melt thermal conductivity |
W/m/K | 内部方法 | |
顶出温度 Ejection temperature |
℃ | ||
Specific Heat Capacity of Melt Specific Heat Capacity of Melt |
J/kg/℃ |
备注 |
---|
2. 30s |
3. 10°C/min |
【新闻资讯】查看全部
国度为什么制止使用超薄塑料购物袋?
2016-02-22 国务院办公厅在下发“限塑令”时明确,从2008年6月1日起,在全国范围内禁止生产、销售、使用厚度小于0.025毫米的塑料购物袋。沈阳产品质量监督检验院包装所工作人员说,国家实行“限塑令”是为了限制和减少塑料袋的使用,遏制“白色污染”。 塑料购物袋在为消费者提供便利的同时,由于过量使用及回收处理不到位等原因,也造成了严重的能源、资源浪费和环境污染。特别是超薄塑料购物袋容易破损,大多被随意丢弃,成为“白色污染”的主要来源。 据悉,“0.025毫米”是国家相关部门 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |