牌号简介 About |
---|
采用Unipol-PP技术,采用气相流化床反应器和高活性催化剂体系,制备了80熔融流中抗冲共聚聚丙烯,用于注塑成型,得到了高活性聚丙烯2180H。这种可控流变共聚物适用于薄壁注塑包装、家庭用品和消费品应用。高熔体流动大大提高了循环时间,而不会丧失冲击力。包含成核剂和防静电剂。2180H产品提供:高硬度,在23°C和-30°C下具有优异的冲击力,非常高的熔体流动性,优异的模具释放性,优越的加工性能,优异的批量一致性,Pinnacle的2180H聚丙烯被美国食品和药物管理局食品接触通知864覆盖。因此,如21 CFR 176.170表1和表2所述,该聚合物可在使用a-h条件下与所有食品类型接触。该聚合物还符合21 CFR 177.1520(c)、第3.1(a)和3.2(a)项的要求。 80 MELT FLOW MEDIUM IMPACT COPOLYMER POLYPROPYLENE FOR INJECTION MOLDING Pinnacle Polymers Polypropylene 2180H is made via UNIPOL™ PP technology, which utilizes gas-phase fluidized bed reactors with a high activity catalyst system to ensure uniform physical properties and lot-to-lot consistency. This controlled rheology copolymer is intended for use in thin wall injection molded packaging, housewares and consumer products applications. High Melt Flow dramatically improves cycle-times without forfeiting impact. Contains nucleator and antistat. The 2180H product provides: High stiffness Excellent impact at 23°C and -30°C Very high melt flow Excellent mold release Superior processability Excellent lot-to-lot consistency Pinnacle's 2180H polypropylene is covered under US FDA Food Contact Notification 864. As such, this polymer can be used in contact with all food types under Conditions of Use A-H, as described in 21 CFR 176.170, Tables 1 and 2. This polymer also complies with 21 CFR 177.1520(c), items 3.1(a) and 3.2(a). |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.900 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
74 到 86 | g/10min | ASTM D1238 |
收缩率 Shrinkage rate |
|||
MD MD |
1.4 | % | ASTM D955 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength 3 |
|||
屈服,3.20 mm,注塑成型 Yield, 3.20 mm, injection molding 3 |
> 20.0 | MPa | ASTM D638 |
拉伸应变 Tensile strain 3 |
|||
屈服,3.20 mm,注塑成型 Yield, 3.20 mm, injection molding 3 |
5.0 | % | ASTM D638 |
弯曲模量 Bending modulus 4 |
|||
1% 正割,3.20 mm,注塑成型 1% cut, 3.20 mm, injection molded 4 |
MPa | ASTM D790-A | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch 5 |
|||
23℃,3.2mm,注塑成型 23 ℃, 3.2mm, injection molding 5 |
kJ/m² | ASTM D256 | |
23℃,3.2mm,注塑成型 23 ℃, 3.2mm, injection molding 5 |
J/m | ASTM D256 | |
落锤冲击 Drop hammer impact 6 |
|||
-30℃ -30℃ 6 |
J | ASTM D5420 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 类型 1, 2.0 in/min |
3 类型 1, 0.050 in/min |
4 Type I |
5 方法G, 几何形状GC |
【新闻资讯】查看全部
人工智能将助力石化行业转型
2017-05-26 5月23日,中国石油和化工行业人工智能联盟筹备会在上海举行,会议联合发起倡议成立中国石油和化工人工智能联盟。 届时,联盟将通过有效的合作交流机制,在石油和化工行业推广人工智能技术,普及人工智能知识,创新人工智能服务,共同培育推进中国石油和化学工业转型升级的新动能。 人工智能首次被纳入政府工作报告,不仅为人工智能应用创新提供了政策支持,更为石油和化工行业改造提升带来了机遇。中国石油和化工行业人工智能联盟成立,对于石化行业实施创新驱动战略、实现行业智能型变革、促 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |