牌号简介 About |
---|
符合ISO 1043-1的材料规范:聚丙烯热稳定聚丙烯,用50%重量%长的玻璃纤维加固。纤维与聚丙烯基体发生化学耦合。球是圆柱形的,通常也包括10 mm长的嵌入纤维。(-0403=热稳定,-0453=低排放)Celstran注塑件具有高强度、高刚度、高热变形等优异的力学性能。由于部件中内置了纤维骨架,因此在高温和低温下缺口冲击强度会增加。长纤维增强能显著降低蠕变。模制品的各向同性收缩使翘曲最小化。通过注射成型,可以制造出具有高再现性的复杂零件。应用领域:汽车功能/结构件 Material code according to ISO 1043-1: PP Heat stabilized polypropylene reinforced with 50 weight percent long glass fibers. The fibers are chemically coupled to the polypropylene matrix. The pellets are cylindrical and normally as well as the embedded fibers 10 mm long. (-0403 = heat stabilized, -0453 = low emission) Parts molded of CELSTRAN have outstanding mechanical properties such as high strength and stiffness combined with high heat deflection. The notched impact strength is increased at elevated and low temperatures due to the fiber skeleton built in the parts. The long fiber reinforcement reduces creep significantly. The very isotropic shrinkage in the molded parts minimizes the warpage. Complex parts can be manufactured with high reproducibility by injection molding. Application field: Functional/structural parts for automotive |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.34 | g/cm³ | ISO 1183 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
-- -- |
12000 | MPa | ISO 527-2/1A/1 |
80℃ 80℃ |
8500 | MPa | ISO 527-2/1A |
拉伸强度 tensile strength |
|||
断裂 fracture |
145 | MPa | ISO 527-2/1A/5 |
80℃ 80℃ |
90.0 | MPa | ISO 527-2/1A |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ISO 527-2/1A/5 | |
断裂,80℃ Fracture, 80 ℃ |
% | ISO 527-2/1A | |
弯曲模量 Bending modulus |
ISO 178 | ||
23℃ 23℃ |
MPa | ISO 178 | |
80℃ 80℃ |
MPa | ISO 178 | |
弯曲强度 bending strength |
ISO 178 | ||
23℃ 23℃ |
MPa | ISO 178 | |
80℃ 80℃ |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
-30℃ -30℃ |
kJ/m² | ISO 179/1eA | |
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179/1eU | ||
-30℃ -30℃ |
kJ/m² | ISO 179/1eU | |
23℃ 23℃ |
kJ/m² | ISO 179/1eU | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
熔融温度 Melting temperature 2 |
℃ | ISO 11357-3 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 10°C/min |
【新闻资讯】查看全部
环保税首个申报期临近 30省份明白适用税额
2018-01-12 备受关注的环境保护税已经于2018年1月1日起正式施行,即将于一季度征收的首个申报期也日渐临近。1月10日,记者从财政部、国税总局、环保部获悉,目前各地已经普遍成立环保税征管准备工作小组,建立跨部门协作机制,环保税各项征管准备工作已基本就绪。 据悉,目前除西藏自治区外,各省(区、市)均已出台了本地区应税大气污染物和水污染物的具体适用税额。其中,黑龙江、福建、新疆等12个省份按低限确定税额,其大气、水污染物税额分别为每污染当量1.2元和1.4元。内蒙古、海南、云南等12个省份 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |